A kind of clay powder for puppet animation and preparation method thereof

A clay powder and animation technology, applied in the field of animation production, can solve problems such as limitations and unsatisfactory effects, and achieve the effects of increasing viscosity, improving coloring efficiency and excellent performance.

Inactive Publication Date: 2017-01-18
QINGDAO AGRI UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the production of clay puppet animation, the shape of the puppet often needs to change its posture continuously. In order to facilitate the movement control, the creator needs to consider the character shape and the characteristics of the clay to design a skeleton with strong operability and durability. The performance of clay has caused certain limitations to technical creation, and the effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present embodiment clay powder for drawing is made up of the following raw materials in parts by weight: 55 parts of attapulgite, 15 parts of hydrotalcite, 2.5 parts of sodium lauryl sulfate, 4 parts of tourmaline micropowder, 12 parts of polyethylene, 2 parts of polyacrylic acid 1 part, 1 part of phthalocyanine blue, 5 parts of PETG, 3 parts of ABS high-glue powder.

[0023] The particle size of the attapulgite is 0.1-0.3 mm, the particle size of the tourmaline powder is 0.01-0.05 mm, and the particle size of the hydrotalcite is 0.1-0.2 mm.

[0024] Change puppet animation with clay powder and adopt the following steps to prepare:

[0025] (1) Modification of attapulgite: immerse the attapulgite in deionized water twice its weight, then add the sodium lauryl sulfate and tourmaline powder, mix well, and perform ultrasonic treatment for 6 minutes. The ultrasonic frequency is 70KHz, then filtered and dried to obtain modified attapulgite;

[0026] (2) Coloring: Subme...

Embodiment 2

[0038] The present embodiment clay powder for puppet painting is made up of the following raw materials in parts by weight: 50 parts of attapulgite, 16 parts of hydrotalcite, 2 parts of sodium lauryl sulfate, 5 parts of tourmaline micropowder, 10 parts of polyethylene, 3 parts of polyacrylic acid 1 part, 1 part of phthalocyanine green, 6 parts of PETG, 2 parts of ABS high rubber powder.

[0039] The particle size of the attapulgite is 0.1-0.3 mm, the particle size of the tourmaline powder is 0.01-0.05 mm, and the particle size of the hydrotalcite is 0.1-0.2 mm.

[0040] The puppet animation clay powder adopts the following steps to prepare:

[0041] (1) Modification of attapulgite: immerse the attapulgite in deionized water three times its weight, then add the sodium lauryl sulfate and tourmaline micropowder, mix well, and perform ultrasonic treatment for 8 minutes, The ultrasonic frequency is 68KHz, then filtered and dried to obtain modified attapulgite;

[0042] (2) Colori...

Embodiment 3

[0054] The present embodiment clay powder for puppet painting is made up of the following raw materials in parts by weight: 60 parts of attapulgite, 12 parts of hydrotalcite, 3 parts of sodium lauryl sulfate, 3 parts of tourmaline micropowder, 15 parts of polyethylene, 1 part of polyacrylic acid 2 parts, 2 parts of pigment red 166, 4 parts of PETG, 4 parts of ABS high rubber powder.

[0055] The particle size of the attapulgite is 0.1-0.3 mm, the particle size of the tourmaline powder is 0.01-0.05 mm, and the particle size of the hydrotalcite is 0.1-0.2 mm.

[0056] The preparation method of above-mentioned puppet animation clay powder may further comprise the steps:

[0057] (1) Modification of attapulgite: immerse the attapulgite in deionized water, then add the sodium lauryl sulfate and tourmaline powder, mix well, and perform ultrasonic treatment for 5 minutes, the ultrasonic frequency is 72KHz, Then filter and dry to obtain modified attapulgite; using this method to modi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of animation production and discloses clay powder for puppet animation. The clay powder for the puppet animation consists of the following raw materials in parts by weight: 50 to 60 parts of attapulgite, 12 to 16 parts of hydrotalcite, 2 to 3 parts of lauryl sodium sulfate, 3 to 5 parts of tourmaline micropowder, 10 to 15 parts of polyethylene, 1 to 3 parts of polyacrylic acid, 1 to 2 parts of organic pigment, 4 to 6 parts of polyethylene terephthalate glycol (PETG) and 2 to 4 parts of acrylonitrile-butadiene-styrene (ABS) high-adhesive powder. The invention also discloses a preparation method of the clay powder for the puppet animation, which comprises the steps of modifying the attapulgite, coloring the modified attapulgite, mixing the materials and the like. The obtained clay material is exquisite and stable, has a good coloring effect, is non-greasy and colorfast, has high plasticity, low shrinking percentage after being formed and excellent compressive property, is convenient and durable, and can improve the shaping effect of puppet animation figures.

Description

technical field [0001] The invention belongs to the technical field of animation production, and in particular relates to clay powder for puppet animation and a preparation method thereof. Background technique [0002] Stop-motion animation (stop-motion animation), as its name suggests, is to produce as if alive characters or any bizarre characters imaginable by shooting subjects frame by frame and then showing them continuously. The usual stop-motion animation is generally embodied in the form of puppet animation, and puppet animation, as the name suggests, is puppet animation, which is performed through clay puppets, puppets or their mixed-material characters. The history and tradition of this form of animation The history of hand-drawn animation (cel animation) in the sense is as long, and may even be older. [0003] In recent years, with the release of "Wallace and Gromit", "Chicken Run" and other dramas, puppet animation has received unanimous praise from the audience ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L67/02C08L55/02C08L33/02C08K13/06C08K9/04C08K3/34C08K3/26
CPCC08L23/06C08L2205/035C08L67/02C08L55/02C08L33/02C08K13/06C08K9/04C08K3/346C08K3/26C08K3/34
Inventor 田永江
Owner QINGDAO AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap