Case-making method of silicasol investment casting with elongated hole structure

A silica sol, slender hole technology, applied in the direction of casting molds, casting mold components, manufacturing tools, etc., can solve the problems of only suitable for large-scale products, high cost, long cycle, etc., to achieve flexible application, low cost, and short cycle. Effect

Active Publication Date: 2009-07-15
SHANGHAI ZHONGZHOU SPECIAL ALLOY MATERIALS
View PDF0 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] 1. It is necessary to make molds separately to produce ceramic cores. The cycle is long, the cost is high, and special equipment is required. It is produced by professional manufacturers and is only suitable for large-scale products;
[0017] 2. Most precision casting companies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Case-making method of silicasol investment casting with elongated hole structure
  • Case-making method of silicasol investment casting with elongated hole structure
  • Case-making method of silicasol investment casting with elongated hole structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] Below in conjunction with accompanying drawing and specific embodiment the present invention is described in further detail:

[0038] In order to solve the problems of the technologies described above, the present invention is achieved through the following steps (as Figure 4 shown):

[0039] 1. Make a wax model: use a general-purpose wax injection mold;

[0040] 2. Coating: dip the wax mold with silica sol zircon powder coating;

[0041] 3. Sanding: Sprinkle 100-120 mesh zircon sand on the whole wax model;

[0042] 4. Drying: the module is dried for 2-4 hours;

[0043] The number of times used between steps "2" to "4" is 2-3 times;

[0044] 5. Grouting in the hole;

[0045] 6. Continue to make the shell: after the grouting is completed and the slurry is hardened, make another 2-3 layers of shells;

[0046] 7. Dewaxing: After the shell making is completed, dewax to obtain the mold shell;

[0047] 8. Roasting and pouring;

[0048] where in step "5":

[0049] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a case making method of a silica sol investment casting with a slender hole structure, and the method is achieved through adopting the following steps of max mould preparation 1, doping 2, sanding 3, drying 4, in-hole grouting 5, continuous case making 6, demaxing 7 as well as roasting and casting 8, wherein the steps between the doping 2 and the drying 4 are adopted for 2-3 times; wherein in the step 5, the in-hole grouting is achieved through the following steps: soft white slime is used for plugging up the lower end and a lateral hole of a part, and a stainless steel wire used for ensuring that a mandril is not fractured at the end part is inserted into the end part of the hole, and the diameter of the stainless steel wire is about 2mm; and sizing agent is injected after the process of plugging up the hole and inserting the wire are ready, and the case making is continued after the sizing agent is solidified. The invention has the advantages that a mold core die is independently manufactured, the period is short, and the cost is low; in addition, the method is not limited by the sorts of the dies and is especially suitable for small amount of products or a single product, and the application is flexible.

Description

technical field [0001] The invention relates to a shell-making method of a silica sol investment casting, in particular to a shell-making method of a silica sol investment casting with a slender pore structure. 1. Background technology: [0002] 1. Investment casting is also called lost wax casting. This method is to make the fusible material into a precise and smooth shape (fusible mold), coat the fusible mold with multiple layers of refractory materials, and the refractory materials will form a mold after hardening. The fusible mold in the mold is melted and flowed out, and then the molten metal is poured into the baked mold, and the molten metal becomes a precise and smooth casting after cooling and solidifying in the mold. Investment casting is the highest precision among the existing casting methods. Compared with the traditional sand casting method, its characteristics are as follows: [0003] ①. Use fusible molds to shape, no need to take molds out of the box; [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C9/04
Inventor 冯明明
Owner SHANGHAI ZHONGZHOU SPECIAL ALLOY MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap