A kind of method for preparing propylene carbonate

A technology of propylene carbonate and carbon dioxide, applied in chemical instruments and methods, organic compound/hydride/coordination complex catalysts, organic chemistry, etc. The effect of good performance, high yield and mild reaction conditions

Inactive Publication Date: 2017-04-12
SHENYANG POLYTECHNIC UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many problems in the immobilized ionic liquid catalytic system represented by SBA-15 and silica gel, such as small pores, need for solvents, and poor catalyst stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing propylene carbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] First, add hydroxyl-terminated polyepichlorohydrin to chloroacetic acid in a molar ratio of 1:2.2 into a three-necked flask equipped with a condenser, acetonitrile as a solvent, and start stirring at a temperature of 80°C. After reacting for 1 hour, a small amount of Na 2 CO 3 Add the powder into the three-necked flask until it is completely dissolved, then repeat the addition until the system can no longer be dissolved. After reacting for about 7-8 hours, hydrochloric acid was added dropwise to the obtained liquid to adjust the pH value to be acidic. During the dropping process, the system was layered, the upper layer was a liquid phase, and the lower layer was a granular white solid. The upper liquid phase was rotary evaporated at a temperature of 70° C. and 0.09 MPa to remove the acetonitrile solvent. Then the product was washed 5 times with deionized water to remove some small molecules and excess chloroacetic acid, and then rotated at 70°C and 0.09Mpa to remove a ...

Embodiment 2

[0051] In the same equipment used in Example 1, under the same conditions, just change the catalyst consumption to 5.40g (accounting for 5% of the propylene oxide quality), its catalyzed reaction nearly 90min observes that the carbon dioxide mass flow count value does not change, After the reaction was completed, the purity of the propylene carbonate product was measured to be 99.6%, the calculated conversion rate of propylene oxide was 100.0%, and the selectivity was 99.2%.

Embodiment 3

[0053] In the same equipment used in Example 1, under the same conditions, just change the catalyst consumption to 1.08g (accounting for 1% of the propylene oxide mass), react 2.5h and observe that the carbon dioxide mass flow count value does not change, and the reaction is completed The purity of the propylene carbonate product was measured to be 99.1%, the conversion rate of ethylene oxide was calculated to be 99.8%, and the selectivity of ethylene carbonate was 98.2%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing propylene carbonate by catalytic addition of propylene oxide and carbon dioxide. The method is to realize the carbonylation reaction of carbon dioxide and propylene oxide under the action of an efficient carboxyl-terminated polyether ionic liquid catalyst to prepare propylene carbonate Ester, under the conditions of reaction temperature 60℃~100℃, reaction pressure 1.0~1.5MPa, stirring speed 200~250r / min, catalyst dosage accounted for 1~5% of propylene oxide mass, and reaction time 80~150min, The conversion rate of propylene oxide is above 98%, and the highest can reach 100%. Above 95%.

Description

technical field [0001] The invention relates to a method for preparing propylene carbonate, in particular to a method for preparing propylene carbonate by catalytic addition of propylene oxide and carbon dioxide. Background technique [0002] Cyclic carbonate is a good solvent for the production of high polymers such as polyamide, polyacrylonitrile, polyvinyl chloride, etc. It can also be used as spinning liquid and other chemical auxiliary agents in textiles, and can also be used as a solvent for removing industrial acid gases and concrete additives. In medicine, it can be used as a pharmaceutical component and an organic synthesis intermediate, and can also be used as a plastic foaming agent and a stabilizer for synthetic lubricating oil. In the capacitor battery industry, the mixed solution of ethylene carbonate and propylene carbonate has a high dielectric constant and can be used as the electrolyte of lithium batteries. With the increasing popularity of mobile phones a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D317/36B01J31/06
CPCY02P20/584
Inventor 郭立颖张彬孙洪涛白世阳马秀云常雪婷陈标崔晨
Owner SHENYANG POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com