Preparation process of bamboo composite board

A preparation process and technology for composite boards, which are applied in the field of bamboo products, can solve the problems of general performance and weak interface bonding of bamboo composite boards, and achieve the effects of improving mechanical properties, enhancing plasticization bonding, and promoting mechanical properties.

Inactive Publication Date: 2020-12-11
阜南县德盛隆工艺家具有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Bamboo composite panels have been processed and applied. However, due to the weak interfacial bonding b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] A kind of bamboo composite board preparation technology, comprises the following steps:

[0074] (1) Bamboo powder preparation:

[0075] Bamboo is pulverized to obtain bamboo powder, after the bamboo powder obtained is mixed with grinding liquid, then ground for 2 hours, then dried to obtain ground bamboo powder; the grinding liquid is mixed with organic alcohol, deionized water and tartrate Made; the mixing ratio of the bamboo powder and the grinding liquid is 200g: 200mL. The mixing weight ratio of organic alcohol, deionized water and tartrate in the grinding liquid is 15:15:1.2. The organic alcohol is formed by mixing ethanol and glycerol in a mass ratio of 10:1. Described tartrate is sodium tartrate.

[0076] (2) Preparation of treatment solution:

[0077] Treatment liquid a preparation:

[0078] Adding ethanol, amide compounds, and water together in sequence, and stirring evenly, to obtain treatment liquid a;

[0079] Preparation of treatment solution b: Mix ac...

Embodiment 2

[0087] A kind of bamboo composite board preparation technology, comprises the following steps:

[0088] (1) Bamboo powder preparation:

[0089] Bamboo is pulverized to obtain bamboo powder, and the obtained bamboo powder is mixed with grinding liquid, then ground for 3 hours, and then dried to obtain ground bamboo powder; the grinding liquid is mixed with organic alcohol, deionized water and tartrate Made; the mixing ratio of the bamboo powder and the grinding liquid is 200g: 250mL. The mixing weight ratio of organic alcohol, deionized water and tartrate in the grinding liquid is 15:15:1.2. The organic alcohol is formed by mixing ethanol and glycerol in a mass ratio of 10:1. Described tartrate is sodium tartrate.

[0090] (2) Preparation of treatment solution:

[0091] Treatment liquid a preparation:

[0092] Adding ethanol, amide compounds, and water together in sequence, and stirring evenly, to obtain treatment liquid a;

[0093] Preparation of treatment solution b: Mi...

Embodiment 3

[0101] A kind of bamboo composite board preparation technology, comprises the following steps:

[0102] (1) Bamboo powder preparation:

[0103] Bamboo is pulverized to obtain bamboo powder, and the obtained bamboo powder is mixed with grinding liquid, then ground for 2.5 hours, and then dried to obtain ground bamboo powder; the grinding liquid is mixed with organic alcohol, deionized water and tartrate Made; the mixing ratio of the bamboo powder and the grinding liquid is 200g: 220mL. The mixing weight ratio of organic alcohol, deionized water and tartrate in the grinding liquid is 15:15:1.2. The organic alcohol is formed by mixing ethanol and glycerol in a mass ratio of 10:1. Described tartrate is sodium tartrate.

[0104] (2) Preparation of treatment solution:

[0105] Treatment liquid a preparation:

[0106] Adding ethanol, amide compounds, and water together in sequence, and stirring evenly, to obtain treatment liquid a;

[0107] Preparation of treatment solution b: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of a bamboo composite board. The preparation method comprises the following steps: (1) preparing bamboo powder; (2) preparing a treating fluid; (3) performing primary vacuum treatment; (4) performing vacuum secondary treatment; and (5) performing hot pressing; According to the method, the bamboo powder is subjected to vacuum treatment by adopting a treatment liquid a and a treatment liquid b respectively, the obvious purification effect on the bamboo powder can be achieved, the content of polar compounds such as friedelin, oleic acid, gamma-sitosterol, hexadecanoic acid and 2,3-dihydrobenzofuran in the bamboo powder is reduced through combination of two times of treatment, and the internal organization structure of the bamboo powder is greatlyimproved.

Description

technical field [0001] The invention belongs to the technical field of bamboo products, in particular to a preparation process of a bamboo composite board. Background technique [0002] The existing plate has poor balance between strength, hardness, density and flatness, and has a low reuse rate. And the planks are mostly made of solid wood boards or bamboo boards, which consume a lot of wood. Due to the use of a large amount of wooden boards, forest resources are even more scarce. The regeneration cycle of bamboo is relatively short, and its wood density and hydrophobicity are better than wood, so consider using bamboo boards instead of wood boards. [0003] Bamboo has a short growth cycle and strong renewability. In the process of production and use, it is environmentally friendly and is an important forest resource next to wood. In recent years, the wide use of bamboo has not only effectively alleviated the contradiction between wood supply and demand, but also promoted ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L97/02C08L27/06C08H8/00
CPCC08H8/00C08L27/06C08L97/02
Inventor 马淼
Owner 阜南县德盛隆工艺家具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap