A kind of ceramic glaze and glaze technology, applied in the field of ceramic manufacturing, can solve the problems of few red pigments, dark colors, high prices, etc.
Pending Publication Date: 2022-06-03
武汉甄美颜料有限公司
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although red glazes are widely loved by the masses, it is difficult to manufacture high-quality red glazes due to the small number of red pigments required for the manufacture of red glazes and poor high temperature stability.
Commonly used red pigments for glazes are only a few types such as Dahong, Yuanzihong and Iron Oxide Red. Among them, the red glaze produced by Dahong has the best quality, bright color and high glaze brightness, but the price is very expensive; The red glaze produced by Yuanzihong pigment is also of good quality and bright glaze, but its color is too purple, not the red favored by Chinese people, and the price is relatively expensive; although iron oxide red pigment is cheap, but because of its chemical Poor stability and easy to change color at high temperature. The existing technology uses iron red as the chromogenic agent to produce low-grade red glaze. Not only is the color dark, but the glaze has low brightness and poor thermal shock resistance, making it difficult to achieve high-quality red. Quality requirements for glazes
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] Top Glaze Base Glaze Composition: Feldspar 47.3 Frit 21.3 Kaolin 7 Calcite 10 Quartz 15
[0050] Product: Bright glaze, dark red color, good thermal stability.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a preparation method of red ceramic glaze. The preparation of the high-grade red glaze is realized by increasing the use amount of the iron oxide red pigment and a double-layer glaze process. The red ceramic glaze prepared by the invention is bright in color, bright in glaze surface, high in thermal shock resistance and low in price. The usage amount of the iron oxide red is more than 12%, preferably 16-30%, preferably 20-25%, and especially more than 40%.
Description
1. Technical field [0001] The invention belongs to the field of ceramic manufacturing, and particularly relates to a preparation method of red ceramic glaze. 2. Background technology [0002] Ceramic glaze is one of the important components of ceramics, which plays an important role in strengthening, anti-corrosion, dustproof and beautifying utensils. According to different colors, ceramic glazes are divided into blue glazes, black glazes, yellow glazes, red glazes, gray glazes and brown glazes. Among them, red glazes are the most widely used ceramic glazes. Compared with other color glazes, red glaze has always been favored by the Chinese due to the influence of traditional aesthetic concepts, and it is one of the most widely used color glaze varieties. Although red glaze is widely loved by the masses, it is difficult to manufacture high-quality red glaze due to the small variety of red pigments required for the manufacture of red glaze and poor high temperature stability....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.