Voltage dependent resistor dielectric material of zinc oxide and method of manufacturing electrical resistor
A technology of varistors and dielectric materials, applied in the direction of varistor cores, varistors, coating resistance materials, etc., can solve the problems of low voltage, leakage current, high nonlinear coefficient and stability. Considering each other, it is difficult to meet the requirements of low voltage, high nonlinear coefficient, low pressure sensitive voltage performance and other issues, so as to achieve the effect of low cost, stable pressure sensitive characteristics and low pressure sensitive voltage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment Construction
[0034] The present invention will be further described below in conjunction with the examples.
[0035] Table 1: Formulation Table of Embodiment 1
[0036] components
ZnO
Bi 2 o 3
TiO 2
Sb 2 o 3
MnCO 3
co 2 o 3
Cr 2 o 3
ZrO 2
Ni 2 o 3
SiO 2
content(%)
85
5
1.8
1.5
1.5
1.8
0.5
0.4
0.5
2.0
[0037] According to the formula in Table 1, such as figure 2 The manufacturing process shown in the flow chart prepares a chip zinc oxide varistor. The varistor voltage of the chip varistor is measured to be 5.6V (thickness of the film green body is 20 microns), the nonlinear coefficient is 52, and the leakage current is less than 1.0 microampere (measured at 80% varistor voltage).
[0038] It should be noted that: 1. The drying temperature in steps 2, 3, 6 and 8 is 120-130°C; 2. The pre-shrinkage sintering process conditions in step 2 are: heating rate 6-10°C / min, sint...
PUM
Property | Measurement | Unit |
---|---|---|
current | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com