Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of high-temperature resistant hot-melt pressure-sensitive adhesive

A hot-melt pressure-sensitive adhesive, high-temperature technology, applied in the direction of adhesives, adhesive types, mineral oil hydrocarbon copolymer adhesives, etc., can solve the problems of adverse effects of hot-melt adhesive use temperature, etc., and achieve simple and easy raw material addition process Good, easy to process, high transparency effect

Active Publication Date: 2013-07-24
YUEYANG ORIENTAL YUHONG WATERPROOF TECH +1
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the plasticizer will inevitably have a plasticizing effect on the plastic phase, it will have an adverse effect on the use temperature of the hot melt adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-temperature resistant hot-melt pressure-sensitive adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Heat the equipment to 160°C, add 9.0kg of polyisobutylene 1, 10.3kg of naphthenic oil and 5.1kg of polyisobutylene 2, start stirring, add 20.5kg of elastomer 1 and 5.1kg of elastomer 2, add 0.5kg of antioxidant, and then Add 8.5kg C5 petroleum resin 1 and 41.0kg C5 petroleum resin 2, keep the temperature and stir for 2 hours. Measure its performance. See Table 1.

Embodiment 2

[0017] Heat the equipment to 160°C, add 9.0kg of polyisobutylene 1, 10.3kg of naphthenic oil and 5.1kg of polyisobutylene 2, start stirring, add 21kg of elastomer 1 and 4.3kg of elastomer 2, add 0.5kg of antioxidant, and then add 8.5kg C5 petroleum resin 1 and 41.0kg C5 petroleum resin 2, keep the temperature and stir for 2 hours. Measure its performance. See Table 1.

Embodiment 3

[0019] Heat the equipment to 160°C, add 9.0kg of polyisobutylene 1, 10.3kg of naphthenic oil and 5.1kg of polyisobutylene 2, start stirring, add 19.0kg of elastomer 1 and 6.6kg of elastomer 2, add 0.5kg of antioxidant, and then Add 8.5kg C5 petroleum resin 1 and 41.0kg C5 petroleum resin 2, keep the temperature and stir for 2 hours. Measure its performance. See Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a hot-melt pressure-sensitive adhesive for a high-density polyethylene self-adhesion coiled material. The preparation method comprises the following steps of: compounding another styrene diene styrene block copolymer (SDS) synthetic rubber by using an SDS rubber elastomer as a main matrix resin to modify an elastomer; and mixing with proper sticky resin, softening agents, antioxidant and the like to prepare the hot-melt pressure-sensitive adhesive. The characteristics of SDS synthetic rubber elastomers with two different molecule structures are fully utilized, and the problems of elasticity, room-temperature construction and high-temperature resistant adhesiveness are successfully solved, so that a product which is easy to process, compatible with various materials, and high in transparency, chemical resistance, long-term ageing resistance, high wettability of high-density polyethylene (HDPE) substrates and high in adhesion is obtained.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a method for preparing a hot-melt pressure-sensitive adhesive, in particular to a method for preparing a hot-melt pressure-sensitive adhesive for high-density polyethylene self-adhesive coils. Background technique [0002] High-density polyethylene (HDPE) self-adhesive film waterproof membrane and its pre-paved anti-adhesive construction technology were introduced into my country by American companies in the 1990s, and model laying was carried out in tunnels dug in underground subway intervals. In November 2008 and March 2009, the state issued relevant standards to vigorously promote the application of pre-paved construction technology and self-adhesive waterproof membrane materials. [0003] Since polyethylene is a non-polar material with low surface energy, it is a difficult-to-stick material. Hot-melt pressure-sensitive adhesives used to bond polyethylene materials must have a s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J157/02C09J153/02C09J123/20
Inventor 张正波田凤兰
Owner YUEYANG ORIENTAL YUHONG WATERPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com