A kind of preparation method of water-absorbing anti-fog film layer for automobile glass

A technology for automobile glass and water absorption, which is applied in the field of preparation of water-absorbing anti-fog film for automobile glass, can solve the problems of loss of anti-fog effect, low binding force between surfactant and glass surface, etc., and achieve long-term anti-fog performance, Avoid glass fogging and avoid impact effects

Active Publication Date: 2015-10-28
CHERY AUTOMOBILE CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to relevant tests, turning on the air conditioner to defog will increase the power consumption by 10-15%
[0003] Therefore, it is very necessary to develop spontaneous anti-fog technology. At present, there are many anti-fog agents and anti-fog towel products on the market. The main components are all surfactants, which have a certain anti-fog effect. Very low binding power, loses anti-fog effect after a short period of time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1. Preparation of water-absorbing resin

[0020] Add 30 parts of oxyalkylene polyol resin, molecular weight 400, 33 parts of acrylic polyol resin to 100 parts of ethyl acetate, stir evenly, add 50 parts of TDI-based aromatic isocyanate and 1 part of polyether alkylsiloxane Leveling agent, after mixing uniformly, the water-absorbent resin is obtained.

[0021] 2. Preparation of anti-fog film

[0022] First, use a mixture of methanol and water to degrease the surface of the car glass, then perform physical polishing, then clean it with tap water and distilled water, and then dry it for later use.

[0023] Use water-absorbent resin system to coat the surface of clean and dry automobile glass with roller coating.

[0024] After the film is leveled, place the glass in an anti-fog environment at 120°C for 1.5 hours. The film has good anti-fog performance, the anti-fog time is 15 minutes, and the glass permeability has no visible change after coating.

Embodiment 2

[0026] 1. Preparation of water-absorbing resin.

[0027] Add 40 parts of oxyalkylene polyol resin, molecular weight of 1000, 45 parts of polycaprolactone polyol resin to 80 parts of acetone, add 60 parts of curing agent aliphatic isocyanate and 1.5 parts of high molecular weight polysiloxane after stirring evenly , After stirring, the water-absorbent resin is obtained.

[0028] 2. Preparation of anti-fog film layer.

[0029] First, use ethanol to degrease the surface of the car glass, then perform physical polishing, and then clean it with tap water and distilled water, and then dry for use.

[0030] Use water-absorbent resin system to coat the glass surface on the clean and dry glass surface. The coating process is spin coating.

[0031] After the film is leveled, place the glass in an anti-fog environment at 130°C for 2 hours. The film has good anti-fog performance, the anti-fog time is 18 minutes, and the glass permeability has no visible change after coating.

[0032] Through the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a water absorbent anti-fog film used for automotive glass. The method comprises the following steps: step 1, preparing water absorbent resin from raw materials in parts by weight as follows: adding 10-40 parts of resin containing water absorbent groups and 10-50 parts of crosslinkable cured resin to 50-100 parts of organic solvents, mixing up, adding 20-60 parts of curing agent and 1-5 parts of flatting agent. mixing up and obtaining the water absorbent resin; step 2, preparing the anti-fog film: sequentially degreasing the surface of the automotive glass with the organic solvent, performing mechanical polishing, rinsing with tap water and distilled water respectively, and desiccating; performing surface coating on the clean and dry automotive glass with the water absorbent resin prepared according to the step 1, and placing the water absorbent anti-fog film at a temperature of 80-150 DEG C for 0.5-4h after the leveling of the water absorbent anti-fog film. The water absorbent anti-fog film provided by the invention can absorb and desorb steam without creating fog on the glass, and has a long-term anti-fog function.

Description

Technical field [0001] The invention relates to a material surface treatment method, in particular to a method for preparing a water-absorbing anti-fog film layer for automobile glass. Background technique [0002] In the cold winter or rainy season, the water vapor in the hot air in the car will form fog droplets on the surface of the cold glass, which greatly reduces the visible light transmittance of the glass, affects the driver's vision, and easily leads to traffic accidents. Since there is no hot air from the engine in the electric vehicle, the air conditioner needs to be turned on to defog. According to related tests, the power consumption of defogging the air conditioner will increase by 10-15%. [0003] Therefore, it is very necessary to develop spontaneous anti-fogging technology. At present, there are many anti-fogging agents and anti-fogging towel products on the market. The main ingredients are surfactants, which have a certain anti-fogging effect. However, the surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/32
Inventor 熊建民洪丽陈大华
Owner CHERY AUTOMOBILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap