High-white transparent material formulation and manufacture method of crystal full transparency polishing brick

A technology for polishing tiles and ice crystals, applied in the field of high-white transparent material formulations, can solve the problems of color sensitivity, large deformation, and many pinholes and holes, and achieve high expansion coefficient, stable performance, increased mechanical strength and wear resistance. Effect

Inactive Publication Date: 2007-03-14
关润启
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, the proportion of transparent material in polycrystalline micropowder is about 25-50%. If the proportion of transparent material is further increased, if it reaches more than 95%, large deformation (especially late deformation), many pinholes and melting holes will occur, and the transparent material will be white. Defects such as low temperature (only about 45 degrees), sensitive hair color, large color difference, low yield, etc.
These problems limit the application of transparent materials in micropowder polished tiles, especially the application of high whiteness transparent materials in polished tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-white transparent material formulation and manufacture method of crystal full transparency polishing brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1. Ice crystal jade transparent material formula:

[0026] (1) Formula composition: white stone powder 10, Chaozhou sand 22, Guangxi sand 18, Hunan stone powder 18.5, white jade powder 10, kaolin 12, Heini 4, M flux 6.5.

[0027] (2) Chemical composition of raw materials

[0028]

[0029] 2. Mixing process ratio

[0030] Translucent material: transparent material 100% + L-1300 0.16%

[0031] Transparent material: transparent material 20% + super white material 80%

[0032] 3. Molding process

[0033] Hopper number

A

B

C

D

Powder name

Transparent material

High white transparent material

Translucent material

High white transparent material

Broken fineness (200

Item)%

10

15

15

15

Fabric ratio%

15

35

15

35

[0034] Fabric method: secondary fabric, molding times 3.5-4.0 times / min

[0035] Molding pressure 350-380bar

[0036] 4. Dr...

Embodiment approach 2

[0042] 1. Ice crystal jade transparent material formula: same as Example 1

[0043] 2. Color mixing process ratio transparent green material: transparent material 100% + L-1000 0.15% apple green

[0044] 0.13% transparent white material: transparent 20% + super white 80%

[0045] 3. Molding process

[0046] Hopper number

A

B

C

D

Powder name

Transparent material

High white transparent material

Transparent green material

High white transparent material

Broken fineness (200

Item)%

10

15

15

15

Fabric ratio%

15

35

15

35

[0047] Other molding parameters are the same as the first embodiment

[0048] 4. Drying and sintering process: the same as in Example 1; 5. Firing parameters: the same as in Example 1;

Embodiment approach 3

[0050] 1. Ice crystal jade transparent material formula: same as embodiment 1

[0051] 2. Proportioning of color mixing process Yellow transparent material: transparent material + L1000 0.35%, praseodymium 0.12%;

[0052] Transparent material: transparent material 20% + super white material 80%

[0053] 3. Molding process

[0054] Hopper number

A

B

C

D

Powder name

Transparent material

High white transparent material

Yellow through

High white transparent material

Broken fineness (200

Item)%

10

15

15

15

Fabric ratio%

15

35

15

35

[0055] Other molding parameters are the same as the first embodiment

[0056] 4. Drying and sintering process: the same as in Example 1; 5. sintering parameters: the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to one kind of decorating transparent vitrified ceramic tile and its material recipe and production process. The material for the decorating transparent vitrified ceramic tile consists of white stone powder 10-25 wt%, Chaozhou sand 15-30 wt%, Guangxi sand 15-30 wt%, white jade powder 5-25 wt%, Hunan stone powder 15-30 wt%, kaolin 10-20 wt%, black mud 1-10 wt% and M-type flux 0-10 wt%. The production process includes the steps of compounding material, ball milling, color mixing, spray drying, forming, drying, sintering and polishing. The produced ceramic tile is transparent, high white and high bright, and has no radioactivity, relatively high heat expanding coefficient and other advantages.

Description

Technical field: [0001] The present invention relates to a high-white transparent material formula of ice crystal jade full-permeable decorative craft porcelain vitrified brick and a production method of the brick. Background technique: [0002] With the continuous improvement of the technical level of polished tiles, the application range of transparent materials in polished tiles is also expanding. The production technology of ordinary polycrystalline micropowder, that is, micropowder containing transparent material, has been relatively mature, and manufacturers of various sizes have successively launched some products. Generally, the proportion of transparent material in polycrystalline powder is about 25-50%. If the proportion of transparent material is further increased, if it reaches more than 95%, large deformation (especially post-deformation), many pinholes and melting holes will occur, and the transparent material will be white. Defects such as low intensity (only about...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00C04B41/86
Inventor 关伟华
Owner 关润启
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap