A ceramic metal halide lamp anti-aging high-viscosity printing ink

A technology of ceramic metal halide lamps and printing inks, applied in inks, household utensils, applications, etc., can solve the problems of poor imprinting effect and low adhesion, and achieve good printing effect, good ductility, and not easy to wear.

Active Publication Date: 2016-05-18
JIAGNSU PUYA LIGHTING TECH PUBLIC CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of low adhesion and poor imprinting effect of the ink due to technical defects, the invention provides an anti-aging high-viscosity printing ink for ceramic metal halide lamps. By adding adhesion and chemical substances that promote ink dilution and fusion into the material, the ink Good ductility, can be effectively laid on the surface of the bulb, firmly bonded to the bulb, the printing effect is good, and the imprint is not easy to wear and fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ceramic metal halide lamp anti-aging high-viscosity printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The anti-aging high-viscosity printing ink for ceramic metal halide lamps provided by the present invention has the following raw material composition and weight percentage ratio:

[0032] Silver oxide 7%, lead borate 5%, monohydric alcohol 8%, glycerin 6%, curing agent 1.5%, polyester resin 7%, dispersant 1.6%, defoamer 2.8%, wetting agent 1%, varnish 1%, ethyl acetate 7%, β-myrcene 2%, waste engine oil 3%, castor oil 6%, sodium silicate 3%, and the rest is water.

Embodiment 2

[0034] The anti-aging high-viscosity printing ink for ceramic metal halide lamps provided by the present invention has the following raw material composition and weight percentage ratio:

[0035] Silver oxide 9%, lead borate 8%, monohydric alcohol 9%, glycerin 9%, curing agent 2.5%, polyester resin 10%, dispersant 2.3%, defoamer 3%, wetting agent 1.5%, varnish 3%, ethyl acetate 10%, β-myrcene 4%, waste engine oil 5%, castor oil 8%, sodium silicate 8%, and the rest is water.

Embodiment 3

[0037] The anti-aging high-viscosity printing ink for ceramic metal halide lamps provided by the present invention has the following raw material composition and weight percentage ratio:

[0038] Silver oxide 13%, lead borate 12%, monohydric alcohol 10%, glycerin 11%, curing agent 3.5%, polyester resin 12%, dispersant 3.8%, defoamer 4.0%, wetting agent 1.9%, varnish 5%, ethyl acetate 13%, β-myrcene 6%, waste engine oil 7%, castor oil 9%, sodium silicate 11%, and the rest is water.

[0039] The preparation process of this product:

[0040] 1. Prepare silver oxide, lead borate and ethanol according to the above weight ratio and put them into the ball mill jar, then add agate balls of equal weight (the size to weight ratio of agate balls is 1:1), close the ball mill cover tightly and carry out ball milling. The time is not less than 60 hours, and the speed of the ball mill is not less than 200 rpm; after 60 hours of ball milling, add a certain amount of glycerin according to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed anti-ageing high-viscosity stamping ink for ceramic metal halide lamps comprises the following raw materials in percent by weight: 7-13% of silver oxide, 5-12% of lead borate, 8-10% of a monohydric alcohol, 6-11% of glycerin, 1.5-3.5% of a curing agent, 7-12% of polyester resin, 1.6-3.8% of a dispersant, 2.8-4.0% of an antifoaming agent, and other compositions. The stamping ink is good in ductility, can be effectively paved on the surface of a bulb and firmly pasted on the bulb, and is excellent in printing effect; the mark is not easy to wear or fall off, also the phenomena that the mark has bubbles, is inclined, is fuzzy and has double images are reduced, and the success rate for printing marks is improved. The color rendering property and the light transmittance of the metal halide lamp are guaranteed, and the mark can keep legible and integral for a fairly long period.

Description

technical field [0001] The invention relates to a finished lamp printing plate ink, in particular to a ceramic metal halide lamp anti-aging high-viscosity printing ink. Background technique [0002] The metal halide lamp is a discharge lamp that works on an AC power source and produces arc discharge in the mixed vapor of mercury and rare metal halides. The metal halide lamp is the first high-pressure mercury lamp made by adding various metal halides. Three generations of light sources. Metal halide lamps have the characteristics of high luminous efficiency, good color rendering performance, and long life. Indoor lighting in other places. [0003] The preparatory work that needs to be done before manufacturing metal halide lamps is: 1. The tools, utensils and measuring tools required for the preparation work, and the materials required for the work. 2. Picking materials: pick up the required specifications and quantity of finished lamps, and check the quantity. When manuf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/03C09D11/104
Inventor 陈德军
Owner JIAGNSU PUYA LIGHTING TECH PUBLIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap