Thermoplastic prepreg slurry based on slurry method and preparation method

A thermoplastic and prepreg technology, which is applied in the field of prepreg slurry, can solve the problems of poor stability of thermoplastic resin powder slurry, and achieve the effects of ensuring impregnation effect, improving stability, and facilitating concentration control

Inactive Publication Date: 2020-02-07
JIANGSU ZHAOJUN NEW MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of poor stability of thermoplastic resin powder slurry, the present invention provides thermoplast

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic prepreg slurry based on slurry method and preparation method
  • Thermoplastic prepreg slurry based on slurry method and preparation method
  • Thermoplastic prepreg slurry based on slurry method and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The slurry formula is shown in Table 1:

[0047] Table 1

[0048]

[0049]

[0050] Note: In the table, resin powder and deionized water are mixed as 100 parts (100%), and other additives are calculated separately due to the small amount of addition. The percentage of all additives is based on (the weight of resin powder and deionized water), that is, the percentage of the total amount of resin and deionized water, such as the amount of water-soluble polymer = (the weight of resin powder and deionized water)* 0.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses thermoplastic prepreg slurry based on a slurry method and a preparation method. The slurry is prepared from the following components in percentage by mass: 1-50% of thermoplastic resin, 50-95% of water, 0.1-10% of a water-soluble polymer, 0.01-5% of a surfactant and 0.1-10% of a viscosity reducing agent. The invention further discloses the preparation method of the slurry.According to the thermoplastic prepreg slurry and the preparation method, the viscosity of a system is increased and the stability of resin powder in water is improved by selecting the water-soluble polymer appropriate in type and dosage; moreover, the binding power of resin powder to fibers is increased; in combination with the viscosity reducing agent, the viscosity of the slurry system is adjusted and the stability of the slurry is improved, so that the concentration of the resin slurry is convenient to control and continuous production of a prepreg is achieved; in addition, the dipping effect can be guaranteed and the balance of the stability and the dipping effect is achieved.

Description

technical field [0001] The invention relates to a prepreg slurry, in particular to a thermoplastic prepreg slurry based on a mud method and a preparation method. Background technique [0002] With the demand for energy saving, emission reduction and light weight, the application of thermoplastic resin-based composite materials in the fields of automobiles and aerospace continues to develop, and continuous fiber-reinforced thermoplastic composite materials have gradually attracted attention. Thermoplastic resins have the advantages of high heat resistance, high toughness, and low water absorption. At room temperature, thermoplastic resins are mostly in the form of solid particles; in the molten state, the resin melt has high viscosity, difficult melt flow, and poor impregnation effect with fibers. The ultra-fine resin powder is evenly soaked and dispersed into the fiber bundle by the slurry method, and the resin is fully soaked into the fiber by heating. [0003] The core o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/02C08L29/04C08L71/02C08L83/04C08K13/02C08K5/053C08K5/05C08K3/015C08K5/00C08J3/07B29B7/00B29K105/00
CPCB29B7/005B29K2105/0011B29K2105/0038C08J3/07C08J2377/02C08J2429/04C08J2471/02C08J2483/04C08K5/0058C08K5/05C08K5/053C08K13/02C08K2201/014C08K3/015
Inventor 鲁平才薛胜张凤翻鲁兆鋆
Owner JIANGSU ZHAOJUN NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap