Functional live crystal porcelain and preparation method and application thereof

A technology for functional and crystalline porcelain, applied in the field of functional active crystalline porcelain and its preparation, can solve problems such as single performance, achieve the effect of promoting human health, improving physiological efficacy and health efficacy, and having good application prospects

Active Publication Date: 2015-11-04
广东增福汉坊窑陶瓷文化实业有限公司
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the single and insufficient performance of existing ceramic products, and provide a functional living crystal porcelain, which can

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional live crystal porcelain and preparation method and application thereof
  • Functional live crystal porcelain and preparation method and application thereof
  • Functional live crystal porcelain and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Example 1 Preparation of functional living crystal porcelain

[0051] 1. To prepare functional living crystal porcelain, the steps are as follows:

[0052] S1. Raw material pretreatment:

[0053] S11. respectively calcining potassium feldspar and albite at 980-990°C for 4-5 hours, cooling to room temperature, grinding, and passing through a 125-130 mesh sieve;

[0054] S12. respectively calcining periclase, quartzite, medical stone, and tourmaline at 800-820°C for 7-8 hours, cooling to normal temperature, grinding, and passing through a 125-130 mesh sieve;

[0055] S13. Calcinate agate stone, ferric oxide and meteorite at 965-980°C for 4-5 hours, Xiuyu at 820-830°C for 7-8 hours, cool to room temperature and then grind them to pass through 125-130 mesh screen;

[0056] S14. Calcining kaolin, bentonite and clay respectively at 570-580° C. for 7-9 hours, cooling to normal temperature, grinding, and passing through a 125-130 mesh sieve;

[0057] S2. Preparation of po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses functional live crystal porcelain and a preparation method and application thereof. The functional live crystal porcelain is prepared from, by weight, 23-25.5% of kaolin, 21-23% of clay, 14-18% of bentonite, 15.5-18.5% of quartz stone, 10.5-13.5% of albite, 40-46% of potash feldspar, 14-16.5% of carnelian cobble, 5-6.5% of ferric oxide, 5.5-7% of tourmaline, 7.8-8.7% of medical stone, 5.5-7% of stone needle, 2.8-3.2% of periclase, 5.3-6.7% of hsiuyen jade, 9.6-10.4% of rare earth elements and 0.2-1.4% of titanium peroxide. The functional live crystal porcelain can activate water molecules so that the water molecules can be absorbed by human cells more easily, more importantly, can adjust the variety and content of mineral substance in water, and can further facilitate human health and improve the physiological effect and health effect of water on the human body.

Description

technical field [0001] The invention belongs to the technical field of ceramic modification. More specifically, it relates to a functional living crystal porcelain and its preparation method and application. Background technique [0002] Traditional ceramic products only play the role of decoration or holding things. Ceramic containers do not play any beneficial role for the objects they hold, but are simply used as containers. [0003] The inventor has researched a living crystal porcelain in the early stage, and the made living crystal porcelain product can turn daily drinking water into small molecular mass water (called living water), and the small molecular mass water can enter the cell water channel of the human body, thereby Improve the physiological and health effects of water on the human body; studies have shown that orderly and structured small molecular water is easily absorbed by human cells, and can better participate in the material metabolism, energy metabo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04C04B33/34C04B33/13C04B41/86
Inventor 林俊生林侨山杨史奋
Owner 广东增福汉坊窑陶瓷文化实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap