Positive electrode lithium supplementing material and lithium ion battery comprising same

A technology for lithium ion batteries and positive electrodes, which is applied in the field of positive electrode lithium supplement materials and their preparation, can solve the problems of poor surface structure stability and high residual alkali value, and achieve the effects of improving energy density, reducing residual alkali value, and inhibiting gas production.

Pending Publication Date: 2021-07-27
ZHUHAI COSMX BATTERY CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to improve the prior art Li 2 NiO 2 The material has relatively high residual alkali value and poor surface structure stability, etc., the present invention provides a positive electrode lithium supplement material and a lithium ion battery comprising the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Positive electrode lithium supplementing material and lithium ion battery comprising same
  • Positive electrode lithium supplementing material and lithium ion battery comprising same
  • Positive electrode lithium supplementing material and lithium ion battery comprising same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) According to Li 2 CO 3 with NiCO 3 The molar ratio of 1.05:1.0 weighs 148.38g Li 2 CO 3 , 227.02gNiCO 3 Perform high-speed mixing;

[0050] (2) The mixture is synthesized once in a muffle furnace, and oxygen is introduced into the muffle furnace. The synthesis is carried out in three stages, the synthesis temperature is 500°C / 5h in the low temperature stage; 720°C / 5h in the middle temperature stage; 800°C / 10h in the high temperature stage;

[0051] (3) After the muffle furnace is naturally cooled, the material is taken out and passed through a 300-mesh sieve to obtain Li 2 NiO 2 ;

[0052] (4) Li will be obtained 2 NiO 2 Same as nanoscale ZrO 2 Mix evenly with a high mixer, where ZrO 2 The amount according to Li 2 NiO 2 0.135wt%, sintered at 600°C for 5 hours in an oxygen atmosphere, cooled naturally and took out the material to pass through a 300-mesh sieve to obtain the target ZrO 2 Coated Li 2 NiO 2 , denoted as Li 2 NiO 2 @ZrO 2 .

[0053] F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a positive electrode lithium supplementing material and a lithium ion battery comprising the positive electrode lithium supplementing material, the lithium supplementing material is coated in a special surface coating mode, and the purposes of stabilizing the stability of the surface structure of the material and reducing the residual alkali value are achieved. Meanwhile, the problems that a large amount of gas is easily generated in the charging and discharging process, the structure is unstable, and then a series of side reactions are caused can be solved. Zirconium dioxide is adopted as a coating layer and coats the surface of Li2NiO2, on one hand, zirconium dioxide is used as a non-active material, has a porous structure and inhibits erosion of HF in an electrolyte to protect a Li2NiO2 body material, and meanwhile, free deintercalation of lithium ions can be allowed; on the other hand, the reaction with residual lithium on the surface of Li2NiO2 is carried out, the residual alkali value of the material is reduced, and the gas production problem of the battery is effectively inhibited, so that a stable surface structure is obtained.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, and mainly relates to a positive electrode lithium supplement material, a preparation method thereof and a lithium ion battery comprising the positive electrode lithium supplement material. Background technique [0002] At present, during the first charging process of commercial lithium-ion batteries, about 10wt% of the active lithium in the positive electrode material is consumed, and an irreversible and stable SEI film is formed on the surface of the negative electrode, resulting in irreversible capacity loss, which in turn leads to a decrease in the energy density of lithium-ion batteries. . In response to this problem, the loss of this part of irreversible capacity can usually be eliminated by supplementing lithium at the positive electrode, and the energy density and other electrical properties of the battery can be improved. [0003] For example by choosing Li 2 NiO 2 mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/525H01M4/48H01M4/36H01M4/1391H01M4/131H01M4/04H01M10/0525
CPCH01M4/525H01M4/131H01M4/366H01M4/0471H01M4/483H01M4/1391H01M2004/028H01M10/0525Y02E60/10
Inventor 伍鹏曾家江李素丽
Owner ZHUHAI COSMX BATTERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap