No-baking light foamed heat insulating and sound isolating material and its production process

A technology for thermal insulation, sound insulation and light weight, which can be applied in solid waste management, other household appliances, sustainable waste treatment, etc. good quality effect

Inactive Publication Date: 2008-04-30
郑东风
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the lightweight foam insulation and sound insulation materials produced by normal temperature curing are magnesium cement foam materials containing magnesium oxide and magnesium chloride as base materials. The components are basically filled with ordinary fly ash. The ash content is low, the cost is high, it is not water-resistant, easy to deform, it is an air-hard material, and it is unstable. With the increase of the service life, the strength gradually decreases. It is not suitable for use in humid areas and open air, nor is it suitable for outdoor use wall material
Therefore, the building materials market is subject to certain restrictions by national policies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Put the high activity fly ash into the ball mill to grind, the fineness is 5500cm specific surface area 2 / g.

[0042] Formula: 30 kg of finely ground high-activity fly ash, 6 kg of sulfur-aluminum cement, 0.6 kg of raw gypsum powder, and 24 kg of water.

[0043] Put the above ingredients into the blender in order and stir for 2 minutes, stir evenly to make a slurry for later use.

[0044] Physical foaming: Put 0.3 kg of rosin resin liquid foaming agent and 3 kg of water into the mixer and stir it mechanically for foaming before use.

[0045] Put the slurry and the foam in a mixer at a volume ratio of 1:1 and stir evenly, then pour it into a 1000×1000×90mm mold, demould it after 8 hours, put it in a normal temperature curing room for 25 days, and then mold it into a finished product.

Embodiment 2

[0047] Put the high activity fly ash into the ball mill to grind, the fineness is 5500cm specific surface area 2 / g.

[0048] Formula: 25 kg of finely ground high-activity fly ash, 2.5 kg of sulfur-aluminum cement, 0.5 kg of raw gypsum powder, and 14 kg of water.

[0049] Put the above ingredients into the blender in order and stir for 2 minutes, stir evenly to make a slurry for later use.

[0050] Physical foaming: Put 0.3 kg of animal protein foaming agent and 4 kg of water into the mixer and stir it mechanically for foaming before use.

[0051] Put the slurry and the foam in the mixer at a volume ratio of 1:1.5 and stir them evenly, then pour them into a 1000×1000×60mm mold, demould them after 8 hours, put them in a normal temperature curing room for 30 days, and then mold them into finished products.

Embodiment 3

[0053] Put the highly active fly ash into the ball mill to grind, the fineness is 6500cm specific surface area 2 / g.

[0054]Formula: 25 kg of finely ground high-activity fly ash, 22.5 kg of high-alumina cement, 2.5 kg of raw gypsum powder, and 50 kg of water.

[0055] Put the above ingredients in a blender in order and stir for 4 minutes, stir evenly to make a slurry for later use.

[0056] Physical foaming: Put 0.6 kg of sodium dodecylbenzene sulfonate solution and 4.8 kg of water into the mixer and stir it mechanically for foaming before use.

[0057] Put the slurry and the foam in the mixer at a volume ratio of 4:1 and stir, pour it into a 1000×1000×60mm mold after stirring evenly, demould it after 8 hours, put it into a curing room at 40°C-60°C, 20 The finished product is formed after the day.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention is one kind of no-baking light foamed heat insulating and sound isolating material and its production process. The no-baking light foamed heat insulating and sound isolating material has high activity fly ash, which is produced based on one other patent of the present inventor, as basic material and some other components. It has high water resistance, high strength, high fireproof performance and high stability.

Description

technical field [0001] The invention relates to the field of foaming heat-insulating and sound-insulating building materials, in particular to a non-burning light-weight foaming heat-insulating and sound-insulating material and its production method. Background technique [0002] At present, most of the lightweight foam insulation and sound insulation materials produced by normal temperature curing are magnesium cement foam materials containing magnesium oxide and magnesium chloride as base materials. The components are basically filled with ordinary fly ash. The ash content is low, the cost is high, it is not water-resistant, easy to deform, it is an air-hard material, and it is unstable. With the increase of the service life, the strength gradually decreases. It is not suitable for use in humid areas and open air, nor is it suitable for outdoor use wall material. Therefore, the building materials market is subject to certain restrictions by national policies. Therefore,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B18/08C04B22/14C04B38/02
CPCC04B38/0605Y02W30/91C04B7/02C04B7/32C04B18/08C04B22/143C04B38/10
Inventor 郑东风郑春雷
Owner 郑东风
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap