Hot-rolled ferrite bainite dual-phase steel strip for wheel with 590MPa class tension strength and preparation method thereof

A technology of tensile strength and ferrite, which is applied in the field of steel product production, can solve problems such as inappropriate manufacturing of rims, cracks in the center hole of spokes, and thinning of welds, so as to avoid fatigue test failure, good welding performance, and high fatigue performance Effect

Active Publication Date: 2019-03-29
BENGANG STEEL PLATES
View PDF18 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The 590MPa grade high-strength steel currently used in the market mainly has three structure types, one is the ferritic pearlite type, the hole expansion rate of this steel is low, and it is easy to cause the center hole of the spoke to crack, which is not suitable for the use of passenger car spokes; Ferritic martensitic dual-phase steel, this type of steel has a low yield ratio and is easy to form. It is widely used in the manufacture of wheel spokes, but this type of steel is not suitable for making rims, because of the softening problem in the welding heat-affected zone, it is easy to appear w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A hot-rolled ferritic and bainitic dual-phase steel strip for wheels with a tensile strength of 590MPa, including, by weight percentage, C 0.05%, Si 0.70%, Mn 1.40%, P≤0.020%, S≤0.004 %, Al 0.060%, Nb0.015%, Cr 0.20%, N≤0.0060, O≤0.0020%, the balance is Fe and unavoidable impurities.

[0027] According to another aspect of the present invention, a method for preparing a hot-rolled ferritic-bainite dual-phase steel strip for a wheel with a tensile strength of 590MPa is provided, including the following steps: molten iron pretreatment→converter smelting→LF+RH Refining outside the furnace → slab continuous casting → heating → rough rolling, finishing rolling → controlled cooling → coiling → finished product inspection → delivery.

[0028] in,

[0029] 1) Raw material process:

[0030] The molten iron is pretreated into the furnace with S≤0.003%, and the slag is removed; the fine material scrap is used;

[0031] 2) Converter process:

[0032] The converter pulls carbon ...

Embodiment 2

[0042] A hot-rolled ferritic and bainitic dual-phase steel strip for wheels with a tensile strength of 590MPa, including, by weight percentage, C 0.10%, Si 0.40%, Mn 1.70%, P≤0.020%, S≤0.004 %, Al 0.020%, Nb0.035%, Cr 0.40%, N≤0.0060, O≤0.0020%, the balance is Fe and unavoidable impurities.

[0043] According to another aspect of the present invention, a method for preparing a hot-rolled ferritic-bainite dual-phase steel strip for a wheel with a tensile strength of 590MPa is provided, including the following steps: molten iron pretreatment→converter smelting→LF+RH Refining outside the furnace → slab continuous casting → heating → rough rolling, finishing rolling → controlled cooling → coiling → finished product inspection → delivery.

[0044] in,

[0045] 1) Raw material process:

[0046] The molten iron is pretreated into the furnace with S≤0.003%, and the slag is removed; the fine material scrap is used;

[0047] 2) Converter process:

[0048] The converter pulls carbon on...

Embodiment 3

[0058] A hot-rolled ferritic and bainitic dual-phase steel strip for wheels with a tensile strength of 590MPa, including, by weight percentage, C 0.07%, Si 0.50%, Mn 1.46%, P≤0.020%, S≤0.004 %, Al 0.045%, Nb0.025%, Cr 0.30%, N≤0.0060, O≤0.0020%, and the balance is Fe and unavoidable impurities.

[0059] According to another aspect of the present invention, a method for preparing a hot-rolled ferritic-bainite dual-phase steel strip for a wheel with a tensile strength of 590MPa is provided, including the following steps: molten iron pretreatment→converter smelting→LF+RH Refining outside the furnace → slab continuous casting → heating → rough rolling, finishing rolling → controlled cooling → coiling → finished product inspection → delivery.

[0060] in,

[0061] 1) Raw material process:

[0062] The molten iron is pretreated into the furnace with S≤0.003%, and the slag is removed; the fine material scrap is used;

[0063] 2) Converter process:

[0064] The converter pulls car...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

Provided is a hot-rolled ferrite bainite dual-phase steel strip for a wheel with 590MPa class tension strength. The strip is prepared from, by weight, 0.05-0.10% of C, 0.40-0.70% of Si, 1.40-1.70% ofMn, P less than and equal to 0.020%, S less than and equal to 0.004%, 0.020-0.060% of Al, 0.015-0.035% of Nb, 0.20-0. 40% of Cr, N less than and equal to 0.0060, O less than and equal to 0.0020% and the balance of Fe and inevitable impurities. A preparation method is provided, and the method comprises the the following steps of hot metal pretreatment->converter smelting->LF+RH furnace refining->slab continuous casting->heating->rough rolling and finish rolling->control cooling->rolling->finished product inspection->factory leaving. The 590MPa class wheel steel has stable performance, effectively avoids an unsuited fatigue test which is often encountered in the use of a high-strength wheel steel, cracking of rim welding, thinning of a weld seam and cracking of a center hole of a spoke, andis a material ideal for light weight of the wheel.

Description

technical field [0001] The invention belongs to the technical field of steel product production, and in particular relates to a hot-rolled ferritic bainite dual-phase steel strip for wheels with a tensile strength of 590 MPa and a preparation method of the strip. Background technique [0002] With the continuous development requirements of energy saving and emission reduction and automobile lightweight, the lightweight of wheels has become an urgent development demand of the wheel industry. In order to reduce the weight of the wheel, steel with thinner material and higher strength is bound to be used. As the strength increases, the plasticity decreases, forming is difficult, the sensitivity to fatigue notch increases, and welding is difficult. The tensile strength level of 590MPa is currently the highest strength used in batches in the wheel industry. With the extensive use of this level of high-strength steel, some problems have gradually become prominent. One is the crac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/26C22C38/38C21D8/02
CPCC21D8/0226C21D2211/002C21D2211/005C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/26C22C38/38Y02P10/20
Inventor 刘志璞闵洪刚赵迪姜文超王旭生苗隽张城铭周晏锋
Owner BENGANG STEEL PLATES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap