A kind of normalizing dh36 steel plate for wind power and preparation method thereof

A DH36, steel plate technology, applied in the field of iron and steel metallurgy, can solve the problems of low pass rate of thick wind power steel plates, no relevant patents and reports retrieved, poor performance uniformity and stability, etc., to achieve low comprehensive production costs and improve internal Quality, Guaranteed Purity and Effects of Cleanliness

Active Publication Date: 2021-05-04
ZHANGJIAGANG HONGCHANG STEEL PLATE CO LTD +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Steel plates have high requirements for strength and toughness. The pass rate of thick-gauge wind power steel plates manufactured by existing methods is not high, and the performance uniformity and stability are also poor, making comprehensive production difficult.
[0004] No relevant patents and reports specifically for this type of steel for wind power have been retrieved so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of normalizing dh36 steel plate for wind power and preparation method thereof
  • A kind of normalizing dh36 steel plate for wind power and preparation method thereof
  • A kind of normalizing dh36 steel plate for wind power and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] The process route is as follows: Weigh the components as required to obtain molten iron, KR desulfurization of molten iron, converter smelting, LF refining, RH vacuum treatment, slab continuous casting, slab reheating, rough rolling, intermediate slab cooling, finish rolling , Rapid cooling of steel plate, off-line stack cooling, ultrasonic flaw detection, shot blasting, normalizing, accelerated cooling of steel plate. The control parameters of the smelting furnace and rolling process of this embodiment are shown in Table 1, the smelting composition of the smelting furnace is shown in Table 2, the control parameters of the heat treatment process are shown in Table 3, and the mechanical properties of the steel plate after heat treatment are shown in Table 4.

[0024] Table 1 Example smelting furnaces and rolling process control parameters

[0025]

[0026] Table 2 Example smelting furnace smelting composition

[0027] C％ Si% Mn% P％ S％ Nb% Ti% Al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a normalizing DH36 steel plate for wind power and a preparation method thereof. Weigh each component as required to get molten iron, molten iron KR mechanical stirring desulfurization, converter oxygen blowing smelting, LF refining, RH vacuum treatment, wire feeding, soft stirring, slab continuous casting, slab reheating, rough rolling, intermediate slab Waiting for warm cooling, finishing rolling, accelerated cooling, off-line stack cooling, ultrasonic flaw detection, shot blasting, normalizing, accelerated cooling of steel plates, fire cutting, storage. In the slab reheating stage, the heating temperature is controlled at 1150-1250°C, and the time in the furnace is not less than 1.0min / mm; the rough rolling temperature is controlled at 1000-1100°C, and the final rolling temperature is 860-900°C; the normalizing temperature of the steel plate is 880 ~900°C, the normalizing time in the furnace is not less than 2.0min / mm, and the cooling temperature after normalizing is 540‑600°C. The steel plate of the invention has good performance, low production cost, thick applicable thickness and good application prospect.

Description

technical field [0001] The invention relates to the field of iron and steel metallurgy, in particular to a normalizing DH36 steel plate for wind power and a preparation method thereof. Background technique [0002] With the rapid growth of economic development in demand for electricity and the requirements of sustainable green manufacturing, offshore wind power projects are increasing and the power of generator sets is increasing. The demand for steel plates for wind power is increasing and the thickness of steel plates is increasing. Technical requirements have also been tightened. In the past, Shagang produced more steel plates with a thickness of less than 60mm, and fewer steel plates with a thickness of 60-100mm. Moreover, alloy elements such as Ni, Cu, and V were added to steel plates with similar thick specifications, and the alloy content and carbon equivalent Ceq were higher. The high cost is not conducive to the market promotion and application of Shagang's wind po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C21D8/02C21D1/28C22C33/04
CPCC21D1/28C21D8/0226C21D2211/005C21D2211/009C22C33/04C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14
Inventor 赵辉聂文金郭桐李冉郭志龙林涛铸周子夜芮丰盛乔坤尚建雄叶俊文
Owner ZHANGJIAGANG HONGCHANG STEEL PLATE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com