Low-halogen flame-retardant PP (polypropylene) material as well as preparation method and application thereof
A flame retardant, phosphorus nitrogen flame retardant technology, applied in the field of polymer modified materials, can solve the problem of not being able to maintain a good impact strength retention rate, and achieve good impact performance retention rate, low dosage, and good flame retardant performance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~4
[0061] A low-halogen flame-retardant PP material, in parts by weight, includes the components shown in Table 1 below.
[0062] Table 1
[0063] serial number Example 1 Example 2 Example 3 Example 4 PP resin-1 80 98 85 96 Phosphorus nitrogen flame retardant-1 3 0.5 3 0.5 Halogenated flame retardant-1 0.025 0.1 0.030 0.035
[0064] The specific preparation methods of the low-halogen flame-retardant PP materials of the above-mentioned embodiments 1-4 are as follows:
[0065] The PP resin, phosphorus nitrogen flame retardant and halogenated flame retardant are put into the first section of the twin-screw extruder according to the proportion. After being heated and melted by the twin-screw extruder, they are extruded into strips through the die. Then water-cooled and air-dried, and cut into pellets to obtain a low-halogen flame-retardant PP material.
Embodiment 5
[0067] A low-halogen flame retardant PP material, in parts by weight, includes the same components and contents as those in Example 3, except that the phosphorus-nitrogen flame retardant is phosphorus-nitrogen flame retardant-2.
[0068] The specific preparation method of the low halogen flame retardant PP material is the same as that in Example 3.
Embodiment 6
[0070] A low-halogen flame retardant PP material, in parts by weight, includes the same components and contents as those in Example 3, except that the phosphorus-nitrogen flame retardant is phosphorus-nitrogen flame retardant-3.
[0071] The specific preparation method of the low halogen flame retardant PP material is the same as that in Example 3.
PUM

Abstract
Description
Claims
Application Information

- Generate Ideas
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com