Treatment method for improving abrasion resistance and toughness of rotary blade

A treatment method and the technology of the rotary tiller, which are applied in plasma welding equipment, metal material coating technology, manufacturing tools, etc., can solve the problems that the right-angled rotary tiller is not suitable for paddy field farming, increases operating costs, and increases labor intensity, etc. , to achieve the effect of shortening the process interval, reducing labor intensity and high preheating time

Active Publication Date: 2019-12-24
安徽宏翔农业机械有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After World War II, Japan imported rotary tillers from Europe and the United States for agricultural production. However, because Japan mostly has paddy fields, right-angled rotary tillers are not suitable for paddy field farming. A large number of Japanese scholars began to devote themselves to the research and development of rotary tillers for paddy fields. Introduced the rotary tillage scimitar, and successfully solved the problems of the knife shaft following the grass
According to incomplete statistics, more than 80% of the soil-contacting parts of agricultural machinery are scrapped due to abrasive wear. The early failure of soil-contacting parts of agricultural machinery seriously affects the quality and efficiency of the operation, increases the operation cost, and frequently replaces the invalid tool. It also increases labor intensity, Delay in farming time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method for improving abrasion resistance and toughness of rotary blade

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A treatment method for improving the abrasion resistance and toughness of a rotary tiller, the specific method is as follows:

[0022] (1) Grind the rotary cultivator with a sand mill for 27s, the speed is 2500r / min, the sanding is rotating forward, the sharpening frequency is 60 times / min, the mass fraction is 4% water-based coolant to aid grinding, and the grinding pressure 150N, then cross-polished with water sandpaper with a particle size of 600 mesh at a 45° angle for 2 minutes, washed with deionized water for 4 times, and then put in ethyl diaminopropyl trimethoxy methacrylate with a weight ratio of 1.43:3.25 and The cleaning agent made of 8% acetic acid solution was ultrasonically treated for 60s, the treatment temperature was 34°C, the ultrasonic power was 200W, the frequency was 50kHz, the insulation was kept for 600s, and deionized water was used to clean twice, and then put into the Soak in an alkaline detergent made of sodium hydroxide and sodium tripolyphos...

Embodiment 2

[0032] A treatment method for improving the abrasion resistance and toughness of a rotary tiller, the specific method is as follows:

[0033] (1) Grind the rotary cultivator with a sand mill for 25s, the speed is 2300r / min, the sanding is rotating forward, the sharpening frequency is selected to be 50 times / min, the mass fraction is 3% water-based coolant to aid grinding, and the grinding pressure 140N, then use water sandpaper with a particle size of 400 mesh at a 45° angle to dip in water and cross-polish for 1min, then wash it with deionized water for 3 times, and then put in ethyl diaminopropyl trimethoxysilane methacrylate with a weight ratio of 1.3:3.25 and The cleaning agent made of 8% acetic acid solution was ultrasonically treated for 40s, the treatment temperature was 33°C, the ultrasonic power was 200W, the frequency was 50kHz, the insulation was kept for 580s, and deionized water was used to clean once, and then put into the Soak in an alkaline detergent made of so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of metal machining, in particular to a treatment method for improving abrasion resistance and toughness of a rotary blade, and belongs to the technical field of rotary blade machining. The treatment method has the advantages that the treatment method is simple, the cost is low, the rotary blade can be improved continuously without breaking and bending,wear resistance can be improved, the load of a tractor can be greatly reduced, the soil crushing capacity is high, the sharpness is high, the wear resistance is high, green and environmentally friendly and the like; and the requirement for fine tillage can be met, the working procedure interval is shortened, the replacement frequency of the rotary blade is reduced, and the working efficiency is improved, the strength is high, the toughness is good, the rotary blade is not only wear-resistant, but also does not break and bend when colliding hard objects such as bricks and stones.

Description

technical field [0001] The invention belongs to the technical field of rotary tiller blade processing, in particular to a treatment method for improving the abrasion resistance and toughness of the rotary tiller blade. Background technique [0002] The rotary tiller is a knife-shaped accessory for the rotary tiller used in farmland deflection. There are mainly two types of tillage machines used in the field: conventional plows and rotary tillers. The rotary tiller has the dual functions of plowing and harrowing, and plays an important role in agricultural machinery. The rotary tiller came out in the middle of the 19th century. It was not until the 1920s that Europe successfully developed the right-angled rotary tiller that the rotary tiller was popularized and used in Europe early. After World War II, Japan imported rotary tillers from Europe and the United States for agricultural production. However, because Japan mostly has paddy fields, right-angled rotary tillers are n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B23K10/02C23C22/62C23C22/78
CPCB23K10/027B23P15/00C23C22/62C23C22/78
Inventor 刘超曹成茂刘正元汪永武李梦龙王骏吴问天余飞端梦云
Owner 安徽宏翔农业机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap