A defoamer and plastic technology, applied in the field of plastic defoamer, can solve the problems of reduced performance of plastic products and strict storage conditions, and achieve the effect of improving performance, avoiding failure, and improving self-protection function.

Active Publication Date: 2014-10-01
ZHEJIANG JIANDE HONGXING CALCIUM
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a plastic defoamer to solve the problem that the performance of plastic products is reduced due to the difficulty in eliminating the moisture in the plastic raw materials during the production of plastics, and the existing plastic defoaming masterbatch has stricter storage conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Mix 20kg of calcium oxide powder with a particle size of ≤200 mesh and 16kg of a mixture of linear low density polyethylene and styrene-butadiene rubber at a weight ratio of 1:1, 10kg of butyl stearate, 2.5kg of polymethyl acrylate, and 3kg of stearic acid Zinc and 1.5 kg of titanate coupling agent were mixed, kneaded at 110°C for 20 minutes, and then extruded and granulated by a twin-screw extruder to prepare a plastic defoamer.

Embodiment 2

[0017] 25kg of calcium oxide powder with a particle size of ≤200 mesh, 12kg of a mixture of linear low-density polyethylene and styrene-butadiene rubber with a weight ratio of 1:1, 5kg of ethylene bisstearamide, 4kg of polymethyl acrylate, and 2kg of stearic acid The barium and 3 kg of titanate coupling agent were mixed, kneaded at 150° C. for 20 minutes, and then extruded and granulated by a twin-screw extruder to prepare a plastic defoamer.

Embodiment 3

[0019] 23kg of calcium oxide powder with a particle size of ≤200 mesh, 15kg of a mixture of linear low-density polyethylene and styrene-butadiene rubber with a weight ratio of 1:1, 8kg of oxidized polyethylene wax, 5kg of polymethyl acrylate, and 4.5kg of calcium stearate Mix with 0.5 kg titanate coupling agent, knead at 120° C. for 20 minutes, and then extrude and granulate with a twin-screw extruder to prepare a plastic defoamer.

[0020] By placing the prepared plastic defoamer in the air and weighing it at different times, see Table 1 for details.

[0021] Table 1

[0022] time in air Example 1 Example 2 Example 3 1h 100% 100% 100% 2h 100% 100% 100% 5h 100% 100% 100% 10h 100% 100% 100% 24h 100% 100% 100% 10d 100.3% 100.5% 100.3%

[0023] By adding the plastic defoamer prepared by each embodiment of the present invention to plastics such as PVC, PP, PS and ABS, compared with the plastic product without adding pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of plastic processing, in particular to a plastic defoamer. A plastic defoamer of the present invention is made of the following components in parts by weight: 40-50 parts of calcium oxide, 30-40 parts of linear low-density polyethylene and styrene-butadiene rubber in total, and 10-20 parts of lubricant , 5-10 parts of polymethyl acrylate, 4-9 parts of metal soap, 1-3 parts of titanate coupling agent. The invention coats the plastic defoamer with polymethyl acrylate, isolates the contact between the plastic defoamer and the air and prevents moisture absorption, improves the safety and applicability of the plastic defoamer, and at the same time uses a coupling agent to reduce the impact of calcium oxide on the plastic The influence of the performance has achieved the effect of eliminating the residual moisture in the plastic without affecting the basic performance of the plastic.

Description

technical field [0001] The invention relates to the field of plastic processing, in particular to a plastic defoamer. Background technique [0002] The application of plastics in the manufacturing industry is ubiquitous at this stage. There are all kinds of plastic products. The application of plastics is not only diverse, but also in a wide range of fields. However, there is a common problem in the process of plastic applications. Due to The plastic masterbatch contains moisture. During the secondary processing of the plastic, due to the increase in temperature, the moisture in the plastic vaporizes rapidly at high temperature, but the moisture is wrapped by the molten plastic melt, and the moisture cannot escape, resulting in Moisture stays in the plastic or on the surface to form many holes and bubbles. Such holes and bubbles will not only affect the appearance of the final product, but also lead to a significant decrease in the mechanical properties of plastic products, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L9/06C08L33/08C08K3/22C08K5/098C08K13/02
Inventor 周建红
Owner ZHEJIANG JIANDE HONGXING CALCIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap