A technology of pre-coating and aluminum plate, which is applied in the direction of coating, device for coating liquid on the surface, special surface, etc. It can solve the problems such as poor bonding of aluminum plate, achieve the expansion of manufacturing process, improve deep drawing formability, and improve operational effect

Inactive Publication Date: 2011-11-16
KOBE STEEL LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there are no functional groups and starting points of chemical bonds such as hydroxyl, carboxyl, ester bond, i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Precoated aluminum plate
  • Precoated aluminum plate
  • Precoated aluminum plate

Examples

Experimental program
Comparison scheme
Effect test

Example

[0077] first embodiment

[0078] Hereinafter, the best mode of the precoated aluminum sheet of the present invention will be specifically described with reference to appropriate drawings.

[0079] In the attached drawings, figure 1 It is a partial cross-sectional view schematically showing the structure of the precoated aluminum sheet of the present invention.

[0080] (pre-coated aluminum sheet)

[0081] like figure 1 As shown, a precoated aluminum plate 1 forms a precoated film 3 containing an intermolecularly crosslinked base resin 4 and fine particles 5 on the surface of an aluminum plate 2 . Here, the surface of the aluminum plate 2 refers to at least one surface of the aluminum plate 2 . Each configuration will be described below.

[0082] (aluminum plate)

[0083] The aluminum plate 2 of the present invention is made of aluminum or an aluminum alloy, and the aluminum plate (aluminum plate or aluminum alloy plate) 2 used in the present invention is not particular...

Example

[0125] second embodiment

[0126] (pre-coated aluminum sheet)

[0127] like figure 1 As shown, the pre-coated aluminum plate 1 of the present invention is a pre-coated aluminum plate 1 with a pre-coated film 3 formed on the outermost surface of the aluminum plate 2. The pre-coated film 3 is made of epoxy resin and non-yellowing isocyanate It is composed of a thermosetting resin (base resin) 4 that is intermolecularly cross-linked with a curing agent, and has a gel fraction of not less than 70% and not more than 92%. In addition, although the microparticles|fine-particles 5 are not an essential component (constitution) of this invention, but are preferably contained in the precoat film 3, it is shown in a figure. Here, the surface of the aluminum plate 2 means at least one surface of the aluminum plate 2 . Each configuration will be described below.

[0128] (aluminum plate)

[0129] Since it is the same as the first embodiment, description is omitted.

[0130] (pre-coat...

Example Embodiment

[0160] Example

[0161] first embodiment

[0162] Next, the precoated aluminum plate of the present invention will be specifically described by comparing the examples satisfying the conditions of the present invention and the comparative examples not satisfying the conditions of the present invention.

[0163] (first embodiment)

[0164] In the first embodiment, the durability of the film in the cleaning step, which is an essential object of the present invention, was investigated for the precoated aluminum plate of the present invention.

[0165] When discussing the precoated aluminum plate of the present invention, as the aluminum plate used as a raw material, an alloy number A1100-H24 having a plate thickness of 0.3 mm was used. After alkali degreasing with a weak base degreasing agent, chromium phosphate treatment is performed as a base treatment. The condition of chromium phosphate treatment is 20mg / m2 in terms of chromium adhesion 2 . In addition, the mechanical pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Arithmetic mean roughnessaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

A precoated aluminum plate (1) has a precoated film (3) on an aluminum plate (2), wherein the precoated film includes molecular cross-linked base resin (4) and particles (5), wherein said precoated film (3) includes 50% or more of gel fraction and has a surface roughness of 0.25 micrometers or more in the arithmetic average (Ra).

Description

technical field [0001] The present invention relates to a pre-coated aluminum sheet (Pre-coated Aluminum Sheet) using an aluminum sheet as a raw material, which is mainly used for industrial electronic equipment, consumer electronic equipment, and electronic components for automobiles. Background technique [0002] In Patent Document 1 and Patent Document 2, housings (covers, etc.) of commercial electronic devices such as optical disc drives can be applied to form an aluminum plate into a box shape by 90-degree bending workability. The technology for producing box-shaped frames by bending is a technology that can be continuously formed by using a roll-shaped plate with a forward die. In addition, the continuous forming technology using quick-drying stamping oil has also been established, so there is no need for press forming. The post-cleaning process is excellent in productivity. However, since the frame manufactured by bending processing inevitably has gaps at the corners...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/08B05D5/06B05D7/14B32B15/09
CPCB05D2202/25B05D7/14
Inventor 服部伸郎
Owner KOBE STEEL LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap