Hydroxy acrylic resin for ultra-fast dry automobile varnish and preparation method thereof

A hydroxyacrylic acid, ultra-fast drying technology, applied in coatings and other directions, can solve the problems of high price of varnishes, difficult to popularize and use in a large range, varnishes cannot have drying speed at the same time, etc., to achieve excellent leveling, cost-effective, paint The appearance of the film is smooth and bright

Inactive Publication Date: 2013-04-03
同宇新材料(广东)股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, ordinary domestic repair varnishes are difficult to meet the needs of the market
[0003] In order to solve the problem that the varnish cannot have a very fast drying speed and an excellent appearance at the same time, it is generally solved by using optimal resins, curing agents, catalysts, solvents, etc., to a certain extent, it can also endow the coating with very fast surface drying and Internal chemical crosslinking, while ensuring the excellent and even excellent appearance quality of the paint film, but the price of this kind of varnish is relatively high, and it is difficult to popularize and use it on a large scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydroxy acrylic resin for ultra-fast dry automobile varnish and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Prepare raw materials:

[0032] Get 28 kilograms of trimethylbenzenes and 10 kilograms of xylenes, mix and form A material;

[0033] Get 20 kilograms of styrene, 12 kilograms of sec-butyl methacrylate, 10 kilograms of hydroxypropyl methacrylate, 2 kilograms of methacrylic acid and 0.4 kilogram of maleic anhydride, and mix them into B material;

[0034] Get 1 kilogram of benzoyl peroxide, 2 kilograms of dicumyl peroxide and 3 kilograms of di-tert-butyl peroxide and mix to form C material;

[0035] 2. Put material A into the reactor and raise the temperature to 152°C;

[0036] 3. Add material B dropwise, the dropping time is controlled at 3.5 hours, and the temperature in the reactor is controlled at 152°C;

[0037] 4. After the dropwise addition, keep warm at 152°C for 4 hours;

[0038] 5. Add material C and keep warm for another 4 hours;

[0039] 6. Lower the temperature below 80° C., filter and pack to obtain the ultra-fast-drying hydroxyacrylic resin for automo...

Embodiment 2

[0041] 1. Prepare raw materials:

[0042] Get 29 kilograms of trimethylbenzenes and 12 kilograms of xylenes, mix and form A material;

[0043] Get 22 kilograms of α-styrene, 13 kilograms of tert-butyl methacrylate, 11 kilograms of hydroxypropyl methacrylate, 3 kilograms of methacrylic acid and 0.4 kilogram of maleic anhydride, and mix them into material B;

[0044] Get 2 kilograms of benzoyl peroxide, 3 kilograms of dicumyl peroxide and 2 kilograms of di-tert-butyl peroxide and mix to form C material;

[0045] 2. Put material A into the reactor and heat up at 148°C;

[0046] 3. Add material B dropwise, the dropping time is controlled within 4 hours, and the temperature in the reactor is controlled at 148°C;

[0047] 4. After the dropwise addition, keep warm at 148°C for 4 hours;

[0048] 5. Add material C and keep warm for another 4 hours;

[0049] 6. Lower the temperature below 80° C., filter and pack to obtain the ultra-fast-drying hydroxyacrylic resin for automobile var...

Embodiment 3

[0051] 1. Raw material preparation:

[0052] Get 30 kilograms of mesitylene and 15 kilograms of dimethylbenzene, mix and form A material;

[0053] Get 22 kilograms of styrene, 12 kilograms of tert-butyl methacrylate, 12 kilograms of hydroxypropyl methacrylate, 4 kilograms of methacrylic acid and 0.5 kilogram of fumaric acid, and mix them into B material;

[0054] Get 2 kilograms of benzoyl peroxide, 1 kilogram of dicumyl peroxide and 3 kilograms of di-tert-butyl peroxide and mix to form C material;

[0055] 2. Put material A into the reactor and heat up at 150°C;

[0056] 3. Add material B dropwise, the dropping time is 3 hours, and the temperature in the reactor is controlled at 150°C;

[0057] 4. After the dropwise addition, keep warm at 150°C for 4 hours;

[0058] 5. Add material C and keep warm for another 4 hours;

[0059] 6. Lower the temperature below 80° C., filter and pack to obtain the ultra-fast-drying hydroxyacrylic resin for automobile varnishes of the present...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of hydroxy acrylic resin for ultra-fast dry automobile varnish. The preparation method comprises the following steps of: 1) putting a material A into a reaction kettle, and heating the material A to the temperature of between 140 and 160 DEG C; 2) dripping a material B for 3 to 4 hours, and controlling the temperature in the reaction kettle at 140 to 160 DEG C; 3) after the dripping is finished, preserving the heat for 3.5 to 4.5 hours at the temperature of between 140 and 160 DEG C; 4) adding a material C, and performing heat preservation reactionfor 3.5 to 4.5 hours; and 5) cooling the reaction product to be less than 80 DEG C, and filtering the reaction product, wherein the material A comprises 10 to 15 weight parts of dimethyl benzene and 28 to 32 weight parts of trimethyl benzene; the material B comprises 20 to 25 weight parts of styrene or alpha-styrene, 12 to 15 weight parts of sec-butyl methacrylate or tert-butyl methacrylate, 10 to 12 weight parts of propyl methacrylate or ethyl methacrylate or ethyl acrylate, 2 to 4 weight parts of methyl acrylic acid, and 0.3 to 1.0 weight part of maleic anhydride or fumaric acid; and the material C is 6 to 9 weight parts of initiator. The hydroxy acrylic resin is applied to the varnish, and has ultra-fast dry curing property, good construction performance and varnish film appearance.

Description

technical field [0001] The present invention relates to a resin for automobile varnishes, in particular to a super-fast-drying hydroxyacrylic resin for automobile varnishes and a preparation method thereof. The resin is mainly used for high-grade automobile varnishes, has super-fast-drying and curing properties, and It has good construction performance and paint film appearance. Background technique [0002] High-quality fast-drying car refinish varnish means fast car refinishing service and satisfactory car refinishing quality to a certain extent. In the application of automotive refinishing paint, it often takes a period of time to dry the varnish after it is painted, and the subsequent polishing and other treatments can only be carried out after drying. The drying speed of the varnish often affects the work efficiency of the car refinishing, thus improving the performance of the varnish. The drying speed is generally valued; as the last paint film for car repair, the fin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F220/28C08F220/06C08F222/06C08F222/02C09D125/14
Inventor 杨剑黎邹发泽郑业梅何伍南张雁裕
Owner 同宇新材料(广东)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com