A kind of anti-moisture absorption aqueous polyurethane dispersion and its preparation method and application

A polyurethane dispersion and moisture technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of spots, easy fogging on the surface, poor water resistance, etc. The effect of obvious function

Active Publication Date: 2022-04-15
XUCHUAN CHEM SUZHOU
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Purpose of the invention: The technical problem to be solved is to provide a moisture-absorbing water-based polyurethane dispersion to solve the problems in the prior art of water-based polyurethane coating resins such as poor water barrier, easy fogging or spots on the surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-moisture absorption aqueous polyurethane dispersion and its preparation method and application
  • A kind of anti-moisture absorption aqueous polyurethane dispersion and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0054] A kind of preparation method of anti-moisture absorption aqueous polyurethane dispersion, concrete steps are as follows:

[0055](1) Put polyether diol, polyether polyol with functionality ≥ 3, side chain alkane diol and polyisocyanate into the reaction kettle, stir evenly, add catalyst and solvent, react at 60-100°C for 1-2h, Obtain PU prepolymer;

[0056] (2) Cool down the PU prepolymer obtained in step (1) to 65°C, add a hydrophilic chain extender, a polyol chain extender and a solvent, then raise the temperature to 60-90°C, and continue the reaction for 3-6h;

[0057] (3) cool down and add solvent to dilute;

[0058] (4) When the temperature drops below 35°C, add a neutralizing agent and neutralize for 10-30 minutes;

[0059] (5) under high-speed stirring, the PU prepolymer obtained in step (4) is dispersed in water to obtain a PU dispersion;

[0060] (6) The amine chain extender is prepared into an aqueous solution with a mass fraction of 5-40%, added to the PU ...

Embodiment 4

[0070] Surface component quality Function / manufacturer Waterborne Polyurethane Dispersion 95 Silok 8000 0.5 Wetting agent / Sloco Silok 8144 0.3 Leveling agent / Sloco UH-450VF 2 Thickener / Addico XWB-F115 0.3 Curing agent / Asahikawa KA-920 2 Color paste / Kai Shiai

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an anti-moisture absorption water-based polyurethane dispersion and a preparation method and application thereof, belonging to the field of water-based polyurethane coating resins. In the present invention, polyether diol, polyether polyol with a functionality ≥ 3, side chain alkane diol and polyisocyanate are reacted together to obtain a prepolymer, and then a chain extender is added to continue the reaction to obtain a moisture-absorbing water-based polyurethane coating A resin dispersion, the water-based polyurethane coating resin can be prepared by using the moisture-absorbing water-based polyurethane coating resin dispersion. The water-based polyurethane coating resin finally prepared by the present invention has the characteristics of being able to block water vapor and not fogging when wet.

Description

Technical field: [0001] The invention belongs to the technical field of water-based polyurethane coating resin, and in particular relates to a moisture-absorbing water-based polyurethane coating resin and its preparation method and application. Background technique: [0002] Waterborne polyurethane is widely used in coatings, adhesives, leather finishing agents and fabric coatings due to its non-toxic and environmentally friendly characteristics. The film-forming process of water-based polyurethane belongs to the fusion of multi-phase systems, which can well reflect its air and moisture permeability in the application field. However, when in use, liquids such as water, beverages, blood, and urine can easily penetrate into the back of the water-based polyurethane coating, making cleaning such as printing difficult. Therefore, improving the water-permeable and air-permeable properties of water-based polyurethane coatings can greatly expand the application of water-based polyu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/48C08G18/12C08G18/34C08G18/32C09D175/08
CPCC08G18/7614C08G18/7671C08G18/4812C08G18/4854C08G18/4825C08G18/12C08G18/34C08G18/32C09D175/08C08G18/348C08G18/3206C08G18/3228
Inventor 高强郭艳欣陈亚磊朱小强张大华
Owner XUCHUAN CHEM SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap