Optical radiation resistant exterior wall paint

An exterior wall coating and anti-sunlight technology, applied in the field of exterior wall coatings that resist solar radiation, can solve problems such as large-area cracks, wall peeling, unable to meet the requirements of water resistance and moisture resistance, and achieve strong corrosion resistance, Strong anti-aging performance and good water resistance

Inactive Publication Date: 2007-11-28
邹文和
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, water-based acrylic paints are often used as exterior wall paints for grain storage warehouses, but this paint cannot meet the special requirements for storing grain, such as acrylic paints cannot be heat-insulated and cannot meet the heat-insulation requirements; large-area tortoises often appear cracks, the wall is gradually soaked in water, resulting in a large area of ​​peeling off the wall, which cannot meet the requirements of water resistance and moisture resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] formula:

[0030] Toluene 40kg 120 # Gasoline 15kg Alkyd resin 8kg

[0031] VAE 4.5kg DBP2kg Neoprene 10kg

[0032] Appropriate amount of pigment;

[0033] Preparation steps: according to the formula requirements, toluene, 120 # Gasoline is metered into the reaction kettle with a high-speed shear emulsifier and mixed fully, then alkyd resin, VAE, DBP, and neoprene are metered in, and the high-speed shear emulsifier is used for shear emulsification at a speed of 1500 rpm , After cutting for 1 hour and 10 minutes, add the pigment, and continue to emulsify and grind. When the fineness of the material reaches below 60 μm, it can be filtered and filled into a finished product.

Embodiment 2

[0035] formula:

[0036] Toluene 50kg 120 # Gasoline 20kg Alkyd resin 10kg

[0037] VAE 8kg DBP5kg Neoprene 20kg

[0038] Appropriate amount of pigment;

[0039] The preparation steps are basically the same as those in Example 1. The rotational speed of the high-speed shear emulsifier is 2000 rpm, and the pigment is added after shearing for 1.5 hours.

Embodiment 3

[0041] formula:

[0042] Toluene 70kg 120 # Gasoline 35kg Alkyd resin 13kg

[0043] VAE 9kg DBP6.5kg Neoprene 35kg

[0044] Appropriate amount of pigment;

[0045] The preparation steps are the same as those in Example 1. The rotational speed of the high-speed shear emulsifier is 2500 rpm, and the pigment is added after shearing for 1 hour and 45 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a radiation reactant exterior wall paint in the field of exterior wall paint producing technology. It is formed by toluene, 120# petrol, alkyd resin, VAE, DBP, chloroprene rubber and painting; it has the following preparing steps: adding the toluene and the 120# petrol into the autoclave sterilizer to mix them, adding the alkyd resin, VAE, DBP and chloroprene rubber and using high speed cutting emulsion machine to do cutting emulsion, adding the painting after 1-2h and emulsion erasing until the material purity achieves to below 60mu m, then filter charging the product.

Description

technical field [0001] The present invention relates to an exterior wall paint, in particular to a solar radiation resistant exterior wall paint which hardly absorbs sunlight. Background technique [0002] Grain storage is a major event related to the national economy and the people's livelihood. The warehouse must meet the storage requirements and must be heat-insulated, water-resistant, and moisture-proof. In the prior art, water-based acrylic paints are often used as exterior wall paints for grain storage warehouses, but this paint cannot meet the special requirements for storing grain, such as acrylic paints cannot be heat-insulated and cannot meet the heat-insulation requirements; large-area tortoises often appear Cracks cause the wall to gradually soak in water, causing large areas of the wall to peel off, which cannot meet the requirements of water resistance and moisture resistance. Contents of the invention [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D111/00C09D5/33
Inventor 邹文和刘建国张委国
Owner 邹文和
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com