Silicic acid mud interior wall decorating material and preparation method thereof

A decorative material and silicate mud technology, which are applied in the field of silicate mud interior wall decorative materials and their preparation, and can solve the problem of poor texture, inability to meet the requirements of decorative effect and air quality, and lack of air humidity adjustment and lasting purification effects. and other problems, to achieve the effect of eliminating odor, good interior wall decoration effect, and improving activation performance.

Inactive Publication Date: 2013-07-10
商志民
View PDF5 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the harmful components of this paint do not exceed the standard, the texture is poor, and it does not have the effect of regulating and lasting purification of indoor air humidity, and cannot meet people's requirements for decorative effects and air quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicic acid mud interior wall decorating material and preparation method thereof
  • Silicic acid mud interior wall decorating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1, specific formula: 500 grams of diatomite, 50 grams of sepiolite, 50 grams of kaolin, 100 grams of lime calcium, 50 grams of heavy calcium, 50 grams of wollastonite, 50 grams of white cement, 50 grams of silica sand, talcum powder 50 grams, 5 grams of nano-titanium dioxide, 10 grams of ethylene-vinyl acetate copolymer, 1 gram of cellulose ether, 1 gram of magnesium aluminum silicate, 1 gram of easily dispersible fiber, and 5 grams of inorganic pigment.

Embodiment 2

[0043] Embodiment 2, specific formula: 100 grams of diatomite, 400 grams of sepiolite, 50 grams of kaolin, 100 grams of lime calcium, 50 grams of heavy calcium, 50 grams of wollastonite, 50 grams of white cement, 50 grams of silica sand, talcum powder 50 grams, 5 grams of nano-titanium dioxide, 10 grams of ethylene-vinyl acetate copolymer, 1 gram of cellulose ether, 1 gram of magnesium aluminum silicate, 1 gram of easily dispersible fiber, and 5 grams of inorganic pigment.

Embodiment 3

[0044] Embodiment 3, specific formula: 100 grams of diatomite, 50 grams of sepiolite, 200 grams of kaolin, 100 grams of lime calcium, 50 grams of heavy calcium, 50 grams of wollastonite, 50 grams of white cement, 50 grams of silica sand, talcum powder 50 grams, 5 grams of nano-titanium dioxide, 10 grams of ethylene-vinyl acetate copolymer, 1 gram of cellulose ether, 1 gram of magnesium aluminum silicate, 1 gram of easily dispersible fiber, and 5 grams of inorganic pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a silicic acid mud interior wall decorating material and a preparation method thereof. The silicic acid mud interior wall decorating material mainly comprises diatomite, sepiolite, kaolin, sierozem, coarse whiting, wollastonite, white cement, silica sand, talcum powder, nanometer titanium dioxide, ethylene-vinyl acetate copolymer, cellulose ether, aluminium-magnesium silicate, easily dispersed fiber, inorganic pigments and has the functions of humidity control and air purification. The preparation method comprises the following steps of: firstly acidizing the diatomite, the sepiolite and the kaolin, removing harmful ingredients in the diatomite, the sepiolite and the kaolin, improving the activation property of the material, then filtering, washing, drying and crushing, and finally adding the diatomite, the sepiolite and the kaolin and the other components to a dry powder blender for uniformly stirring. When being used, water is added to powder, so that the powder is prepared into paste or emulsion; the silicic acid mud interior wall decorating material is suitable for roll coating, spray finishing, blade coating and the like in interior wall decoration and has the functions of indoor humidity adjustment, peculiar smell elimination, removal of harmful gases such as formaldehyde and toluene in air and lasting environmental protection and simultaneously has the characteristics of rich color, strong sense of texture and environmental friendliness.

Description

technical field [0001] The invention belongs to interior decoration materials, in particular to a kind of diatomite, sepiolite, kaolin, lime calcium, heavy calcium, wollastonite, white cement, silica sand, talcum powder, nano-titanium dioxide, ethylene-vinyl acetate copolymer, The main raw materials are cellulose ether, magnesium aluminum silicate, easily dispersible fiber and inorganic pigment, and the silicate mud interior wall decoration material with the functions of humidity control and air purification and its preparation method are mainly suitable for interior wall decoration. Background technique [0002] At present, the indoor air pollution caused by conventional decorative materials widely used in the market has attracted more and more attention. With the continuous improvement of people's living conditions, people's selection standards for wall decoration materials are getting higher and higher, and The environmental protection performance of the material is liste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 商志民
Owner 商志民
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap