Preparation method of gelatin/poli vinyl alcohol (PVA) composite films improved by inorganic imvite

A technology of inorganic montmorillonite and composite membrane, which is applied in the field of preparation of gelatin/PVA composite membrane, can solve the problems of limited mechanical properties, limited application surface of composite membrane, etc., and achieves increased mechanical properties, good degradability, and good compatibility. Effect

Inactive Publication Date: 2012-07-18
HENAN UNIV OF SCI & TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Gelatin is a protein composed of various amino acids and derived from animal bodies. It is a natural polymer material. Because of its good biocompatibility, degradability, and film-forming properties, it is often combined with other Or a variety of different synthetic polymer materials to prepare degradable composite materials, among many synthetic polymer materials, polyvinyl alcohol (PVA) is a commonly used polymer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] A preparation method of gelatin / PVA composite film modified by inorganic montmorillonite, the process includes the following steps:

[0013] (1) Preparation of polyvinyl alcohol solution: Weigh 4-11 parts by weight of polyvinyl alcohol into a three-necked flask, then measure 80-105 parts by weight of distilled water into the three-necked flask, and place the flask at 80-90°C Stir in a constant temperature water bath until the polyvinyl alcohol is completely dissolved to obtain an aqueous solution of polyvinyl alcohol, namely A solution;

[0014] (2) Preparation of gelatin solution: Weigh 5-10 parts by weight of gelatin into a beaker, then measure 80-100 parts by weight of distilled water into the beaker, swell for 30 minutes at room temperature, and stir in a constant temperature water bath at 50°C When the gelatin is completely dissolved, filter to remove impurities to obtain a gelatin solution, namely B solution;

[0015] (3) Preparation of gelatin / PVA composite film: Weigh...

Example Embodiment

[0021] Example 1

[0022] Weigh 10g of polyvinyl alcohol into a three-necked flask, add 90g of distilled water, mechanically stir it in a constant temperature water bath at 90°C until it is completely dissolved, and filter to remove impurities to obtain an aqueous solution of polyvinyl alcohol with a solution concentration of 10%;

[0023] Weigh 10g of gelatin into a beaker, add 90g of distilled water, swell at room temperature for 30 minutes, then stir in a constant temperature water bath at 50°C until it is completely dissolved, and then filter to remove impurities to obtain a gelatin solution with a solution concentration of 10%;

[0024] Add the above polyvinyl alcohol solution and gelatin solution to a 250ml three-necked flask at a weight ratio of 4:1, then add 0.6% of the total weight of the two solutions, plasticizer ethylene glycol, and store at 0°C for 5 hours. Add 0.05% sodium-based montmorillonite of the total weight of the two solutions, and then mechanically stir the rea...

Example Embodiment

[0026] Example 2

[0027] Weigh 10g of polyvinyl alcohol into a three-necked flask, add 90g of distilled water, mechanically stir it in a constant temperature water bath at 90°C until it is completely dissolved, and filter to remove impurities to obtain an aqueous solution of polyvinyl alcohol with a solution concentration of 10%;

[0028] Weigh 10g of gelatin in a beaker, add 90g of distilled water, swell at room temperature for 30 minutes, then stir in a 50°C constant temperature water bath until it is completely dissolved, and then filter to remove impurities to obtain a gelatin solution with a solution concentration of 10%;

[0029] Add the above polyvinyl alcohol solution and gelatin solution to a 250ml three-necked flask at a weight ratio of 4:1, then add 0.6% of the total weight of the two solutions, plasticizer glycerin, and store them at 5°C for 2 hours, then add two Sodium-based montmorillonite with 0.08% of the total weight of the solution, then mechanically stirred for 4 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of gelatin/poli vinyl alcohol (PVA) composite films improved by inorganic imvite and relates to the preparation method of the gelatin/PVA films. PVA water solution and gelatin water solution are firstly prepared, then, two kinds of solution are mixed according to a certain proportion, plasticizers are added, then, the mixed solution is stored for a period of time at low temperature being 0 to 10 DEG C, a certain mount of inoganic imvite is added, then the mixed solution is stirred in thermostatic waterbath under 30-70 DEG C to be uniformly mixed, the uniformly mixed solution is poured into a mold for natural curtain coating, next, the materials are dried at the room temperature, and the gelatin/PVA composite films improved by the inorganic imvite are obtained. Compared with the ordinary films, the gelatin/PVA composite films prepared by the preparation method have the advantages that good compatibility and degradability are realized, meanwhile, the mechanical property is much better than that of ordinary films, and the tensile strength and the fracture elongation of the films are improved to different degrees.

Description

technical field [0001] The invention relates to a preparation method of a gelatin / PVA composite film, in particular to a preparation method of a gelatin / PVA composite film improved with inorganic montmorillonite. Background technique [0002] Gelatin is a protein composed of various amino acids and derived from animal bodies. It is a natural polymer material. Because of its good biocompatibility, degradability, and film-forming properties, it is often combined with other Or a variety of different synthetic polymer materials to prepare degradable composite materials, among many synthetic polymer materials, polyvinyl alcohol (PVA) is a commonly used polymer material, PVA is a non-toxic, non-toxic An irritating hydrophilic polymer with good bio-affinity, film-forming properties and good mechanical properties. The ordinary gelatin / PVA composite film prepared with these two materials can also be used in a certain ratio. It has the advantages of both materials, but in general its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J5/18C08L29/04C08L89/00C08K13/02C08K3/34C08K5/053
Inventor 高喜平姚大虎赫玉欣陆昶张玉清李纪伟刘如意徐冉
Owner HENAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap