Efficient electrode for treating industrial circulating cooling water and preparation method of efficient electrode

A technology of circulating cooling water and electrodes, which is applied in water/sewage treatment, chemical instruments and methods, water/sludge/sewage treatment, etc. It can solve the problems of electrochemical activity, weak sterilization ability, high price and high energy consumption , to achieve the effect of increasing reactive sites, strong bactericidal ability and low energy consumption

Active Publication Date: 2019-08-09
HUANENG CLEAN ENERGY RES INST
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its price is expensive, its electrochemical activity and bactericidal ability are not strong, and its energy consumption is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient electrode for treating industrial circulating cooling water and preparation method of efficient electrode
  • Efficient electrode for treating industrial circulating cooling water and preparation method of efficient electrode

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the high-efficiency electrode for treating industrial circulating cooling water according to the present invention comprises the following steps:

[0032] 1) Select a titanium plate and pretreat the titanium plate;

[0033] 2) the first SnCl 4 ·5H 2 O and the soluble metal salt containing Ce are dissolved in the first organic solvent, and then aged to obtain the precursor solution A;

[0034] 3) the second part of SnCl 4 ·5H 2 O, SbCl 3 and RuCl 3 Dissolved in the second part of organic solvent, and then aged to obtain precursor solution B;

[0035] 4) Apply the precursor solution A to the titanium plate obtained by step 1) in stages, wherein, after each application of the precursor solution A, it is grilled and roasted to obtain Ti / Ce-SnO 2 electrode;

[0036] 5) Brush the precursor solution B onto the Ti / Ce-SnO obtained in step 4) 2 Electrodes, wherein, after each brushing is completed, it is baked and roasted to be used for processi...

Embodiment 1

[0050] The preparation method of the high-efficiency electrode for treating industrial circulating cooling water according to the present invention comprises the following steps:

[0051] 1) Select a titanium plate and pretreat the titanium plate;

[0052] 2) the first SnCl 4 ·5H 2 O and the soluble metal salt containing Ce are dissolved in the first organic solvent, and then aged to obtain the precursor solution A;

[0053] 3) the second part of SnCl 4 ·5H 2 O, SbCl 3 and RuCl 3 Dissolved in the second part of organic solvent, and then aged to obtain precursor solution B;

[0054] 4) Apply the precursor solution A to the titanium plate obtained by step 1) in stages, wherein, after each application of the precursor solution A, it is grilled and roasted to obtain Ti / Ce-SnO 2 electrode;

[0055] 5) Brush the precursor solution B onto the Ti / Ce-SnO obtained in step 4) 2 Electrodes, wherein, after each brushing is completed, it is baked and roasted to be used for processi...

Embodiment 2

[0067] The preparation method of the high-efficiency electrode for treating industrial circulating cooling water according to the present invention comprises the following steps:

[0068] 1) Select a titanium plate and pretreat the titanium plate;

[0069] 2) the first SnCl 4 ·5H 2 O and the soluble metal salt containing Ce are dissolved in the first organic solvent, and then aged to obtain the precursor solution A;

[0070] 3) the second part of SnCl 4 ·5H 2 O, SbCl 3 and RuCl 3 Dissolved in the second part of organic solvent, and then aged to obtain precursor solution B;

[0071] 4) Apply the precursor solution A to the titanium plate obtained by step 1) in stages, wherein, after each application of the precursor solution A, it is grilled and roasted to obtain Ti / Ce-SnO 2 electrode;

[0072] 5) Brush the precursor solution B onto the Ti / Ce-SnO obtained in step 4) 2 Electrodes, wherein, after each brushing is completed, it is baked and roasted to be used for processi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an efficient electrode for treating industrial circulating cooling water and a preparation method of the efficient electrode. The efficient electrode comprises a Ti matrix, a SnO2-Ce intermediate layer and a SnO2-Sb-Ru active layer which are distributed in sequence from top to bottom. The electrode has the advantages that the catalytic activity is high, the corrosion resistance stability is high, the bactericidal capacity is strong, the energy consumption is low, the preparation is relatively simple, and the cost is low.

Description

technical field [0001] The invention belongs to the technical field of electrochemical water treatment, and relates to a high-efficiency electrode for treating industrial circulating cooling water and a preparation method thereof. Background technique [0002] The circulating water system is one of the indispensable energy media for the production of metallurgy, energy and chemical enterprises. With the increase of the concentration ratio of circulating cooling water, the phenomenon of microbial reproduction, fouling and corrosion will appear in the system. In order to prevent the water quality from deteriorating indefinitely, on the one hand, part of the concentrated water must be discharged to supplement the clean water, and on the other hand, sterilization, anti-scaling and anti-corrosion treatment must be carried out. At present, the chemical agent method is generally used to control the quality of circulating cooling water. This method has problems such as high chemica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/461
CPCC02F1/46109C02F2001/46142
Inventor 王广任志博张畅余智勇
Owner HUANENG CLEAN ENERGY RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap