Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Composition for high-property heat-resisting corrosion-resisting glass fiber

A glass fiber, high-performance technology, applied in the field of high-performance heat-resistant and corrosion-resistant glass fiber compositions, can solve the problems of poor acid resistance of fibers, and achieve the effects of high grade, light weight and wide source of raw materials

Active Publication Date: 2013-11-06
NANJING FIBERGLASS RES & DESIGN INST CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And the above glass contains more Na 2 O and K 2 O, fiber acid resistance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for high-property heat-resisting corrosion-resisting glass fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] Embodiments of the present invention and S-2 ? 、Advantex ? 、Hiper-tex ? 、HS2 ? 、HS4 ? The glass fiber comparison data are shown in the table below:

[0040]

[0041] Calculate the required amount of various raw materials according to the chemical composition of the formulas listed in the above table, and mix them evenly to prepare batches after accurate weighing, and place them in a platinum-rhodium alloy melting crucible at a temperature range of 1500 ° C to 1530 ° C , melted while stirring, and melted for 20 hours to obtain clarified and homogenized molten glass. Flow the molten glass onto a heat-resistant steel plate, and obtain a glass block after cooling, and then part of the melted glass Put it into a single-hole platinum-rhodium wire drawing furnace, remelt it at 1440 ° C ~ 1450 ° C, and draw it into Continuous glass fiber with a diameter of 5-22 μm. The new eco-strength of the glass fibers of the above-mentioned embodiments with a diameter of 7-8 μm wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystallization temperatureaaaaaaaaaa
diameteraaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a composition for high-property heat-resisting corrosion-resisting glass fiber. The composition comprises the following components: 55-63wt% of SiO2, 18-23wt% of Al2O3, 8-16wt% of MgO, 7-13wt% of CaO, 0-1wt% of CeO2, 0-0.5wt% of Li2O, 0-0.4wt% of Fe2O3, 0-2wt% of TiO2, 0-0.5wt% of WO3 and 0-1.5wt% of Bi2O3, wherein the total content of SiO2, Al2O3, MgO and CaO is 94-98wt%; and CeO2, Li2O, Fe2O3, TiO2, WO3 and Bi2O3 are modifiers, the content of a single modifier is 0 at different times, and the total content of the modifiers is 2-6wt%. According to the invention, raw materials are adopted to produce the high-property heat-resisting corrosion-resisting glass fiber, thus the production difficulty is low, and the cost is low; and the produced glass fiber can be used as a reinforcing material and a heat-resisting heat-insulating material of a resin-based composite material and has the characteristics of high strength, corrosion resistance, high temperature resistance and light mass.

Description

technical field [0001] The invention is a composition for high-performance heat-resistant and corrosion-resistant glass fiber. The glass fiber can be used in the field of advanced composite materials and high-temperature heat insulation materials with high performance requirements such as high strength, high temperature resistance, and high acid resistance. performance fiberglass composition field. Background technique [0002] Continuous glass fiber has the characteristics of large specific surface area, high specific strength, heat resistance, non-combustibility, stable physical and chemical properties, etc., and has certain functional designability. Since its birth in the 1930s, with the development of glass fiber production technology, the product has been widely used And aerospace, aviation, automobile, shipbuilding, petrochemical, electrical, electronics, construction, environmental protection, energy, sports and leisure equipment, medical and health and other fields. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C13/00
CPCC03C3/087C03C3/095C03C13/00
Inventor 祖群黄松林陈汉仪刘劲松
Owner NANJING FIBERGLASS RES & DESIGN INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com