Three-dimensional jade ceramic tile and preparation method thereof

A three-dimensional, ceramic tile technology, which is applied in the field of ceramic tile preparation technology, can solve the problems of three-dimensional effect and poor texture of jade, and achieve rich decorative effects, high market price and wide application

Active Publication Date: 2020-04-17
佛山市禅城区科捷陶瓷原料有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problems of the three-dimensional effect of the existing ceramic tiles and the poor texture of jade, the present invention provides a three-dimensional jade ceramic tile and its preparation method, and prepares a kind of pattern lines with clear layers, three-dimensional internal texture, and a surface similar to Translucent, warm and soft jade ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-dimensional jade ceramic tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The preparation method of the three-dimensional three-dimensional jade ceramic tile of the present invention is as follows: first, batching is carried out according to the formula composition of the raw materials, after ball milling, sieving to remove iron, and spray granulation, the stale homogenization is carried out, and then the fabric is laid out in the form of digital fabric Layer and blank layer, because the ceramic tiles are pressed and formed in the way of anti-beating, so in the digital fabric, the fabric layer is first laid out and then the blank layer is laid out, and then pressed, dried, fired at high temperature, polished and waxed. Three-dimensional three-dimensional jade ceramic tiles.

[0028] The fabric layer is made of digital cloth. Firstly, the jade material is laid out in layers of different thicknesses according to the predetermined texture, and then the white material and high-temperature color material are laid out in different thickness layers a...

Embodiment 1

[0037] Weigh the jade material, white material and high-temperature color material according to the formula composition of the raw materials, and carry out stale homogenization after ball milling, sieving to remove iron, and spray granulation. / 100g glaze slurry, the moisture content of the dusting powder is 6.0%, the fineness of the powder is controlled: above 60 mesh ≤ 3%; 60-80 mesh: 45-55%; 80-100 mesh: 40-50%; below 100 mesh ≤5%; moisture is 5-6.5%. The fabric layer and the blank layer are laid out in the way of digital cloth, and three-dimensional jade ceramic tiles are obtained after pressing, drying, high-temperature firing, polishing and waxing.

[0038] The raw material composition of the jade material is calculated by weight: 40 parts of potassium feldspar, 5 parts of quartz, 18 parts of white clay, 15 parts of wollastonite, 2 parts of wollastonite, 20 parts of high temperature frit A; Composition: SiO2 69.18%; Al2O3 4.58%; K2O3.48%; Na2O 2.75%; CaO 9.40%; MgO 5.01...

Embodiment 2

[0042] Weigh the jade material, white material and high-temperature color material according to the formula composition of the raw materials, and carry out stale homogenization after ball milling, sieving to remove iron, and spray granulation. / 100g glaze slurry, the moisture content of the dusting powder is 6.0%, the fineness of the powder is controlled: above 60 mesh ≤ 3%; 60-80 mesh: 45-55%; 80-100 mesh: 40-50%; below 100 mesh ≤5%; moisture is 5-6.5%. The fabric layer and the blank layer are laid out in the way of digital cloth, and three-dimensional jade ceramic tiles are obtained after pressing, drying, high-temperature firing, polishing and waxing.

[0043] The raw material composition of the jade material is calculated by weight: 45 parts of potassium feldspar, 5 parts of quartz, 20 parts of white clay, 7 parts of wollastonite, 3 parts of wollastonite, 23 parts of high temperature frit A; Composed of: SiO 2 69.18%; Al 2 o 3 4.58%;K 2 O3.48%; Na 2 O 2.75%; CaO 9....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of ceramic tile preparation processes, and particularly discloses a three-dimensional jade ceramic tile and a preparation method thereof. According to theinvention, a surface material layer is made of digital cloth; jade materials are arranged in layers with different thicknesses according to preset textures, then white materials and high-temperature pigments are arranged in layers with different thicknesses according to preset textures, and the white materials, the high-temperature pigments and the jade materials are three-dimensionally arranged in multiple modes of overlapping, transition overlapping and non-overlapping; and the raw materials of the jade materials include, in parts by weight, 30-50 parts of potassium feldspar or albite, 0-15parts of quartz, 15-25 parts of clay, 5-30 parts of dolomite, 0-10 parts of wollastonite and 10-40 parts of a high-temperature frit A. The prepared three-dimensional jade ceramic tile is clear in pattern line layering and three-dimensional in internal texture, has a non-completely transparent surface, and feels warm, humid and soft.

Description

technical field [0001] The invention relates to the technical field of ceramic brick preparation technology, in particular to a three-dimensional three-dimensional jade ceramic brick and a preparation method thereof. Background technique [0002] Because of its good permeability and fine and soft texture, natural jade can be used as high-end decorations such as background walls and landscape decorations after polishing. , the internal texture is clearly visible, especially high-end and elegant. However, natural jade resources are limited and expensive, which cannot meet the needs of mass consumption. [0003] At present, there are some imitation jade materials on the market that are bonded with organic resin and stone powder, but their hardness is low, and their thermal stability and chemical stability are also poor. At the same time, with the continuous innovation of ceramic tile decoration technology, the effect of its surface pattern, color, and texture can also achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86C04B41/89C03C8/14C03C8/08
CPCC04B41/86C04B41/5022C04B41/89C04B41/52C03C8/14C03C8/08C03C8/04C04B41/50
Inventor 詹长春柯美云段椿肖荣杨海云陈宗玲邹美星
Owner 佛山市禅城区科捷陶瓷原料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com