A kind of nickel-containing sludge sintering pretreatment method

A pretreatment and sludge technology, applied in the direction of improving process efficiency, etc., can solve the problems of high chromium content of sintered agglomerates, low pelleting strength, poor agglomeration strength, etc., to reduce processing costs, improve sintering efficiency, and agglomerate rate-boosting effect

Active Publication Date: 2022-02-22
BEIJING GEOENVIRON ENG & TECH +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned problems, the present invention solves the low pelletizing strength and uneven particle size faced by the existing nickel-containing sludge sintering pretreatment process, slow burning on the material layer during the sintering process, low efficiency, small processing capacity, low agglomeration rate, Due to technical problems such as poor agglomeration strength and excessive chromium content in sintered agglomerates, the present invention proposes a sintering pretreatment method for nickel-containing sludge, including:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nickel-containing sludge sintering pretreatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The moisture content of the nickel-containing sludge after drying is 24%, the organic matter content of the copper-containing sludge after drying is 33%, and the laterite nickel ore SiO 2 The content is 43%; in the mixture, the nickel-containing sludge after drying accounts for 50%, the copper-containing sludge after drying accounts for 40%, and the laterite nickel ore accounts for 10%. The fuel used is coke powder with a fixed carbon content of 81.2%, and the added weight ratio is 15.00% of the mass of the mixture. Using a disc granulator to produce balls with a particle size of 10mm-20mm, the balls are fed into a horizontal sintering furnace for sintering. The daily processing capacity is 126 tons, and the agglomeration rate is 74.5%. The chromium content of the sintered agglomerate is 2.15%.

Embodiment 2

[0030] The moisture content of the nickel-containing sludge after drying is 35%, the organic matter content of the copper-containing sludge after drying is 31%, and the laterite nickel ore SiO 2 The content is 38%; the dried nickel-containing sludge in the mixture accounts for 60%, the dried copper-containing sludge accounts for 30%, and the laterite nickel ore accounts for 10%. The fuel used is coke powder with a fixed carbon content of 81.2%, and the addition ratio is 15.30% of the mass of the mixture. Using a disc granulation machine to produce balls with a particle size of 10mm-20mm, the balls are fed into a horizontal sintering furnace for sintering. The daily processing capacity is 117 tons, and the agglomeration rate is 74.2%. The chromium content of the sintered agglomerate is obtained. 2.37%.

Embodiment 3

[0032] The moisture content of the nickel-containing sludge after drying is 41%, the organic matter content of the copper-containing sludge after drying is 28%, and the laterite nickel ore SiO 2 The content is 33%. In the mixture, the nickel-containing sludge after drying accounts for 60%, the copper-containing sludge after drying accounts for 25%, and the laterite nickel ore accounts for 15%. The fuel used is coke powder, with a fixed carbon content of 81.2%, and the addition ratio is 15.75% of the mass of the mixture. Using a disc granulation machine to produce balls with a particle size of 10mm-20mm, the balls are fed into a horizontal sintering furnace for sintering. The daily processing capacity is 110 tons, and the agglomeration rate is 80.2%. The chromium content of the sintered block is obtained. 2.03%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a sintering pretreatment method for nickel-containing sludge, which belongs to the technical field of nickel-containing sludge pretreatment, and comprises drying the nickel-containing sludge; combining the dried nickel-containing sludge with the dried copper-containing sludge Mix mud, laterite nickel ore and fuel to obtain a mixture; pelletize the mixture to obtain a spherical mixture; put the spherical mixture into the sintering equipment for sintering to obtain agglomerates; dry the nickel-containing sludge and dry The mass ratio of dry copper-containing sludge and laterite nickel ore is 5-7 parts: 2-4 parts: 1-2 parts, and the fuel quality is 15%-18% of the mixture quality. The present invention adds dried copper-containing sludge and laterite nickel ore, and the content of metal chromium in the obtained agglomerate is significantly reduced, and can be stabilized below 2.50%, and the adverse effect on the subsequent smelting process is significantly reduced.

Description

technical field [0001] The invention belongs to the technical field of nickel sludge pretreatment, in particular to a sintering pretreatment method of nickel-containing sludge. Background technique [0002] Nickel-containing sludge mainly comes from the wastewater treatment process of the metal surface treatment industry, which often contains a variety of heavy metals, with complex components and a moisture content as high as 60% to 70%. Heavy metal hydroxides such as nickel, copper, and chromium in nickel-containing sludge are in an unstable state. If they are randomly stacked, heavy metals are likely to dissolve again under the action of rainwater leaching, polluting soil or groundwater, and causing environmental and ecological damage. harm. Therefore, this type of sludge has been included in the "National Hazardous Waste List" (2021 Edition), and the hazardous waste category is HW17 (surface treatment waste). On the other hand, with the depletion of mineral resources, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/16C22B7/00C22B23/00
CPCC22B1/16C22B23/005C22B7/00Y02P10/20
Inventor 刘超霍成立杨文明王荀黄仙王志平庞杰
Owner BEIJING GEOENVIRON ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com