Coffee carbon multi-component fiber weaving fabric and preparation method thereof

A multi-component fiber, coffee carbon fiber technology, applied in the direction of fabrics, textiles, textiles and papermaking, etc., to achieve the effect of high strength, excellent wearing performance and good drape

Active Publication Date: 2014-03-05
SHANDONG WOYUAN NEWFASHIONED FABRIC
View PDF7 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at present, it is basically used in underwear, T-shirts, socks and other knitwear in the international and domestic industries. There are still few studies on woven clothing fabrics containing coffee carbon fiber, because there are many technical problems, especially the pilling. Difficult to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coffee carbon multi-component fiber weaving fabric and preparation method thereof
  • Coffee carbon multi-component fiber weaving fabric and preparation method thereof
  • Coffee carbon multi-component fiber weaving fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] 1. It is made of the following raw materials: warp yarn, blended with the following raw materials in weight percentage:

[0057]

[0058]The weft filaments are two kinds of filaments arranged alternately at 1:1:

[0059] Coffee Carbon Filament 160D,

[0060] PTT filament 100D.

[0061] Two, preparation method comprises the steps:

[0062] Preparation before weaving of warp yarns and weft filaments → weaving → gray fabric inspection → scouring and pre-shrinking treatment → pre-singing → pre-singeing → high temperature and high pressure overflow dyeing → dehydration → opening width → tenter drying → post-singing → Soft finishing→calendering→pot steaming→cloth inspection→rolling;

[0063] 1. Preparation process before weaving of warp yarn and weft filament:

[0064] ①Doubling and double twisting:

[0065] Warp yarn: use a twist doubling machine to parallel two Z-twist 65S / 1 single yarns with the above-mentioned fiber ratio to form a plied yarn 65S / 2; twist with a t...

Embodiment 2

[0117] 1. Made of the following raw materials:

[0118] Radial yarn, blended from the following raw materials in weight percentages:

[0119]

[0120] The weft filaments are two kinds of filaments arranged alternately at 1:1:

[0121] Coffee Carbon Filament 150D,

[0122] PTT filament 120D.

[0123] Two, preparation method comprises the steps:

[0124] Preparation before weaving of radial yarns and weft filaments → weaving → gray fabric inspection → scouring and pre-shrinking treatment → pre-singing → pre-singeing → high temperature and high pressure overflow dyeing → dehydration → opening width → tenter drying → post-singing → Soft finishing→calendering→pot steaming→cloth inspection→rolling;

[0125] 1. Preparation process before weaving:

[0126] ①Doubling and double twisting:

[0127] Radial yarn: two 55S / 1 single yarns are paralleled with a twisted doubling machine to form a 55S / 2 ply yarn; twisted with a two-for-one twister, the twist is 1400T / m, S twist, and the...

Embodiment 3

[0147] 1. Made of the following raw materials:

[0148] Radial yarn, blended from the following raw materials in weight percentages:

[0149]

[0150] The weft filaments are two kinds of filaments arranged alternately at 1:1:

[0151] Coffee Carbon Filament 155D,

[0152] PTT filament 105D.

[0153] Two, preparation method comprises the steps:

[0154] Preparation before weaving of radial yarns and weft filaments → weaving → gray fabric inspection → scouring and pre-shrinking treatment → pre-singing → pre-singeing → high temperature and high pressure overflow dyeing → dehydration → opening width → tenter drying → post-singing → Soft finishing→calendering→pot steaming→cloth inspection→rolling;

[0155] 1. Preparation process of radial yarn and weft filament before weaving:

[0156] ①Doubling and double twisting:

[0157] Radial yarn: two 60S / 1 single yarns are paralleled with a twisted doubling machine to form a plied yarn of 60S / 2; twisted with a two-for-one twister, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
Basis weightaaaaaaaaaa
Basis weightaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of spinning, dyeing and finishing, and particularly relates to coffee carbon multi-component fiber weaving fabric and a preparation method of the coffee carbon multi-component fiber weaving fabric. The coffee carbon multi-component fiber weaving fabric is made of the following raw materials of warp direction yarns and weft direction filaments, wherein the warp direction yarns are formed by blending the following raw materials, by weight, 25-45% of coffee carbon fibers, 25-40% of bamboo fibers, 20-30% of cationic modified polyester fibers and 0.5-0.8% of conductive fibers, and the weft direction filaments are formed by alternately ranking 150D-160D coffee carbon fiber filaments and 100D-120D PTP fiber filaments at the ratio of 1 to 1. The coffee carbon multi-component fiber weaving fabric has the advantages that different characteristics of the coffee carbon fibers and the other fibers are exerted, comfort of the apparel fabric and the uvioresistant function and other protection functions are integrated, physicochemical indexes are good, dyefastness is high, and cost performance of the fabric is high. The preparation method is provided, the process is reasonable, and a new path is opened up for improving high performance and comfort of the coffee carbon multi-component fiber weaving fabric.

Description

technical field [0001] The invention belongs to the field of textile dyeing and finishing, and in particular relates to a coffee carbon multi-component fiber woven fabric and a preparation method thereof. Background technique [0002] Coffee carbon fiber is a functional fiber produced by using the coffee grounds left after drinking coffee, which is calcined and made into crystals, and then ground into nano-powders, which are added to polyester fibers. It has the functions and characteristics of antibacterial and deodorizing, diverging negative ions and anti-ultraviolet rays, heat storage and heat preservation, low-carbon environmental protection, and is being promoted as a new product and the concept of green environmental protection. [0003] However, at present, it is basically used in underwear, T-shirts, socks and other knitwear in the international and domestic industries. There are still few studies on woven clothing fabrics containing coffee carbon fiber, because ther...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/04D03D15/217D03D15/283D03D15/47D03D15/50D03D15/533
Inventor 东明洪武光信刘文和王红玲唐凯
Owner SHANDONG WOYUAN NEWFASHIONED FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com