Protective wound dressing device for oral and pharyngeal space

a protective wound and pharyngeal technology, applied in the field of medical and surgical wound dressings, can solve the problems of patients experiencing dehydration, pain and postoperative bleeding still significant, and pain and postoperative bleeding

Inactive Publication Date: 2013-06-20
ETHICON INC
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The materials and methods of this patent provide a safe and effective way to protect post-surgical wounds in the mouth. The dressing is made of a water-soluble material that can be easily removed without causing any danger to the patient. This helps to reduce pain, bleeding, and recovery time. Overall, this technology offers a better way to care for post-surgical wounds.

Problems solved by technology

Although tonsillectomies and adenoidectomies are considered to be safe procedures, they still have significant morbidities of pain and postoperative bleeding.
Post-operative pain causes great discomfort upon swallowing.
In an attempt to avoid this pain, patients may experience dehydration and poor oral intake due to their lack of drinking and eating.
This lack of knowledge regarding the natural history of the tonsillectomy scab presents a challenge to the design of a protective wound dressing.
Foreign body ingestion and aspiration are primarily pediatric problems.
However, even with use of this surgical method, post-operative pain and bleeding are still significant morbidities.
However, the cost of this treatment is not commensurate with the reimbursement level for these surgical procedures.
These appear to suffer from a limited ability to adhere to the operative site (adherence), ability to hold together (cohesiveness), and / or ability to remain in place for a clinically relevant period (durability).
Fibrin sealants lack the durability to protect the wound through the time of healing.
Hissong et al discloses preferred polymeric film-forming medical sealants, but does not disclose how the polymeric film-forming medical sealant would slough from the tonsillectomy fossa.
The suture strip may slough more like a balloon and cause a greater choking hazard due to its conforming nature.
These pores and channels create random defects in the bulk material.
When fragments are created their size is unpredictable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Protective wound dressing device for oral and pharyngeal space
  • Protective wound dressing device for oral and pharyngeal space

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0064]Preparation of a Water-Soluble Molding Matrix with an Open Cell Configuration

[0065]28.35 grams of unflavored Knox® gelatin (Kraft Foods, Inc.) was added to a beaker containing 236.6 mL purified cold water. Approximately ten drops of green food coloring were added to the mixture to tint the resulting water-soluble molding matrix. The beaker was placed on a stir plate and heated to approximately 60° C. and the contents were stirred at a medium speed of agitation for approximately thirty minutes until all gelatin was in solution. While still at the elevated temperature, the solution was poured in a flexible silicone mold with dimensions of 100 mm by 100 mm with a cell of 10 mm by 10 mm and a cell depth of approximately 10 mm. The solution was poured into the flexible mold such that the solution filled the cell only and did not cover the entire mold surface. The silicone mold containing the solution was placed into a refrigerator for 24 hours. The resulting water-soluble molding m...

example 2

[0066]Preparation of a Water-soluble Molding Matrix with a Film-Spanned Configuration

[0067]6 grams of polyvinyl alcohol powder (molecular weight approximately 20,000 Daltons, MP Biomedicals, LLC) was added to a beaker containing 60 mL of a 50 / 50 by volume mixture of isopropyl alcohol and purified water. Approximately five to six drops of red food coloring were added to the mixture to tint the resulting water-soluble molding matrix. The beaker was placed on a stir plate and heated to approximately 80° C. and the contents were stirred at a medium speed of agitation for approximately thirty minutes until all powder was in solution. While still at the elevated temperature, the solution was poured in a flexible silicone mold with dimensions of 150 mm by 150 mm with a cell of 5 mm by 5 mm and a cell depth of approximately 3 mm. The solution was poured into the flexible mold such that the solution filled the cell as well as a thin film layer over the entire cell area. The silicone mold con...

example 3

[0068]Durability Evaluation of Wound Dressing Utilizing Example 1 Water-soluble Molding Matrix

[0069]A bench method was developed to evaluate samples produced according to the present invention. The test fixture was kept at approximately 37° C. to approximate body temperature. Samples were kept moist using saline to simulate saliva or other bodily fluids. Samples were subjected to an abrasive force generated by a roller to simulate swallowing. The average adult swallows 1000 times a day (Gleeson, D C. Oropharyngeal swallowing and aging: A review. J. Commun. Disord. 1999: 32;373-396). As a result, 500 cycles of the test apparatus (one back and forth motion) represents approximately one day. Since this abrasive force was much more aggressive than swallowing, these test results were considered a “worst case scenario”.

[0070]A foam pad (McMaster-Carr) was placed onto the bed of an Elcometer 1720 Abrasion Tester to support the test sample. A piece of collagen (250 mm by 150 mm by ˜5 mils, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The present invention provides a wound dressing comprising a tessellated water-soluble molding matrix comprised of a polymer selected from the group consisting of polyvinyl alcohol, gelatin, and mixtures thereof and a 1,1-disubstituted ethylene monomer. The present invention further provides methods of using the wound dressing and kits containing the wound dressing.

Description

BACKGROUND OF THE INVENTION[0001]The present invention relates to medical and surgical wound dressings and methods for making and using such dressings. In particular, the present invention relates to medical and surgical wound dressings where the wound dressing incorporates a water-soluble molding matrix to cause the resulting wound dressing to slough as particles of predictable maximum size and geometry. The medical and surgical wound dressings of the present invention provide a treatment to seal post-surgical sites of the oral and pharyngeal space that do not pose a choking hazard.[0002]Approximately one million tonsillectomies, adenoidectomies, and tonsillectomy / adenoidectomy procedures combined were coded as surgical procedures in the United States in 2007. Although tonsillectomies and adenoidectomies are considered to be safe procedures, they still have significant morbidities of pain and postoperative bleeding. Post-operative pain causes great discomfort upon swallowing. In an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): A61L26/00
CPCA61F13/122A61L26/0052A61L15/32A61L15/58A61L15/62A61L15/64A61L24/06A61L26/0014A61L26/0038A61L2430/36A61L15/24C08L29/04C08L35/04A61P17/02
Inventor KEPLINGER, SCOTT ALAN
Owner ETHICON INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com