Decoration glaze for inner wall tile and its preparation method

Abstract

The present invention discloses one kind of decoration glaze for inner wall tile and its preparation process and test method on water permeating effect. The decoration glaze consists of mineral materials, including clay, zirconium silicate, ceramic stone powder, etc in 20-60 weight portions, and titanium containing clinker in 40-80 weight portions. Its material components include Li2O / Na2O / K2O 0.5-10 weigh portions, CaO 3-15 weigh portions, MgO 0.5-3.5 weigh portions, SiO2 55-80 weigh portions, Al2O3 5-25 weigh portions, B2O3 0.5-10 weigh portions, ZrO2 2.0-15 weigh portions, P2O5 0-10 weigh portions, TiO2 2-15 weigh portions, and BaO 2-15 weigh portions. Its preparation process includes the first preparing titanium containing clinker, mixing the titanium containing clinker with mineral materials and ball milling to 100-200 mesh. The decoration glaze for inner wall tile can result in beautiful artistic effect.

Description

technical field [0001] The present invention relates to the raw material of ceramic products and its preparation method and ceramic tile glaze detection method, more specifically relates to a kind of cosmetic glaze for interior wall brick body and its preparation method, and a kind of ceramic interior wall tile product glaze surface resistance Test method for water penetration (seepage) effect. Background technique [0002] At present, before the general ceramic interior wall tiles are laid, they need to be soaked in water for a certain period of time before being laid on the wall. In this way, uneven water immersion marks will be produced on the glazed surface of the brick body after laying, which makes the laying There are usually two reasons for uneven water immersion marks on the glazed surface of ceramic interior wall tiles after laying ceramic tiles. One is that water directly penetrates the cosmetic glaze layer to reach the surface. Under the glaze, water marks appea...

AI Technical Summary

Problems solved by technology

[0002] At present, before the general ceramic interior wall tiles are laid, they need to be soaked in water for a certain period of time before being laid on the wall. In this way, uneven water immersion marks will be produced on the glazed surface of the brick body after laying, which makes the laying There are usually two reasons for uneven water immersion marks on the glazed surface of ceramic interior wall tiles after laying and pasting. One is that water directly penetrates the cosmetic glaze layer to reach the surface. Under the glaze, water marks appear on the glazed surface of the brick body; the second is that although the water does not penetrate the cosmetic glaze layer to reach the under glaze, the traces of water pass through the cosmetic glaze layer and the surface glaze layer, resulting in water immersion marks on the glazed surface of the brick body

For the solution to this problem, no relevant patents have been retrieved

In addition, regarding whether the glazed surface of tiles has the effect of water penetration (seepage), there is no unified testing method and evaluation standard for tile manufacturers at present.