Environmental protection coating with visible light catalytic function and preparation method thereof

An environmentally friendly coating and visible light technology, applied in the direction of radiation-absorbing coatings, powder coatings, alkali metal silicate coatings, etc., can solve the problems of easy loss of doping elements, loss of catalytic activity, weak light absorption ability, etc., to avoid accelerated Effect of aging and destroying resin, low cost, degrading harmful substances

Active Publication Date: 2017-01-04
SKSHU PAINT
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, photocatalysts that respond to visible light in this way have weak light absorption ability, generally low catalytic activity, and the problem of easy loss of doping elements, resulting in loss of catalytic activity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental protection coating with visible light catalytic function and preparation method thereof
  • Environmental protection coating with visible light catalytic function and preparation method thereof
  • Environmental protection coating with visible light catalytic function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] An environmentally friendly paint with visible light catalysis function, prepared from the following raw materials in the following weight ratio:

[0038]

[0039]

[0040] The preparation method of the environmental protection paint with visible light catalysis function is as follows:

[0041] Put each raw material into a ball mill and grind for 6 hours at a speed of 1500 rpm;

[0042] After the paint is ground, it is filtered with a 400-mesh filter and filled with nitrogen at a pressure of 0.10 MPa for packaging.

Embodiment 2

[0044] An environmentally friendly paint with visible light catalysis function, prepared from the following raw materials in the following weight ratio:

[0045]

[0046] The preparation method of the environmental protection paint with visible light catalysis function is as follows:

[0047] Put each raw material into a ball mill and grind for 0.5 hour at 700 rpm;

[0048] After the paint is grinded, it is filtered with a 300-mesh filter and filled with nitrogen at a pressure of 0.13Mpa for packaging.

Embodiment 3

[0050] An environmentally friendly paint with visible light catalysis function, prepared from the following raw materials in the following weight ratio:

[0051]

[0052]

[0053] The preparation method of the environmental protection paint with visible light catalysis function is as follows:

[0054] The raw materials were put into a ball mill and milled for 3 hours at a speed of 1100 rpm.

[0055] After the paint is ground, it is filtered with a 350-mesh filter and filled with nitrogen at a pressure of 0.12 MPa for packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an environment-friendly coating with visible light catalysis function, and a preparation method thereof, belonging to the field of a coating for building decoration. The environment-friendly coating with visible light catalysis function is prepared by the following active ingredients in parts by weight: 1-20 parts of modified nanocrystalline iron oxide powder with visible light catalysis function, 20-70 parts of silicate, 2-5 parts of gypsum powder, 1-10 parts of titanium dioxide, 0.1-5 parts of powder anticaking agent, 1-10 parts of curing conditioning agent, 1-10 parts of inorganic pigment, and 1-20 parts of filler. The prepared environment-friendly coating with visible light catalysis function not only has the characteristic of strong light absorption capability, but also widens the application range of light catalysis technology, and has higher catalytic activity regardless of ultraviolet light and visible light. In addition, the prepared environment-friendly coating with visible light catalysis function is easily available in raw materials, and low in cost.

Description

Technical field [0001] The invention relates to an environmentally friendly paint with photocatalytic function and a preparation method thereof, in particular to an environmentally friendly paint with visible light catalysis function and a preparation method thereof, and belongs to the field of architectural decoration paints. Background technique [0002] Environment and energy are major issues facing and urgently to be solved in the 21st century. Photocatalysis has become an ideal environmental pollution treatment technology and clean energy production due to its unique properties such as deep reaction at room temperature and direct use of solar energy as a light source to drive the reaction. technology. [0003] The photocatalytic method can completely mineralize and remove a variety of organic pollutants, and provides a highly effective method for the removal of various organic pollutants and reducing inorganic pollutants, especially toxic and harmful substances that are diffic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D1/02C09D7/12C09D5/03C09D5/32C09D5/00
Inventor 洪杰刘晓彬胡必忠
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap