A kind of novel composite plate and preparation method thereof

A composite board, a new type of technology, applied in the field of building boards, can solve the problems of large forest resources, easy thermal expansion and cold contraction, ecological environment damage, etc., to achieve the effect of saving forest resources, natural and convenient materials, and natural and beautiful appearance

Active Publication Date: 2017-01-18
朱青海
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned boards are all made of wood as the main raw material. Therefore, they have the following defects: 1), they need to consume a large amount of forest resources, which directly cause the destruction of the ecological environment; After being soaked in water, it will be seriously deformed, which will affect its use), flammable, and very easy to expand with heat and contract with cold (determined by the characteristics of the wood itself)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of novel composite plate and preparation method thereof
  • A kind of novel composite plate and preparation method thereof
  • A kind of novel composite plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The novel composite board of this embodiment includes: a bottom plate 2 and a panel layer 1; the panel layer 1 is pasted on the bottom plate 2;

[0036] In terms of parts by weight, the raw material components of the bottom plate 2 include: 90 parts of PVC particles, 40 parts of calcium carbonate powder, 3 parts of stabilizers, 1.0 parts of foaming agents, 6 parts of foaming regulators, and 0.3 parts of polyethylene wax. , 0.3 parts of internal lubricant, 0.2 parts of oxidized polyethylene wax, 4 parts of chlorinated polyethylene, 0.5 parts of internal lubricant additives, 9 parts of wood flour.

[0037] Among them, the panel layer 1 is a log or bamboo skin surface layer, and its thickness is 0.3mm. The foaming agent is composed of a mixture of AC yellow foaming agent and NC white foaming agent in a mass ratio of 1:3; panel layer 1 and bottom plate The thickness ratio of 2 is 1:8; the water content of the panel layer 1 is 6%.

Embodiment 2

[0039] The novel composite board of this embodiment includes: a bottom plate 2 and a panel layer 1; the panel layer 1 is pasted on the bottom plate 2;

[0040] In parts by weight, the raw material components of the bottom plate 2 include: 100 parts of PVC particles, 50 parts of calcium carbonate powder, 4.5 parts of stabilizers, 1.2 parts of foaming agents, 7 parts of foaming regulators, and 0.4 parts of polyethylene wax. , 0.35 parts of internal lubricant, 0.3 parts of oxidized polyethylene wax, 5 parts of chlorinated polyethylene, 1 part of internal lubricant additives, 10 parts of wood flour.

[0041] Among them, the panel layer 1 is a log or bamboo skin surface layer, and its thickness is 2mm. The foaming agent is composed of a mixture of AC yellow foaming agent and NC white foaming agent in a mass ratio of 1:3; panel layer 1 and bottom plate 2 The thickness ratio is 1:9; the water content of the panel layer 1 is 10%.

Embodiment 3

[0043] The novel composite board of this embodiment includes: a bottom plate 2 and a panel layer 1; the panel layer 1 is pasted on the bottom plate 2;

[0044] In terms of parts by weight, the raw material components of the bottom plate 2 include: 110 parts of PVC particles, 60 parts of calcium carbonate powder, 6 parts of stabilizers, 1.4 parts of foaming agents, 8 parts of foaming regulators, and 0.5 parts of polyethylene wax. , 0.4 parts of internal lubricant, 0.4 parts of oxidized polyethylene wax, 6 parts of chlorinated polyethylene, 1.5 parts of internal lubricant additives, 11 parts of wood flour.

[0045] Among them, the panel layer 1 is a log or bamboo skin surface layer, and its thickness is 3mm. The foaming agent is composed of a mixture of AC yellow foaming agent and NC white foaming agent in a mass ratio of 1:3; panel layer 1 and bottom plate 2 The thickness ratio is 1:10; the water content of the panel layer 1 is 12%.

[0046] In addition, in all the embodiments of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of building boards and in particular relates to a novel composite board and a preparation method thereof. The novel composite board comprises a bottom board and a panel layer which is stuck on the bottom board, wherein the bottom board comprises the following raw materials in parts by weight: 90-110 parts of PVC particles, 40-60 parts of calcium carbonate powder, 3-6 parts of a stabilizer, 1.0-1.4 parts of a foaming agent, 6-8 parts of a foaming regulator, 0.3-0.5 part of polyethylene wax, 0.3-0.4 part of internal lubricant, 0.2-0.4 part of oxidized polyethylene wax, 4-6 parts of chlorinated polyethylene, 0.5-1.5 parts of an internal lubricant additive and 9-11 parts of wood powder. The novel composite board has the good waterproof and damp-proof effects and solves the problem that common boards in the prior art are soaked by water so as to seriously deform. The novel composite board also has the recycling characteristic and solves the technical problem that a large amount of wood needs to be consumed in wooded boards in the prior art.

Description

Technical field [0001] The invention relates to the field of building boards, in particular to a novel composite board and a preparation method thereof. Background technique [0002] Board is a kind of engineering construction material widely used in construction and interior decoration. In this field, the selection of boards is mainly based on natural wood materials. The existing wooden boards currently on the market consist of the following types: (1) solid wood logs; (2) multilayer solid wood; (3) reinforced composite wood. The above-mentioned boards are all made of wood as the main raw material. Therefore, they have the following shortcomings: 1) It needs to consume a lot of forest resources, which directly causes the destruction of the ecological environment; 2) It is not waterproof (for example, it is After blister, it will be severely deformed, which will affect its use), flammable, and very easy to expand and contract (determined by the characteristics of the wood itself...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B21/08B32B27/06B32B27/30C08L27/06C08L23/28C08L97/02C08L23/06C08L23/30C08K3/26C08J9/10
Inventor 朱青海
Owner 朱青海
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com