A kind of production process of small particle size mechanism blue charcoal barbecue carbon
A production process and a technology for grilling charcoal, which is applied in the field of production technology of small particle size machine-made blue charcoal grilling charcoal, and can solve the problem of high production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] A kind of production technology of small particle size mechanism blue charcoal barbecue carbon, its specific preparation scheme is as follows:
[0032] Add 15kg of magnesium oxide, 6kg of manganese carbonate, 1.2kg of calcium oxide and 0.5kg of sodium acetate into the reaction kettle, stir and mix evenly, add 0.8kg of boron mud and 8kg of surface-modified rice husk fiber, control the temperature at 90°C, and stir for 5 hours After the completion, the temperature is controlled at 120°C and dried for 60 minutes, and then heat-treated at 200°C for 120 minutes to obtain a desulfurizing agent; the obtained desulfurizing agent is mixed with 1000kg of pulverized coal particles, 5kg of oxidant and 40kg of 3% high-efficiency binder After the solution is mixed evenly, it is heat-preserved at 100° C. for 10 minutes. After the completion, it is punched and formed at 6 MPa. After drying, the above-mentioned small particle size machine-made blue charcoal barbecue carbon can be obtaine...
Embodiment 2
[0044] A kind of production technology of small particle size mechanism blue charcoal barbecue carbon, its specific preparation scheme is as follows:
[0045] Add 28kg of magnesium oxide, 8kg of manganese carbonate, 2.4kg of calcium oxide and 2.5kg of sodium acetate into the reaction kettle, stir and mix evenly, add 1.2kg of boron mud and 10kg of surface-modified rice husk fiber, control the temperature at 100°C, and stir for 8 hours After the completion, the temperature is controlled at 130°C and dried for 90 minutes, and then heat-treated at 240°C for 150 minutes to obtain a desulfurizing agent; the obtained desulfurizing agent is mixed with 1400kg of pulverized coal particles, 8kg of oxidant and 50kg of 6% high-efficiency binder After the solution is mixed evenly, it is heat-preserved at 120° C. for 30 minutes. After the completion, it is punched and formed at 9 MPa. After drying, the above-mentioned small-sized mechanical blue charcoal barbecue carbon can be obtained.
[0...
Embodiment 3
[0057] A kind of production technology of small particle size mechanism blue charcoal barbecue carbon, its specific preparation scheme is as follows:
[0058] Add 36kg of magnesium oxide, 9kg of manganese carbonate, 3.6kg of calcium oxide and 5kg of sodium acetate into the reaction kettle, stir and mix evenly, add 1.6kg of boron mud and 12kg of surface-modified rice husk fiber, control the temperature at 120°C, and stir for 10 hours. After completion, the temperature is controlled at 150°C and dried for 120 minutes, and then heat-treated at 300°C for 180 minutes to obtain a desulfurizing agent; the obtained desulfurizing agent is mixed with 1800 kg of pulverized coal particles, 10 kg of oxidant and 60 kg of 10% high-efficiency binder solution After mixing evenly, heat-preserve at 150°C for 60 minutes, press and form at 12MPa after completion, and dry to obtain the small particle size machine-made blue charcoal barbecue carbon.
[0059] Described high-efficiency adhesive is a k...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More