Method for eliminating edge fault of aluminium killed steel with low manganese-sulfur ratio and low carbon

A low-carbon aluminum-killed steel, manganese-sulfur ratio technology, applied in the field of steel rolling, to achieve the effect of reducing production costs and smelting difficulty

Active Publication Date: 2012-02-29
首钢股份公司迁安钢铁公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a method for solving the edge defect of low Mn / S low carbon aluminum killed steel, for low Mn / S low carbon aluminum killed steel after passing the slab off the assembly line, heat preservation and in the hot rolling process for heating and Adjustment and Control of Rolling Process to Eliminate Strip Edge Defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for eliminating edge fault of aluminium killed steel with low manganese-sulfur ratio and low carbon
  • Method for eliminating edge fault of aluminium killed steel with low manganese-sulfur ratio and low carbon
  • Method for eliminating edge fault of aluminium killed steel with low manganese-sulfur ratio and low carbon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] Specific implementation examples

[0019] The rolling of low-carbon aluminum-killed steel SPHC (a low-carbon aluminum-killed steel named after a Japanese brand name) was carried out on the 2250mm hot continuous rolling production line of Shougang Qiangang by using the method and control means involved in the present invention. The size of the slab is 230×1250×9000mm, the rolling specification of No. 1~9 is 3.0×1275mm, and the rolling specification of No.10~12 is 3.0×1110mm.

[0020] Table 1 Key points of process control, ℃

[0021]

[0022]

[0023] 1. For No. 1-9 slabs, stack cooling after off-line, the calculated cooling rate is 8°C / min, and air-cooling after No. 10-12 slabs off-line;

[0024] 2. The temperature and residence time of the slabs in each section of the heating furnace are shown in Table 1, and the slabs of No. The slab is cold loaded and heated according to conventional methods;

[0025] 3. For rough descaling of slabs No. 1 to 9, single descali...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for eliminating an edge fault of aluminium killed steel with low manganese-sulfur ratio and low carbon, belonging to the technical field of steel rolling. The method comprises the following technological steps of: cooling an offline plate blank in an insulating pit, or slowly cooling by stacking; controlling the atmosphere in a heating furnace and the residence time in each stage, the temperature and the total residence time in the furnace of the plate blank; rolling in an equivalent width mode or widening mode; and adjusting a scale removing mode and a layercooling mode. The invention has the advantage of eliminating the influence of Mn / S on the quality of steel edges by optimizing heating and rolling technologies under the premise of not increasing extra equipment and investment. Compared with the prior art for eliminating the influence of Mn / S on the quality of band steel edges by increasing the content of Mn or reducing the content of S in the plate blank, the invention can greatly reduce production cost and smelting difficulty. The method is economical and effective, meets the requirements of low carbon and economy of green steel, and is especially applicable to the production of low-carbon aluminium killed steel with 10-30 Mn / S.

Description

technical field [0001] The invention belongs to the technical field of steel rolling, and in particular provides a method for solving edge defects of low-manganese-sulfur ratio (manganese-sulfur ratio is represented by Mn / S) low-carbon aluminum-killed steel, and relates to the production of low-Mn / S low-carbon by hot continuous rolling The solution to the edge defects of aluminum-killed steel is suitable for the method of producing lip cracks at the edge of strip steel in the rolling process of low-carbon aluminum-killed steel with Mn / S controlled between 10-30. Background technique [0002] Low-carbon aluminum-killed steel, as a very large amount of stamping steel, generally needs to be used after cold rolling, so it is expected that the hot-rolled plate of this steel type has a lower yield strength. Reducing the content of solid solution elements such as Mn has a significant effect on reducing the yield strength, but reducing the Mn content will cause the Mn / S of the slab ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/22B21B37/74B21B45/04
Inventor 李明魏建全武军宽王伦亢小敏刘风刚胡志远关建东刘兰霄焦会丽安冬洋
Owner 首钢股份公司迁安钢铁公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com