Acrylate emulsion pressure-sensitive adhesive for beautiful textured paper masking tapes, preparation method and applications thereof

A masking tape and acrylate technology, applied in the field of pressure-sensitive adhesives, can solve the problems of high peeling force of masking tape, poor human body, and environmental pollution, and achieve fast coating drying speed, high solid content, and low peeling Effect

Active Publication Date: 2015-02-25
XIANGYANG SUNVALOR AEROSPACE FILMS CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the adhesives used for masking tape generally contain organic solvents, such as toluene, benzene, etc., which pollute the environment and are not good for the human body.
[0003] CN 102226068 describes a masking tape adhesive and its preparation method, which solves the problem of environmental protection of organic solvents, but the peeling force of the masking tape prepared by it is relatively large, and the solid content is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The acrylate emulsion pressure-sensitive adhesive for masking tape of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0040] 2-Ethylhexyl Acrylate 49

[0041] Butyl acrylate 4.2

[0042] Butyl methacrylate 0.4

[0043] 2-hydroxypropyl acrylate 0.05

[0044] Acrylic 0.4

[0045] Ethylene glycol dimethacrylate 0.14

[0046] Anionic emulsifier 2A1 0.2

[0047] Nonionic emulsifier TX-10 0

[0048] Chain transfer agent tert-dodecyl mercaptan 0.01

[0049] Ammonium persulfate 0.4

[0050] Sodium bicarbonate 0.2

[0051] Deionized water 45

[0052] The preparation method of the acrylate emulsion pressure-sensitive adhesive for the masking tape of the masking tape is characterized in that the specific steps are as follows:

[0053] (1) Mix 50% ionized water, 80% anionic emulsifier 2A1, all nonionic emulsifier TX-10, 50% ammonium persulfate and all 2-ethylh...

Embodiment 2

[0058] The acrylate emulsion pressure-sensitive adhesive for masking tape of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0059] 2-Ethylhexyl Acrylate 49.5

[0060] Butyl acrylate 3

[0061] Butyl methacrylate 1.69

[0062] 2-hydroxypropyl acrylate 0.02

[0063] Acrylic 0.1

[0064] Ethylene glycol dimethacrylate 0.1

[0065] Anionic emulsifier 2A1 0.12

[0066] Nonionic emulsifier TX-10 0.05

[0067] Chain transfer agent tert-dodecyl mercaptan 0.02

[0068] Ammonium persulfate 0.25

[0069] Sodium bicarbonate 0.15

[0070] Deionized water 45

[0071] The preparation method of the acrylate emulsion pressure-sensitive adhesive for the masking tape of the masking tape is characterized in that the specific steps are as follows:

[0072] (1) Mix 50% ionized water, 80% anionic emulsifier 2A1, all nonionic emulsifier TX-10, 50% ammonium persulfate and all 2-...

Embodiment 3

[0077] The acrylate emulsion pressure-sensitive adhesive for masking tape of the present invention is prepared by polymerizing the raw materials of each component in a reactor, and its composition ratio is as follows in parts by weight:

[0078] 2-ethylhexyl acrylate 50.2

[0079] Butyl Acrylate 2.0

[0080] Butyl methacrylate 1.33

[0081] Acrylate -2-hydroxypropyl ester 0.2

[0082] Acrylic 0.15

[0083] Ethylene glycol dimethacrylate 0.12

[0084] Anionic emulsifier SDS 0.18

[0085] Nonionic emulsifier TX-10 0.02

[0086] Chain transfer agent tert-dodecyl mercaptan 0

[0087] Ammonium persulfate 0.5

[0088] Sodium bicarbonate 0.3

[0089] Deionized water 45

[0090] The preparation method of the acrylate emulsion pressure-sensitive adhesive for the masking tape of the masking tape is characterized in that the specific steps are as follows:

[0091] (1) Mix 50% ionized water, 80% anionic emulsifier SDS, all nonionic emulsifier TX-10, 50% ammonium persulfate and a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an acrylate emulsion pressure-sensitive adhesive for beautiful textured paper masking tapes, and a preparation method thereof. The provided acrylate emulsion pressure-sensitive adhesive is prepared from the following components through a pre-emulsification semi-continuous polymerization technology: 2-ethylhexyl acrylate, butyl acrylate, methylbutyl acrylate, 2-hydroxypropyl acrylate, carboxyl-containing functional monomers, internally-crosslinked polyacrylate monomers, and a chain transfer agent. The prepared acrylate emulsion pressure-sensitive adhesive has the advantages of high solid content, low gel content, and good stability, and can be used as a single-component adhesive directly.

Description

technical field [0001] The invention belongs to pressure-sensitive adhesives, in particular to an acrylate emulsion pressure-sensitive adhesive for masking tape and a preparation method thereof. Background technique [0002] Masking tape is widely used in interior decoration, spraying of household appliances, shielding protection of electronic circuit boards and spraying of high-end cars. Masking tape is composed of masking paper and pressure-sensitive adhesive, and the pressure-sensitive adhesive is coated on the masking paper. Its color separation effect is clear and clear, and it also has an arc art effect, which has brought a new technological revolution to the decoration and spraying industry, and made the industry glow with new vitality. However, the adhesives used for masking tapes currently contain organic solvents, such as toluene and benzene, which pollute the environment and are not good for the human body. [0003] CN 102226068 describes a masking tape adhesive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J7/04C08F220/18C08F220/06C08F222/14C08F220/28C08F2/26C08F2/30C08F2/38
Inventor 武鹏姜云刚冯小平何伟
Owner XIANGYANG SUNVALOR AEROSPACE FILMS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap