Lightweight polyurethane elastomer as well as manufacturing method and application thereof

A polyurethane elastomer and lightweight technology, which is applied in the field of polyurethane materials to achieve excellent mechanical properties, ensure lightweight, and reduce density

Active Publication Date: 2022-04-19
广东安拓普聚合物科技股份有限公司
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Although the existing technology has given some solutions to the lightweight of polyurethane elastomers, most of them are aimed at the application of shoe sole materials
However, there are no relevant reports on the application of various line cables such as automotive application cables and optical fiber cables. Due to different application scenarios, polyurethane elastomers used in automotive application cables, optical fiber cables, etc. need better mechanical properties. , and at the same time need to take into account a certain flame retardant performance and lightweight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight polyurethane elastomer as well as manufacturing method and application thereof
  • Lightweight polyurethane elastomer as well as manufacturing method and application thereof
  • Lightweight polyurethane elastomer as well as manufacturing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment and

[0067] The preparation method of embodiment and comparative example polyurethane elastomer:

[0068] 1) At 40°C, mix and stir the isocyanate component A and the isocyanate-reactive component B respectively for further use;

[0069] 2) At 40°C, the isocyanate component A and the isocyanate-reactive component B are uniformly mixed by a high-speed mixer, and then poured into a mold at 140°C. After reaction curing molding, demoulding, and aging, light weight can be obtained Quantification of polyurethane elastomers. The raw materials used in Examples and Comparative Examples are listed in Table 1.

[0070] Table 1 embodiment and comparative example raw material data table (mass parts)

[0071]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a light-weight polyurethane elastomer as well as a manufacturing process and application thereof. The polyurethane elastomer is obtained by reacting an isocyanate component and an isocyanate reactive component, the isocyanate reactive component comprises polyether polyol 1, polyether polyol 2, a chain extender, a cross-linking agent, a catalyst, white phosphorus calcium stone, a dispersing agent and hollow microspheres. On the basis of low density and light weight, the polyurethane elastomer disclosed by the invention also has excellent mechanical property and flame retardant property, and can be used for various line cables such as automobile application cables, optical fiber cables and the like.

Description

technical field [0001] The invention relates to the field of polyurethane materials, in particular to a lightweight polyurethane elastomer and its manufacturing method and application. Background technique [0002] Polyurethane elastomer has a unique structure of soft and hard block copolymers. This structure makes polyurethane elastomers have high strength, high elasticity, good wear resistance, oil resistance, low temperature softness, high elongation, and good corrosion resistance. Excellent performance. At the same time, it has both the high elasticity of rubber and the ease of processing of plastics. It has been widely used in shoe materials, plates, pipes, films, cables, auto parts, medical treatment, sports and leisure and other fields. In recent years, due to the growing demand for lightweight materials, the development of lightweight polyurethane elastomers has become a current research hotspot. [0003] Patent CN102660113B discloses a thermoplastic polyurethane m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08G18/20C08K3/32C08J9/32C08L75/08
CPCC08G18/6685C08G18/4812C08G18/4816C08G18/3206C08G18/3228C08G18/2063C08K3/32C08J9/32C08J2375/08C08J2203/22
Inventor 刘悦钟荣栋李同兵
Owner 广东安拓普聚合物科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap