Thermal roll-oil composition of dispersing oily clay wear-resistant anti-skid agent

A technology of composition and hot-rolling oil, which is applied in the direction of lubricating composition, additives, petroleum industry, etc., and can solve problems such as toxicity

Active Publication Date: 2007-04-04
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] There are also some patents that use full oil-soluble formulations, such as JP8041486 (1996), which introduces the addition of 0.05-20wt% lipophilic carboxylic acid, sulfonic acid and anhydride, partial ester, amide and salt hot-rolled oil to inhibit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal roll-oil composition of dispersing oily clay wear-resistant anti-skid agent
  • Thermal roll-oil composition of dispersing oily clay wear-resistant anti-skid agent
  • Thermal roll-oil composition of dispersing oily clay wear-resistant anti-skid agent

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0064] Add 4.00 grams of American quaternary ammonium salt modified bentonite, 4.00 grams of oleic acid and maleic anhydride adduct, and 200 grams of toluene into a three-necked flask, reflux for 36 hours, evaporate the toluene under reduced pressure, and dissolve the product with 150SN base oil, number a.

example 2

[0066] Modified bentonite with 4.00 grams of domestic quaternary ammonium salt, 11.12 grams of oleic acid, and 250 grams of toluene, refluxed for 12 hours, evaporated the toluene under reduced pressure, and dissolved the product in 150SN base oil, number B.

example 3

[0068] Modified bentonite with 4.00 grams of quaternary ammonium salts produced in the United States, 4.00 grams of sebacic acid, and 250 grams of toluene, refluxed for 12 hours, evaporated the toluene under reduced pressure, and dissolved the product in 150SN base oil, coded C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A hot-pressed oil composition containing oily-dispersing clay antifriction anti-slip agent has excellent dispersing ability, abrasion resistance and lubricity. The composition consists of 0.1-15wt% sulfur-contained extreme pressure agent from alkyl polysulfide, mineral oil sulfide and thiopoly alcohol ester, 0.1-20wt% phosphor-contained anti-scuff agent from organic phosphate, phosphonate ester, phosphate ester, acid amine salt organic phosphate, amine salt phosphate ester, phosphoamidster, dialkyl phosphateodithioate, dimercaptothioliazole phosphorodithioate and acid phosphate imidazoline salt and 0.01-1wt% oil-soluble clay anti-scuff lubricant of organic modified clay and C4-C24 hydroxy-acid compound or C13-C64 hydroxy-acid contained condensate. It has excellent dispersibility, abrasion resistance and lubricity.

Description

technical field [0001] The invention relates to a hot rolling oil composition. Background technique [0002] The use of hot-rolling oil is a new technology in the field of modern steel rolling. Early hot-rolling did not use oil but was lubricated with water. Later, hot-rolling oil was directly used to lubricate the rolls. Its ingredients include mineral oil, animal and vegetable oils, and synthetic fatty acids. Lubricating oil, causing great pollution. The lubricity of hot rolling has been greatly developed in the past ten years. At present, many large-scale hot rolling mills use the lubrication technology of water and oil co-spraying instead of pure oil lubrication. During the rolling process, a very small amount of hot rolling oil and A large amount of water (more than 99.5%) is mixed, forced to emulsify, sprayed onto the surface of the work roll, and the emulsion is brought into the deformation zone through the rotation of the roll, which not only effectively cools the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M105/36C10M137/10C10N40/20
Inventor 韦淡平范静芸兰晓艳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap