Method for preparing acid fracturing, temperature-controlled and variable-viscosity polymer and polymer cross-linked body

A polymer and acid fracturing technology, which is applied in the field of acid fracturing in oil and gas wells, can solve problems such as low viscosity, acid fluid loss, and acid-rock reaction speed gap, so as to ensure effective reaction, reduce damage, and improve acid fracturing effect and economical effects

Inactive Publication Date: 2010-10-13
BEIJING FRAC TECH DEV
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Gelling acid systems commonly used in the prior art, such as gelling acid, emulsifying acid, and surfactant retarded acid, have relatively low viscosity (generally not greater than 100 mPa.s) in reducing acid fluid loss and acid rock reaction speed. big gap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing acid fracturing, temperature-controlled and variable-viscosity polymer and polymer cross-linked body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Embodiment 1: a kind of preparation method of the polymer that is used for acid fracturing temperature control becomes viscous, comprises the following steps:

[0049] 1) Put AMPS and AA into the deionized water in the reaction kettle in turn, stir until completely dissolved, slowly add carbonate under stirring, the amount of carbonate added is 13% to 16% of the total weight of AMPS and AA %, stirred until completely dissolved; the weight ratio of AMPS, AA and deionized water is:

[0050]AMPS 43~55

[0051] AA 1~5

[0052] Deionized water 254~280;

[0053] Carbonate in the present embodiment can be one or two compound use in potassium carbonate, potassium bicarbonate, sodium carbonate, sodium bicarbonate, ammonium carbonate, ammonium bicarbonate etc., as potassium carbonate and ammonium carbonate (potassium carbonate And the weight ratio of ammonium carbonate is 2: 1);

[0054] 2) Add acrylamide accounting for 26% to 30% of the total amount to the solution obtained ...

Embodiment 2

[0066] Embodiment 2: A kind of preparation method of the polymer cross-linked body that is used for acid fracturing temperature control becomes viscous, comprises the following steps:

[0067] 1) Put AMPS and AA into the deionized water of the reaction kettle in turn, stir until completely dissolved, slowly add potassium carbonate accounting for 13% of the total amount of materials (the total weight of AMPS and AA) under stirring, and stir until completely dissolved; AMPS , The weight ratio of AA to deionized water is:

[0068] AMPS 43

[0069] AA 1

[0070] Deionized water 280;

[0071] 2) Add acrylamide (AM) accounting for 26% (by weight) of the total amount to the solution obtained in step 1), and stir until it is completely dissolved;

[0072] 3) In the solution obtained in step 2), add methacryloyloxyethyltrimethylammonium chloride (DMC) accounting for 0.3% (weight ratio) of the total amount, stir evenly, and control the temperature of the obtained solution at 6℃~8℃, ...

Embodiment 3

[0093] Embodiment 3: A kind of preparation method of the polymer cross-linked body that is used for acid fracturing temperature control becomes viscous, comprises the following steps:

[0094] 1) Put AMPS and AA into the deionized water in the reactor in turn, stir until completely dissolved, slowly add potassium bicarbonate accounting for 13% of the total amount of materials (the total weight of AMPS and AA) under stirring, and stir until completely dissolved; The weight ratio of AMPS, AA and deionized water is:

[0095] AMPS 43

[0096] AA 1

[0097] Deionized water 280;

[0098] 2) Add acrylamide (AM) accounting for 26% (by weight) of the total amount to the solution obtained in step 1), and stir until it is completely dissolved;

[0099] 3) In the solution obtained in step 2), add methacryloyloxyethyltrimethylammonium chloride (DMC) accounting for 0.3% (weight ratio) of the total amount, stir evenly, and control the temperature of the obtained solution at 6℃~8℃, adjust...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing an acid fracturing, temperature-controlled and variable-viscosity polymer and a polymer cross-linked body. The polymer is coupled with a compound cross-linking agent to form the polymer cross-linked body; the polymer cross-linked body can be used for performing formation acid fracturing at the temperature of less than 120 DEG C; the viscosity of the polymer is about 20mPa.s at the temperature of 25 DEG C; the polymer is cross-linked at the temperature of between 60 and 90 DEG C for 5 to 10 minutes and can be hung, so that the viscosity of the polymer is up to 100mPa.s; and the viscosity of the polymer can be kept between 10 and 20mPa.s at the temperature of 120 DEG C. Since the polymer has a variable-viscosity characteristic, formation filtration is effectively reduced, active acid liquor can penetrate into the deep part of the formation, effective reaction of the acid liquor and reservoir rock is ensured and acid fracturing effect and economic benefit are improved.

Description

technical field [0001] The invention relates to the field of acid fracturing of oil and gas wells in oil and gas field development engineering, in particular to a polymer and a polymer cross-linked body used for acid fracturing to become viscous under temperature control. Background technique [0002] Carbonate oil and gas reservoirs occupy an important position in the distribution of oil and gas reservoirs in the world. According to preliminary statistics, carbonate rock reservoirs have been discovered and developed in 57 sedimentary basins in nearly 40 countries and regions in the world. Reserves account for 48% and 28% of the world's total oil and gas reserves, and oil and gas production account for about 60% and 30% of the world's total oil and gas reserves. [0003] Since the 1970s, my country has successively discovered and developed more than 30 carbonate buried hill oil and gas reservoirs in Shengli, North China, Liaohe, Tarim and other basins, occupying an important...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/58C08F220/56C08J3/24C09K8/62
Inventor 韩林陆现桥武志勇王善江申斌徐建富
Owner BEIJING FRAC TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com