Polyester vortex spun woven fabric and preparation method thereof

A manufacturing method and technology of vortex spinning, applied in the manufacture of polyester vortex spinning woven fabrics, in the field of polyester vortex spinning woven fabrics, can solve the problems of low product yield, washability, poor wear resistance, and easy deformation of clothes

Active Publication Date: 2013-07-24
HANGZHOU AOHUA TEXTILE
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem solved by the present invention is that the fabrics provided by the prior art are not evenly dry, and the resulting fabrics are extremely prone to pilling, have poor washability and abrasion resistance, and the clothes are easily deformed, which cannot satisfy people's growing demand for clothing fabrics. Higher requirements, low production efficiency, inconvenient operation, and low product yield, and then provide a method for manufacturing polyester vortex woven fabrics and polyester vortex woven fabrics woven by this manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention is preferably specifically described below through examples, but the protection scope of the present invention is not limited thereto.

[0024] The present invention relates to a kind of manufacturing method of polyester vortex spinning woven fabric, and described manufacturing method comprises the following steps:

[0025] Step 1: use a carding machine to produce polyester fiber raw slivers or cationic polyester fiber raw slivers, draw on a drawing frame to obtain polyester fiber or cationic polyester fiber cooked slivers;

[0026] In this step, the polyester fiber or cationic polyester fiber has a density of 1.2-1.4D and a length of 38mm; generally, a polyester fiber with a density of 1.4D and a length of 38mm is selected for drawing, and 25 thick and thin yarns are prepared. The final product feels soft yet rigid.

[0027] Step 2: Place polyester fiber or cationic polyester fiber cooked slivers on a vortex spinning machine, and spin polyester v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing polyester vortex spun fabrics. The raw slivers of polyester fibers with cations are drawn on a drawing frame to obtain cooked slivers of polyester fibers, and the polyester vortex spun single yarns are spun at a certain speed, and are finished. Warp, parallel, and sizing to obtain polyester vortex spun single yarn as the warp beam of polyester vortex spun fabric, use single warp beam loom to use polyester vortex spun single yarn as warp, and other raw materials as weft, according to different requirements. As a whole, the polyester vortex woven fabric is obtained through secondary light desizing, disperse dyeing and drying; the polyester vortex woven fabric woven by this manufacturing method is suitable for clothing fabrics, with smooth surface and soft hand feeling. It has excellent anti-pilling, washability and moisture absorption. Compared with ordinary polyester-viscose fabrics, the surface quality is improved, the cost is reduced, and the energy consumption of the process of twisting into strands is saved. It is suitable for fabric processing and weaving in large quantities.

Description

technical field [0001] The invention belongs to the technical field of textiles and textile manufacturing, and in particular relates to a method for manufacturing a polyester vortex woven fabric and the polyester vortex woven fabric manufactured by the manufacturing method. Background technique [0002] Polyester vortex woven fabric is also called polyester cloth, which is mainly used for clothing manufacturing. Because it has the effect of wool-like fabric, it has good air permeability and moisture permeability and is easy to wash, so it is a wool-like top and pants material for men and women. The main fabric in. [0003] Along with the continuous improvement of people's living standards, in the fast-paced, high-efficiency, heavy-duty modern society, people desire to pursue randomness, comfort and practicality in nature. If it is not well dried, it is very easy to pilling, has poor washability and wear resistance, and is easy to deform after several washings, which cannot ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D13/00D06M15/11D06P1/00D06P3/52D06M101/32D03D15/283
Inventor 朱生贤
Owner HANGZHOU AOHUA TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products