SBR modified emulsified asphalt and preparation method thereof

A technology for emulsified asphalt and modification, applied in building components, building insulation materials, buildings, etc., can solve the problems of strict production equipment and process requirements, poor high-temperature performance, general low-temperature performance, etc., and achieve good low-temperature crack resistance. performance, improved high temperature performance, increased viscosity

Active Publication Date: 2021-10-26
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

SBS modified emulsified asphalt has the advantages of high temperature resistance and fatigue resistance, but the low temperature performance is average, the requirements for production equipment and technology are strict, and the cost performance is poor; SBR modified emulsified asphalt has a simple production process and has the advantages of low temperature crack resistance. But high temperature performance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • SBR modified emulsified asphalt and preparation method thereof
  • SBR modified emulsified asphalt and preparation method thereof
  • SBR modified emulsified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of SBR modified emulsified asphalt of the present invention, as figure 1 As shown, follow the steps below:

[0036] S1, weigh 66-69 parts of base asphalt according to the following parts by mass, 2-3 parts of CMK-50 cationic emulsifier, 3-4 parts of SBR styrene-butadiene latex, 0.2-0.4 parts of carboxymethyl cellulose (CMC), Anhydrous Calcium Chloride (CaCl 2 ) 0.2-0.4 parts, water 29-31 parts.

[0037] S2, heat the weighed base asphalt to a hot-melt state of 130-140°C, pour it into the asphalt tank, set the colloid mill speed to 9000-10000r / min, open the internal circulation system of the asphalt tank, and disperse the hot-melt asphalt into Homogeneous body; last for 25-35 minutes, the function is to disperse the hot-melt asphalt into a homogeneous body, which is beneficial to the emulsification effect.

[0038] S3, preparation of soap solution: heat water to 85-90°C, add carboxymethyl cellulose, stir with glass rod until carboxymethyl cellulo...

Embodiment 1

[0043] Example 1, SBR modified emulsified asphalt is composed of the following parts by mass: 66 parts of 70# heavy traffic asphalt, 3 parts of CMK-50 cationic emulsifier, 4 parts of SBR styrene-butadiene latex, 0.2 parts of carboxymethyl cellulose, no 0.4 parts of calcium chloride water, 31 parts of water.

Embodiment 2

[0044] Example 2, SBR modified emulsified asphalt is composed of the following parts by mass: 69 parts of 70# heavy traffic asphalt, 2 parts of CMK-50 cationic emulsifier, 3 parts of SBR styrene-butadiene latex, 0.4 parts of carboxymethyl cellulose, no 0.2 parts of calcium chloride water, 29 parts of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an SBR modified emulsified asphalt and a preparation method thereof. The SBR modified emulsified asphalt is composed of the following parts by mass: 66-69 parts of base asphalt, 2-3 parts of cationic emulsifier, and 3-3 parts of SBR styrene-butadiene latex 4 parts, 0.2-0.4 parts of carboxymethyl cellulose, 0.2-0.4 parts of anhydrous calcium chloride, 29-31 parts of water. The SBR modified emulsified asphalt of the invention has high storage stability, enhanced adhesion between asphalt and aggregate, good low-temperature ductility and excellent low-temperature crack resistance, and solves the problems existing in the prior art.

Description

technical field [0001] The invention belongs to the technical field of highway engineering, and relates to an SBR modified emulsified asphalt and a preparation method thereof. Background technique [0002] In my country, modified emulsified asphalt is widely used in road surface sealant mixture. Currently, the commonly used modified emulsified asphalt in sealant mixture includes SBS modified emulsified asphalt and SBR modified emulsified asphalt. SBS modified emulsified asphalt has the advantages of high temperature resistance and fatigue resistance, but the low temperature performance is average, the requirements for production equipment and technology are strict, and the cost performance is poor; SBR modified emulsified asphalt has a simple production process and has the advantages of low temperature crack resistance. But the high temperature performance is not good. How to obtain a modified emulsified asphalt with simple production process and good high and low temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L9/08C08L1/28C08K3/16
Inventor 孙志林马帅杰
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com