Preparation method of fiber-base-fabric foamed epoxy resin cloth

A technology of epoxy resin and fiber cloth, which is applied in the processing of textile materials, textile and papermaking, liquid/gas/vapor textile processing, etc. Small batch production, simple equipment and process, easy to adjust the effect of the formula

Inactive Publication Date: 2014-10-15
杨贤斌
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The foaming epoxy resin currently on the market is independent and agglomerated, and the agglomerated foaming epoxy resin cannot be precisely controlled in quantity
In recent years, although some manufacturers have pressed epoxy foamed resin into sheets, the thinnest thickness is generally around 2mm. Sheet-shaped foamed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0011] The basic principle of the present invention is: use the (woven) fiber base fabric to resist the physical strength of pulling, impregnate the fiber cloth into the solvent foamed epoxy resin to combine the fiber base fabric and the foamed epoxy resin, which greatly expands the hair The use range and precision of foamed epoxy resin.

[0012] The purpose of the present invention is to provide a novel preparation method for producing fiber cloth-based foamed epoxy resin cloth in view of the defects of the prior art. This method has the characteristics of simple process, low investment, convenient formula adjustment and small batch production; it is especially suitable for the production of thick fiber cloth.

[0013] The invention provides a preparation method of fiber cloth-based foamed epoxy resin cloth, which belongs to a solvent-based preparation method. The raw materials used in the method include fiber cloth-based, foaming agent, epoxy resin and solvent, and specifically i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of fiber-base-fabric foamed epoxy resin cloth. The preparation method is characterized in that raw materials include fiber base fabric, foaming agent, epoxy resin, auxiliaries and organic solvent. The preparation method comprises the following steps: respectively adding the foaming agent, the epoxy resin and auxiliaries into organic solvent to be stirred and mixed until the foaming agent, the epoxy resin and the auxiliaries are completely dissolved to form a mixed solution, then impregnating the fiber base fabric into the mixed solution, and drying, reeling, packaging and warehousing the fabric after the fiber base fabric is fused with the mixed solution. The preparation method is convenient to operate and has the advantages of less investment, high efficiency, low cost and the like.

Description

technical field [0001] The invention relates to a preparation method, in particular to a preparation method of fiber cloth-based foamed epoxy resin cloth. Background technique [0002] The foaming epoxy resins currently on the market are independent and agglomerated, and the agglomerated foaming epoxy resins cannot be precisely controlled quantitatively at all. In recent years, although some manufacturers have pressed epoxy foamed resin into sheets, the thinnest thickness is generally around 2mm. Sheet-shaped foamed epoxy resins have no strength before reaction, and cannot be made very thin or made Moreover, because sheet-shaped foamed epoxy resin is easily deformed and broken by external force, it cannot be rolled as tightly as carbon fiber prepreg, which greatly limits its scope of use and affects the strength of the entire system. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing a fiber ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06B3/10D06M15/55
Inventor 杨贤斌
Owner 杨贤斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap