Chromatic bituminous cement improving workability

A technology for colored asphalt and cementitious materials, applied in the field of asphalt cementitious materials, can solve the problems of polluting the environment, unfavorable popularization and use, large energy consumption, etc.

Inactive Publication Date: 2008-06-25
SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A notable defect disclosed in the above-mentioned patent is that it needs to be heated to an extremely high temperature during specific construction, which not only requires a large amount of energy consumption, but also pollutes the environment, makes construction difficult, and it is impossible to add too much proportion to the composition. Polymers that limit the high temperature stability of colored asphalt binders are not conducive to popularization and use. Therefore, it is very desirable to develop and research a new colored asphalt binder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromatic bituminous cement improving workability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0018] Raw materials used:

[0019] Refined lubricating oil, viscosity at 40°C: 3.5Pa.S, flash point: 335°C, aromatic content: 68wt%, density at 15°C: 0.98g / cm3

[0020] Petroleum resin, produced by Korea Kolon Company, trade name: Hikotack P140, softening point 145°C, average molecular weight (GPC method) 2200

[0021] Polyethylene wax with a molecular weight of 3000-6000 and a softening point of 120-150°C

[0022] SEBS, SIS and SBR

[0023] Heat the extracted lubricating oil to 175°C, then add petroleum resin, polyethylene wax, SEBS, SIS and SBR, and stir with a stirrer at a speed of 200 rpm for 60 minutes to prepare the finished colored asphalt binder . The specific composition ratio (percentage by weight), and the performance results of the binder and the mixture tested by the testing method specified in the JTJ052-2000 standard "Testing Procedures for Asphalt and Asphalt Mixtures in Highway Engineering" of the Ministry of Communications of China are shown in Table 1. ...

Embodiment 4

[0030] Example 4

[0031] The colored asphalt cement and aggregates are mixed into Marshall specimens and rutting specimens to form, in which the stones above 2.36mm are made of diabase, and the 2.36mm-0.075mm is made of quartzite gradation, and the following gradation is adopted:

[0032]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a colorful asphalt binder. The component of the colorful asphalt binder of the invention calculated by weight percentage comprises 20-65 per cent of petroleum resin, 30-79 per cent of lubricant refined extract oil and 1-5 per cent of polyethylene wax. By pulling a little of polyethylene wax into conventional colorful asphalt binder, temperature of mixing, spreading and rolling of asphalt mixture can be greatly reduced and negative influence on final colorful asphalt pavement is not caused, which allows an easy construction. As the same time, the reduction of construction temperature and odor emitted by the binder are decreased, which are in favor of environment protection. As the same time, addition of SEBS, SIS and SBR allows the colorful asphalt binder to be provided with better high-temperature stability.

Description

technical field [0001] The invention relates to an asphalt binder, in particular to a binder for colored asphalt. Background technique [0002] The mechanical properties and rheological properties of colored asphalt binder are the same as those of general road heavy traffic asphalt. The main principle of colored asphalt binder pavement is to use colored asphalt binder and add various pigments to make it have various required colors. At the same time, by using colored stones or light-colored stones, it can have a longer-lasting color effect. A good colored asphalt binder should meet the following three requirements: [0003] Colored asphalt binder has good performance and should try to meet the requirements of heavy traffic asphalt or even modified asphalt; it has good anti-rutting performance and good water damage resistance. [0004] At present, there have been many patents and documents disclosing their own colored asphalt binders, some of which have been industrialized, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L57/02C08L23/06
Inventor 黄子章
Owner SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap