Abstract

The invention provides the formulation and method for preparing encaustic concrete tile by using attle, wherein the formula of the raw material include (by weight parts): attle 53-58, cement (P.O 42.5#) 29-33, additive (TW-3 high efficiency water reducing agent) 0.5-1, and balancing water.

Description

technical field

[0001] The invention relates to a raw material formula and method for producing concrete colored tiles from stone chips. Background technique

[0002] With the rapid development of my country's construction industry, people put forward higher requirements for housing construction. Not only should there be neat streets, beautiful squares, and large green areas, but also a colorful roof to make the buildings colorful and beautify the environment and life. According to the national policy, sloping roofs and colored roofs will be vigorously developed. The Ministry of Construction has already clearly stipulated that in the future, at least 30% of urban buildings must use sloping roofs to improve the waterproof, heat insulation, and heat preservation functions of buildings and beautify the environment.

[0003] Colored concrete tiles not only have high strength, light weight, waterproof, drainage and other functions, but also have the advantages of low production ...

Examples

Embodiment 1

[0027] Embodiment 1: Utilize stone chip to produce the raw material formula of concrete colored tile, proportion by weight:

[0028] Stone chips with a particle diameter of 1 to 5 mm 53

[0029] Cement (P.O 42.5#) 33

[0030] Admixture (TW-3 superplasticizer) 1

[0031] water 13.

[0032] The method for utilizing stone chips to produce concrete colored tiles comprises the following steps:

[0033] a. Concrete preparation:

[0034] a) First sieve the stone chip waste residue with a 1mm / hole sieve to remove the fine powder smaller than 1mm; then use a 5mm / hole sieve to remove the coarse slag larger than 5mm, and take the remaining stone chips in the middle sieve;

[0035] b) Put a predetermined amount of stone chips after sieving into the concrete mixer, and start mixing for 4 to 5 minutes;

[0036] c) Put a predetermined amount of cement into the stone chips after stirring, and start stirring for 1 to 2 minutes;

[0037] d) Add a predetermined amount of water dissolved wi...

Embodiment 2

[0044] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0045] Stone chips with a particle diameter of 1-5mm 55

[0046] Cement (P.O 42.5#) 31

[0047] Admixture (TW-3 superplasticizer) 0.8

[0048] water 13.2.

[0049] Its production method is identical with embodiment 1.

[0050] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0051] Stone chips with a particle diameter of 1-5mm 55

[0052] Cement (P.O 42.5#) 31

[0053] Admixture (TW-3 superplasticizer) 0.8

[0054] water 13.2.

[0055] Its production method is identical with embodiment 1.

Embodiment 3

[0056] Embodiment 3: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0057] Particle diameter 1 ~ 5mm stone chips 58

[0058] Cement (P.O 42.5#) 29

[0059] Admixture (TW-3 superplasticizer) 0.5

[0060] water 12.5.

[0061] Its production method is identical with embodiment 1.

technical field

[0001] The invention relates to a raw material formula and method for producing concrete colored tiles from stone chips. Background technique

[0002] With the rapid development of my country's construction industry, people put forward higher requirements for housing construction. Not only should there be neat streets, beautiful squares, and large green areas, but also a colorful roof to make the buildings colorful and beautify the environment and life. According to the national policy, sloping roofs and colored roofs will be vigorously developed. The Ministry of Construction has already clearly stipulated that in the future, at least 30% of urban buildings must use sloping roofs to improve the waterproof, heat insulation, and heat preservation functions of buildings and beautify the environment.

[0003] Colored concrete tiles not only have high strength, light weight, waterproof, drainage and other functions, but also have the advantages of low production ...

Examples

Embodiment 1

[0027] Embodiment 1: Utilize stone chip to produce the raw material formula of concrete colored tile, proportion by weight:

[0028] Stone chips with a particle diameter of 1 to 5 mm 53

[0029] Cement (P.O 42.5#) 33

[0030] Admixture (TW-3 superplasticizer) 1

[0031] water 13.

[0032] The method for utilizing stone chips to produce concrete colored tiles comprises the following steps:

[0033] a. Concrete preparation:

[0034] a) First sieve the stone chip waste residue with a 1mm / hole sieve to remove the fine powder smaller than 1mm; then use a 5mm / hole sieve to remove the coarse slag larger than 5mm, and take the remaining stone chips in the middle sieve;

[0035] b) Put a predetermined amount of stone chips after sieving into the concrete mixer, and start mixing for 4 to 5 minutes;

[0036] c) Put a predetermined amount of cement into the stone chips after stirring, and start stirring for 1 to 2 minutes;

[0037] d) Add a predetermined amount of water dissolved wi...

Embodiment 2

[0044] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0045] Stone chips with a particle diameter of 1-5mm 55

[0046] Cement (P.O 42.5#) 31

[0047] Admixture (TW-3 superplasticizer) 0.8

[0048] water 13.2.

[0049] Its production method is identical with embodiment 1.

[0050] Embodiment 2: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0051] Stone chips with a particle diameter of 1-5mm 55

[0052] Cement (P.O 42.5#) 31

[0053] Admixture (TW-3 superplasticizer) 0.8

[0054] water 13.2.

[0055] Its production method is identical with embodiment 1.

Embodiment 3

[0056] Embodiment 3: Utilize stone chip to produce the raw material formula of concrete color tile, proportion by weight:

[0057] Particle diameter 1 ~ 5mm stone chips 58

[0058] Cement (P.O 42.5#) 29

[0059] Admixture (TW-3 superplasticizer) 0.5

[0060] water 12.5.

[0061] Its production method is identical with embodiment 1.