Preparation method for anti-flaming bamboo floor

A bamboo floor, flame retardant technology, applied in the direction of floors, buildings, building structures, etc., can solve problems such as fire hazards, reduce free formaldehyde content, good loss resistance, and good flame retardant performance. Effect

Inactive Publication Date: 2012-06-13
朱江福
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wood-based panels are wood fiber raw materials separated into various shapes of unit materials by mechanical processing, and then combined and pressed into various boards, including medium density fiberboard, particle board, plywood and other varieties, which are widely used in furniture manufacturing and construction industries. , interior decoration industry; but wood-based panels are combustible materials, and there is a greater risk of fire in use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for anti-flaming bamboo floor
  • Preparation method for anti-flaming bamboo floor
  • Preparation method for anti-flaming bamboo floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: a kind of fire-retardant bamboo floor preparation method, it comprises the following steps successively

[0017] (1) The original bamboo warp is cut into pieces and sawed to obtain a plain board;

[0018] (2) Carbonization treatment, put the bamboo chips into a high-pressure treatment tank, then introduce high-pressure saturated steam into the tank, raise the pressure to 0.2MPa, keep the heat for 3 hours, and finally release the pressure. water out again;

[0019] (3) Drying, place the base plate in a drying oven to control the temperature in the drying oven to 150°C, the humidity to 75%, and the drying time to 2 hours, so that the moisture content of the base plate is adjusted to 8%;

[0020] (4) Flame retardant treatment: vacuum pressure impregnation method, vacuum degree 80kPa, vacuum time 1.5h, impregnation pressure 0.5MPa, impregnation time 2h; flame retardant consists of the following raw materials with the following components and corresponding per...

Embodiment 2

[0024] Embodiment 2: a kind of fire-retardant bamboo floor preparation method, it comprises the following steps successively

[0025] (1) The original bamboo warp is cut into pieces and sawed to obtain a plain board;

[0026] (2) Carbonization treatment, put the bamboo chips into a high-pressure treatment tank, then introduce high-pressure saturated steam into the tank, raise the pressure to 0.3MPa, keep the heat for 4 hours, and finally release the pressure. water out again;

[0027] (3) Drying, place the base plate in a drying oven to control the temperature in the drying oven to 160°C, the humidity to 80%, and the drying time to 3 hours, so that the moisture content of the base plate is adjusted to 5%;

[0028] (4) Flame retardant treatment: Vacuum pressurized impregnation method, vacuum degree 87kPa, vacuum time 2h, impregnation pressure 0.6MPa, impregnation time 3h; flame retardant is mixed with the following components and corresponding percentages of raw materials be ...

Embodiment 3

[0032] Embodiment 3: a kind of flame-retardant bamboo floor preparation method, it comprises the following steps successively

[0033] (1) The original bamboo warp is cut into pieces and sawed to obtain a plain board;

[0034] (2) Carbonization treatment, put the bamboo slices into the high-pressure treatment tank, then introduce high-pressure saturated steam into the tank, raise the pressure to 0.25MPa, keep the heat for 3.5 hours, and finally release the pressure. water out again;

[0035] (3) Drying, place the base plate in a drying oven to control the temperature in the drying oven to 155°C, the humidity to 77%, and the drying time to 2.5 hours, so that the moisture content of the base plate is adjusted to 6%;

[0036] (4) Flame retardant treatment: adopt vacuum pressure impregnation method, vacuum degree 85kPa, vacuum time 1.7h, impregnation pressure 0.5MPa, impregnation time 2.5h; flame retardant consists of components and corresponding percentages as follows Raw mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of bamboo floor processing, in particular to a preparation method for an anti-flaming bamboo floor. The preparation method for the anti-flaming bamboo floor is realized by the following technical scheme that the preparation method for the anti-flaming bamboo floor comprises the following steps: (1) cutting off and hacking an original bamboo, and sawing to obtain a green blank plate; (2) carrying out carbonized treatment, putting a bamboo chip into a high-pressure processing tank, introducing high-pressure saturated vapor into the tank, improving pressure to 0.2-0.3MPa, keeping warm and pressure for 3-4 hours, finally releasing pressure, and bleaching water to take out after pressure is released; (3) drying to cause the moisture content of the blank plate to be regulated to 5-8%; (4) anti-flaming treatment: adopting a vacuum pressurizing and impregnating method, wherein the vacuum degree is 80-87kPa, the vacuum time is 1.5-2 hours, the impregnating pressure is 0.5-0.6MPa, and the impregnating time is 2-3 hours; and (5) carrying out hot pressure at the hot pressing temperature of 120-150 DEG C and the pressure of 2.5-3MPa for 15-20 minutes. The bamboo floor prepared with the method not only has a good favorable physical performance but also has a good anti-flaming effect.

Description

technical field [0001] The invention relates to the field of bamboo floor processing, in particular to a method for preparing a flame-retardant bamboo floor. Background technique [0002] Wood-based panels are wood fiber raw materials separated into various shapes of unit materials by mechanical processing, and then combined and pressed into various boards, including medium density fiberboard, particle board, plywood and other varieties, which are widely used in furniture manufacturing and construction industries. , Interior decoration industry; however, wood-based panels are combustible materials, and there is a greater fire risk in use. In order to reduce fire hazards and increase public safety, it is very necessary to research and develop flame-retardant wood-based panels. Contents of the invention [0003] The object of the present invention is to provide a method for preparing flame-retardant bamboo flooring. The bamboo flooring prepared by the method not only has go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02
Inventor 朱江福
Owner 朱江福
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap