A converter steelmaking and production method technology, applied in the manufacture of converters, etc., can solve problems such as blockage of hoppers, prolonging the smelting cycle, and splashing, and achieve the effects of prolonging service life, shortening smelting time, and reducing production costs
Inactive Publication Date: 2007-10-03
郎雪 +1
View PDF0 Cites 23 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The slagging agent used in existing converter steelmaking, its silicon dioxide SiO 2 If the content is too high, it will increase the total slag in the converter, and if the manganese Mn content is too low, it will affect the amount of Mn at the end point of molten steel. Moreover, due to the addition of calcium fluoride (CaF), fluoride ions will not only seriously erode the furnace lining, but also reduce the service life of the converter lining. Seriously, fluorine ions pollute the environment and endanger human health. In addition, the physical properties of the existing slag-removing agents do not meet the requirements for use. Converter steelmaking brings potential safety hazards. During the steelmaking process, splashing and gun sticking are prone to occur. After the slagging agent is put into the furnace, the temperature of molten iron is lowered, which prolongs the smelting cycle.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0023] This slag-removing agent is used in the No. 4 converter of a steel plant: a combined blowing converter with a nominal capacity of 30 tons. Its components and contents are iron oxide FeO: 43.70%; calcium oxide CaO: 12.40%; manganese oxide MnO: 12.02% ; Magnesium oxide MgO: 2.08%; Aluminum oxide Al 2 o 3 : 2.54%, and the units used for the remaining components have not been tested. The total test volume is 8 tons. The specific test data are shown in Table 1 and Table 2.
[0024]
[0025] furnace number
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The present invention is one kind of no-fluorine composite slag melting agent for converter steelmaking and its production process. The no-fluorine composite slag melting agent as one kind of steelmaking supplementary material consists of FeO 40-50 wt%, CaO 10-20 wt%, MnO 12-45 wt%, H2O 0.5-1 wt%, MgO 1-8 wt%, Al2O3 and SiO2 1-10 wt%, and impurity for the rest. Its production process includes the steps of compounding, grinding, adding adhesive, stirring, pelletizing, curing and roasting. It is used in no-fluorine steelmaking with less invasion to converter lining, long converter service life, less environmental pollution, low production cost and other advantages.
Description
technical field [0001] The invention belongs to auxiliary materials for steelmaking, in particular to a converter steelmaking slag agent. Background technique [0002] The slagging agent used in existing converter steelmaking, its silicon dioxide SiO 2 If the content is too high, it will increase the total slag in the converter, and if the manganese Mn content is too low, it will affect the amount of Mn at the end point of molten steel. Moreover, due to the addition of calcium fluoride (CaF), fluoride ions will not only seriously erode the furnace lining, but also reduce the service life of the converter lining. Seriously, fluorine ions pollute the environment and endanger human health. In addition, the physical properties of the existing slag-removing agents do not meet the requirements for use. Converter steelmaking brings potential safety hazards. During the steelmaking process, splashing and gun sticking are prone to occur. After the slag remover is put into the furnace...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/00C21C5/28
Inventor 朗雪樊龙生
Owner 郎雪
PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.