A technology of ultra-low carbon steel and manufacturing method, which is applied in the field of metallurgy, can solve problems such as carbon increase and nitrogen increase, and achieve the effects of low carbon increase rate, high desulfurization rate, and strong desulfurization ability

Inactive Publication Date: 2008-01-02
ANGANG STEEL CO LTD
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the various problems of the above-mentioned desulfurizers, disclose a deep desulfurizer for ultra-low carbon steel refining and a manufacturing method for deep desulfurization of molten steel, and solve the problem of carburization, nitrogen increase and desulfurization during the desulfurization process. The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Several specific embodiments of the present invention are introduced below.

[0023] Composition: % by weight

[0024] composition

[0025] Choose any composition in the table, prepare according to the following method: its process steps are

[0026] 1 Mixing: Mix the materials in the proportion of ingredients. Among them, CaO: particle size ≤ 1mm, activity ≥ 300ml; CaF 2 , B 2 o 3 , BaO particle size ≤ 1mm, purity ≥ 98%; Al powder purity ≥ 99.5%, particle size composition: -180~+200 mesh content ≥ 70%, -200 mesh content ≤ 30%.

[0027] 2 Pulverization: Put the mixed material into the crusher for pulverization to avoid agglomeration of the material during the mixing process, so that the particle size of the material is ≤1mm.

[0028] 3 Passivation: In order to suppress the reduction of CaO activity in the deep desulfurizer and suppress the surface oxidation of Al powder and the violent reaction in the application process, passivation treatment is carried ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
purityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ultralow carbon steel refining deep-desulfurizer and making method, which comprises the following parts: 60%-69% CaO, 11%-20% Al, 5%-10% MgO, 5%-10% SiO2, 1%-5% Al2O3, 0.5%-1.2% Fe2O3, 1%-3% CaF2, 1%-3% B2O3, 1%-3% BaO and impurity. The making technique comprises the following steps: blending; grinding the material with grain size not more than 1mm; inactivating the material; drying; draining the trace element of water; packing.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular relates to refining technology outside a steelmaking furnace, in particular to a deep desulfurizer for ultra-low carbon steel refining and a manufacturing method thereof. Background technique [0002] In recent years, users have higher and higher requirements for the purity of steel, and the demand for ultra-low sulfur steel has continued to increase, especially ultra-low carbon, ultra-low sulfur high-grade electrical steel, ultra-low sulfur hydrogen-induced crack resistance high-grade pipelines The smelting technology of new steel types such as steel and high-strength steel needs to be developed urgently. The deep desulfurization technology of molten steel plays an increasingly important role in the entire steelmaking process. The research and development of deep desulfurization agents applied to ultra-low carbon steel is particularly important. [0003] A lot of in-depth and me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/064
Inventor 廖相巍温铁光李德刚王文仲潘秀兰姜振生黄玉平王雷
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap