A kind of pmma light diffusing agent and a kind of light diffusing pmma material

A light diffusion agent and light diffusion technology, which is applied in the field of light diffusion PMMA materials and PMMA light diffusion agents, can solve the unstable light transmittance performance of PMMA materials, the decrease of light transmittance, the anti-aging performance, and the thermal processing stability of impact strength Sexual impact and other issues, to achieve excellent atomization effect, improve atomization effect, and excellent impact resistance

Active Publication Date: 2017-10-17
广西海枫光学材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The material has good performance in light transmittance and refractive index, but the anti-aging performance, impact strength, thermal processing stability and other indicators of the material are affected to a certain extent.
At the same time, the light transmittance performance of the above-mentioned PMMA material is not stable, especially when used in LED lighting products, it is easy to age after working for a long time, high temperature, and strong light, which eventually leads to a decrease in light transmittance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pmma light diffusing agent and a kind of light diffusing pmma material
  • A kind of pmma light diffusing agent and a kind of light diffusing pmma material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A PMMA light diffusion agent with high light transmittance and high haze, its raw materials include the following components in parts by weight:

[0046] 75 parts of frozen finely pulverized polysiloxane particles;

[0047] Light scattering agent 1 1.3 parts;

[0048] Light scattering agent 2 6.5 parts;

[0049] 2 parts curing agent;

[0050] 0.2 parts of compatibilizer;

[0051] The light scattering agent 1 is a substance having the following structure

[0052] ;

[0053] The light scattering agent 2 is a substance having the following structure

[0054] ;

[0055] The compatibilizer is 0.04 parts by weight of cetyltrimethylammonium bromide and 0.3 parts of ethyl acetoacetate; the curing agent is a mixture of persulfate and tetrahydrofuran; The siloxane particles refer to the polysiloxane particles obtained by cooling the polysiloxane particles with an average particle diameter of 2.5 μm to -17° C., and then pulverizing them with 80 KHz ultrasonic waves.

[0...

Embodiment 2

[0060] A PMMA light diffusion agent with high light transmittance and high haze, its raw materials include the following components in parts by weight:

[0061] 80 parts of frozen finely pulverized polysiloxane particles;

[0062] 1 1 parts of light scattering agent;

[0063] 28 parts of light scattering agent;

[0064] 0.5 parts of curing agent;

[0065] 0.3 parts of compatibilizer;

[0066] The light scattering agent 1 is a substance having the following structure

[0067] ;

[0068] The light scattering agent 2 is a substance having the following structure

[0069] ;

[0070] The compatibilizer is 0.01 part by weight of cetyltrimethylammonium bromide and 0.5-0.7 part of ethyl acetoacetate; the curing agent is a mixture of persulfate and tetrahydrofuran; The pulverized polysiloxane particles refer to polysiloxane particles obtained by pulverizing polysiloxane particles with an average particle diameter of 2.5 μm to -20° C. with 60 KHz ultrasonic waves.

[0071] T...

Embodiment 3

[0075] A PMMA light diffusion agent with high light transmittance and high haze, its raw materials include the following components in parts by weight:

[0076] 50 parts of frozen finely pulverized polysiloxane particles;

[0077] 12 parts of light scattering agent;

[0078] 25 parts of light scattering agent;

[0079] 2.5 parts of curing agent;

[0080] 0.1 part of compatibilizer;

[0081] The light scattering agent 1 is a substance having the following structure

[0082] ;

[0083] The light scattering agent 2 is a substance having the following structure

[0084] ;

[0085] The compatibilizer is 0.07 parts by weight of cetyltrimethylammonium bromide and 0.5 parts of ethyl acetoacetate; the curing agent is a mixture of persulfate and tetrahydrofuran; The siloxane particles refer to the polysiloxane particles obtained by cooling the polysiloxane particles with an average particle diameter of 2.5 μm to -20° C., and then pulverizing them with 60 KHz ultrasonic waves....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

A PMMA light-diffusing agent, including frozen micro-pulverised polysiloxane particles, light-scattering agents 1 and 2, a curing agent, and a compatibilising agent, wherein the compatibilising agent is a mixture of hexadecyltrimethylammonium bromide and ethyl acetoacetate, and the curing agent is a mixture of a persulphate and tetrahydrofuran.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PMMA light diffusing agent and a light diffusing PMMA material. Background technique [0002] Light-diffusing materials refer to materials that can convert point and line light sources into line and surface light sources. They are generally prepared by dispersing light-diffusing particles with a different refractive index from the substrate in a transparent substrate. They were mostly used as backlight materials for liquid crystal displays in the early days. , also known as light scattering material or astigmatism material. The use of light-diffusing materials for light-emitting diode (LED) lighting is a new field of application that has opened up in recent years. LED lighting is stronger than LCD backlight, and has higher soft light performance; the light diffusing material used for LED lighting must minimize light loss while diffusing light, and have good toughness...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04C08K5/101C08K5/20C08L33/12
CPCC08K5/01C08K5/20C08L83/04
Inventor 林湖彬杜崇铭刘勋
Owner 广西海枫光学材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More