A production method and technology for cultural porcelain, applied in the field of daily-use ceramics, can solve the problems of insufficiently bright and smooth glaze surface, few product designs and colors, low-grade ceramic products, etc., and achieve the effects of simple and elegant color, smooth feel and colorful colors.
Active Publication Date: 2015-11-25
GUANGXI NANSHAN PORCELAIN
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, except for a few enterprises, the celadon products produced by most celadon manufacturers are not uniform in color, the color is not bright enough, the glaze is not bright enough, the product design and color are few, and the grade of ceramic products is low. Further enrich the variety of ceramics, especially celadon, and improve the quality. , to meet the needs of consumers at different levels of society, and has positive significance for promoting industrial development
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0022] The present invention will be described in detail below as an example of a kind of ancient green culture porcelain bowl whose surface pattern is a map of Confucian sages and holy relics.
[0023] The ancient Qing culture porcelain bowl is composed of 95.5% of base material and 4.5% of coloring material in percentage by weight of raw materials of the green body ingredients.
[0024] The ancient Qing culture porcelain bowl has the following raw material weight percentages of raw body base material ingredients: feldspar sand 48%, high white clay 23%, clay 9%, kaolin 20%.
[0025] The ancient Qing culture porcelain bowl is composed of 6% of cobalt black, 7% of fruit green, 9% of chrome green and 78% of mineralizer by weight percentage of the raw materials of the color ingredients.
[0026] Said Ancient Qing Culture Porcelain Bowl, the enamel ingredients are composed of 37% of feldspar, 22% of quartz, 11% of talc, 13% of limestone, 10% of kaolin, 3% of zinc oxide, mineraliza...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
water absorption
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to ancient blue and white porcelain and a production method thereof. The ancient blue and white porcelain comprises a blank body ingredient and a porcelain glaze ingredient. The production method comprises the following steps of: manufacturing a blank body, coloring matters, porcelain glaze, stained paper and applique decoration liquid; mixing a blank substrate with the coloring matters to obtain the blank body ingredient; adding an appropriate amount of water for performing ball milling; and performing iron sieving, clay squeezing, crude refining, ageing, refining, rolling molding, drying, blank trimming, line drawing, glaze applying, stained paper attaching, baking and drawing to obtain a finished product. Due to the adoption of the production method, the principle of color development from body glaze in the conventional celadon color tone is changed, part of color development pigment is added into the blank body substrate to obtain the blank body, stained paper with various historical character miracles or pictures and texts is attached to a glaze layer, the ancient blue and white porcelain obtained by one-step baking at high temperature has the advantages of stable blue tone, abundant colors, shining and smooth appearance, simple and elegant color and luster, high strength, high thermal stability, extremely small dissolved quantity of lead and cadmium, smoothness and light transmittance, safety and sanitation. The preparation method is scientific and reasonable and is suitable for mass production.
Description
technical field [0001] The invention belongs to the technical field of daily-use ceramics, and relates to a ceramic product and a production method thereof, in particular to an ancient blue culture porcelain and a production method thereof. Background technique [0002] Celadon is a kind of famous traditional Chinese porcelain. Celadon is famous all over the world for its delicate porcelain quality, bright and smooth lines, dignified and simple shapes, and pure and colorful colors. Celadon not only includes blue and green, but also has different shades in terms of quality, which is due to the thickness and difference of the glaze layer, which results in different tones after firing. The cyan color comes from the green glaze, so it is called "celadon ware". The celadon porcelain is a high-temperature color glaze variety with iron as the colorant. Turquoise glaze), fired in reducing flame. The color tone of celadon is mainly caused by a certain amount of iron oxide containe...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.